碩士 / 國立臺灣科技大學 / 材料科學與工程系 / 99 / In this thesis, sodium alginate hydrogel was prepared by embedding
calcium alginate microspheres，instead of the conventional way of using
calcium chloride to crosslink sodium alginate hydrogel. In addition to swelling, water retention, basic characterization of biocompatibility tests, mechanical properties by DMA analysis was also employed to test and development of it’s hydrogel.
The results suggest that this new type of Alg-Ca2+ hydrogel was better than the traditional - calcium chloride crosslinked hydrogel,The was demonstrated by the halo test by loading with amoxilin. The application as drug carrier was demonstrated with the loading of hyaluronic acid.
| Identifer | oai:union.ndltd.org:TW/099NTUS5159015 |
| Date | January 2011 |
| Creators | Huai-chi Liu, 劉懷淇 |
| Contributors | Shuenn-kung Su, 蘇舜恭 |
| Source Sets | National Digital Library of Theses and Dissertations in Taiwan |
| Language | zh-TW |
| Detected Language | English |
| Type | 學位論文 ; thesis |
| Format | 57 |
Page generated in 0.0075 seconds