The texture and rotation movements of Ag nano particles and nano films

Thermal evaporator was used to coat a layer of silver nano-particles and thin film on (100) plane of rock salt .
The experiment content can be divide into three parts .
In the first part , the (100) texture of Ag nano-film and the evolution of the microstructure during annealing were studied . Little change in microstructure was found during low temperature annealing . In the second part , the salt surface was treated with deionized water and chlorine to try to align the Ag nano-particles on its surface . The effect of annealing on the texture and the defects of the Ag nano-particles were analyzed . The stacking fault was found to form early in the nucleation stage . In the third part , Ag nano-particles were scattered on the (100) texture , Ag nano-film and their rotation was studied by annealing at different temperature . Most Ag nano-particles were confirmed to rotate to a parallel orientation relationship with the Ag nano-film .

Identiferoai:union.ndltd.org:NSYSU/oai:NSYSU:etd-0706107-171448
Date06 July 2007
CreatorsChieh, Lin-Jen
ContributorsShen, Pouyan, Gan, Der shin, Kao Po-We
PublisherNSYSU
Source SetsNSYSU Electronic Thesis and Dissertation Archive
LanguageCholon
Detected LanguageEnglish
Typetext
Formatapplication/pdf
Sourcehttp://etd.lib.nsysu.edu.tw/ETD-db/ETD-search/view_etd?URN=etd-0706107-171448
Rightscampus_withheld, Copyright information available at source archive

Page generated in 0.002 seconds