The flexible substrate was fabricated by BaTi4O9 mixed with O-Cresol Novolac Epoxy, polyether imide or surface active agents. The electrical and physical characteristic measured had been finished. The dielectric property influence of substrate was changed from percentage of BaTi4O9. The dielectric constant model was used by Jayasundere and Smith equation (J. S. eq.) and Lichtenecker equation (L. eq.)
The study of crystalline grain, orientation and phase transfer temperature was used by SEM, XRD, and DSC, respectively. The dielectric constant and dielectric loss tangent of the composite was measured using an HP4294A impedance analyzer. The TM mode calculated by resonate frequency of the composite was measured using an HP4156C network analyzer. The dielectric constant was obtained to TM mode at high frequency.
The result was showed that dielectric constant at low frequency of BaTi4O9, OCN Epoxy and PEI are 57, 5.8 and 3.65, respectively. OCN Epoxy is better than PEI of electrical characteristic. However, OCN Epoxy is not flexible. For this reason, the PEI was focused on electrical property at high frequency.
The BaTi4O9 exhibited a dielectric constant of 39 at frequency during 3~10 GHz. The dielectric constant was measured of 10 at frequency during 2~16 GHz with 70 wt% PEI composite. The dielectric constant is higher than FR-4 substrate to 6.4 of the composite. The low dielectric constant is obtaining to reduce stuffing.
| Identifer | oai:union.ndltd.org:NSYSU/oai:NSYSU:etd-0731107-182543 |
| Date | 31 July 2007 |
| Creators | Lee, Yi-Chih |
| Contributors | Chih-Yu Huang, Ying-Chung Chen, Rong-Sheng Guo, Chean-Cheng Su, Cheng-Fu Yang |
| Publisher | NSYSU |
| Source Sets | NSYSU Electronic Thesis and Dissertation Archive |
| Language | Cholon |
| Detected Language | English |
| Type | text |
| Format | application/pdf |
| Source | http://etd.lib.nsysu.edu.tw/ETD-db/ETD-search/view_etd?URN=etd-0731107-182543 |
| Rights | unrestricted, Copyright information available at source archive |
Page generated in 0.0208 seconds