Fully conjugated heterocyclic aromatic rod-like polymer poly-p-phenylene- benzobisoxazole (PBO) and coil-like poly-(3-hexylthiophene) (P3HT) were applied as opto-electronically active layer. The two polymers mixed with nano-carbon particles, having excellent optical absorption and electric conductivity, of [6,6]-phenyl C61-butyric acid methyl ester (PCBM) or esterified multi-wall carbon nano-tube (MWNT-COOC10H21) as well as a hole transporting layer of PEDOT:PSS. Photovoltaic (PV) cells of indium-tin-oxide (ITO)/PEDOT:PSS/nano-carbon particle:fully conjugated polymer/Al were fabricated for optical and electrical characterizations.
Tri-layered structure of ITO/PEDOT:PSS/PBO/PCBM/Al produced a straight current-voltage relation showing no PV effects. Upon changing the active layer into PCBM doped P3HT layer (PCBM:P3HT), it produced good PV effects suggesting that the doped layer had a penetrating network to facilitate the PV effects.
When PCBM or MWNT-COOC10H21 was doped into P3HT, the device PV effects were increased significantly with nano-carbon particle concentration. The direct-current electric conductivity parallel to the film surface (£m¡ü)was increased with the nano-carbon particle concentration.
By changing the thickness of hole transporting PEDOT:PSS and of opto-electronically active layers, it was found that when the PEDOT:PSS layer was decreased from 90 nm to 32 nm, there was a slight increase of PV cell efficiency. The active layer of PCBM:P3HT with a thickness of 99 nm had the best optical absorption and charge transport leading to an increase of PV cell efficiency.
| Identifer | oai:union.ndltd.org:NSYSU/oai:NSYSU:etd-0726109-100218 |
| Date | 26 July 2009 |
| Creators | Wang, Lian-bing |
| Contributors | Ming Chen, Jen-wei Huang, Bae-heng Tseng, Shih-jung Bai, Jui-hung Hsu |
| Publisher | NSYSU |
| Source Sets | NSYSU Electronic Thesis and Dissertation Archive |
| Language | Cholon |
| Detected Language | English |
| Type | text |
| Format | application/pdf |
| Source | http://etd.lib.nsysu.edu.tw/ETD-db/ETD-search/view_etd?URN=etd-0726109-100218 |
| Rights | not_available, Copyright information available at source archive |
Page generated in 0.0023 seconds