ABSTRACT
sPBI is a heterocyclic aromatic polymer assuming a para- catenated backbone yielding a rod-like configuration. Because of its rigidity, this rod-like molecule displays superior mechanical tenacity, thermo-oxidative stability, and solvent resistance. It is also the precursor of rigid-rod solid polyelectrolyte exhibiting high solubility and superior ionic conductivity.
Isotropic solution were prepared by dissolving sPBI in distilled methanesulfonic acid containing 0.0, 0.989, 4.76, 9.09, 15.0, 20.0, 23.1 wt. % lithium ion of dopants of LiCF3SO3 or LiN(CF3SO2)2. The room-temperature DC conductivity of sPBI cast film doped with 15.0 wt. % LiN(CF3SO2)2 parallel (
| Identifer | oai:union.ndltd.org:NSYSU/oai:NSYSU:etd-0714103-013011 |
| Date | 14 July 2003 |
| Creators | Lin, Chia-Hung |
| Contributors | Jin-Long Hong, Bae-Heng Tseng, Shih-Jung Bai |
| Publisher | NSYSU |
| Source Sets | NSYSU Electronic Thesis and Dissertation Archive |
| Language | Cholon |
| Detected Language | English |
| Type | text |
| Format | application/pdf |
| Source | http://etd.lib.nsysu.edu.tw/ETD-db/ETD-search/view_etd?URN=etd-0714103-013011 |
| Rights | not_available, Copyright information available at source archive |
Page generated in 0.0012 seconds