This research study investigates the effect of micronized copper azole type C (MCA-C) preservative system on the rolling shear (RS) properties of CLT. In the first part of research, bonding performance of CLT panels treated at two retention levels, 0.96 kg/m3 and 2.5 kg/m3, were evaluated. Three structural adhesive systems, melamine formaldehyde (MF), resorcinol formaldehyde (RF) and one-component polyurethane (1C-PUR) were used to assemble visually graded No. 2 2×6 southern yellow pine (SYP) lumber while manufacturing CLT panels. For treated CLT panels, 1C-PUR provides better bonding performance test results. The RS properties of MCA-C treated CLT panels were studied in the second part of the research. The CLT panels were subjected to out-of-plane loading according to the EN 16351 standard. The mean values of RS strength and modulus of treated CLT were 1.89 MPa and 289.4 MPa respectively.
| Identifer | oai:union.ndltd.org:MSSTATE/oai:scholarsjunction.msstate.edu:td-4046 |
| Date | 09 August 2019 |
| Creators | Tripathi, Sachin |
| Publisher | Scholars Junction |
| Source Sets | Mississippi State University |
| Detected Language | English |
| Type | text |
| Format | application/pdf |
| Source | Theses and Dissertations |
Page generated in 0.0016 seconds