Holes with different sizes from microscale to nanoscale were directly fabricated by focused ion beam (FIB) milling in this paper. Maximum aspect ratio of the fabricated holes can be 5:1 for the hole with large size with pure FIB milling, 10:1 for gas assistant etching, and 1:1 for the hole with size below 100 nm. A phenomenon of volume swell at the boundary of the hole was observed. The reason maybe due to the dose dependence of the effective sputter yield in low intensity Gaussian beam tail regions and redeposition. Different materials were used to investigate variation of the aspect ratio. The results show that for some special material, such as Ni-Be, the corresponding aspect ratio can reach 13.8:1 with Clâ‚‚ assistant etching, but only 0.09:1 for Si(100) with single scan of the FIB. / Singapore-MIT Alliance (SMA)
| Identifer | oai:union.ndltd.org:MIT/oai:dspace.mit.edu:1721.1/7450 |
| Date | 01 1900 |
| Creators | Fu, Yongqi, Ngoi, Kok Ann Bryan |
| Source Sets | M.I.T. Theses and Dissertation |
| Language | English |
| Detected Language | English |
| Type | Article |
| Format | 509804 bytes, application/pdf |
| Relation | Innovation in Manufacturing Systems and Technology (IMST); |
Page generated in 0.0029 seconds