My Ph.D. thesis is presented in two parts. In the first part, I describe the preparation of organic-inorganic hybrid micelles formed from poly(styrene-b-4-vinylpyridine) (PS-b-P4VP) block copolymers and CdSe quantum dots (QDs). Several distinct morphologies were observed including, spheres, finite-sized wormlike networks and clusters of hollow vesicles. A series of experiments were carried out to explore whether these hybrid colloids were thermodynamically stable or formed under kinetic control.
Upon addition of 2-propanol (2-PrOH) to a chloroform solution containing a mixture of PS404-b-P4VP76 plus CdSe QDs (2-PrOH is a good solvent for P4VP block and a precipitant for PS block and QDs), uniform spherical micelles formed almost instantly, with a PS core and a thin P4VP corona to which the QDs were attached. Vigorous stirring of this solution for two days led to the formation of three-dimensional wormlike networks consisted of Y-junctions and cylindrical struts, terminated by bulbous spherical end-caps. Even more profound structural changes occurred when the solution was subjected to prolonged magnetic stirring (e.g. 1 month).
ii
In contrast, manipulating the chemical composition of the initial block copolymer could trigger a spontaneous structural transition from sphere to network of wormlike micelles over 2 h without the need of stirring.
The second part of the thesis begins by describing a modular approach for preparing polyferrocenyldimethylsilane (PFS) block copolymers via a Cu-catalyzed alkyne/azide coupling reaction to covalently combine two homopolymers synthesized separately. This strategy opens the door to a broad library of novel functional PFS block copolymers, for example, poly(ferrocenyldimethylsilane-b-N-isopropyl acrylamide) (PFS-b-PNIPAM).
In an attempt to expand our understanding of PFS block copolymer self-assembly in polar solvents, I investigated the self-assembly of a new polymer (PFS26-b-PNIPAM105) in alcohol solvents. When the block polymer was dissolved in methanol, ethanol and 2-propanol, it formed long fiber-like micelles with uniform width. I also showed that micelles of this polymer underwent seeded growth in methanol, leading to cylindrical micelles that were nearly mono- dispersed in length.
| Identifer | oai:union.ndltd.org:TORONTO/oai:tspace.library.utoronto.ca:1807/43769 |
| Date | 14 January 2014 |
| Creators | Zhang, Meng |
| Contributors | Winnik, Mitchell A. |
| Source Sets | University of Toronto |
| Language | en_ca |
| Detected Language | English |
| Type | Thesis |
Page generated in 0.0025 seconds