A viscometer was designed and built to study the rheological behavior of slags over a range of rates of shear of three orders of magnitude, up to a shear stress of [formula omitted]. The following slag compositions were studied (wt.%) 1) 42 Si02 - 20 A12O3 - 38 CaO, 2) 40.3 Si02 - 19.2 Al 2 O3 - 36.5 CaO - 4.0 CaF2, and 3) 37.8 Si02 - 18.0 Al 2 – O3 - 34.2 CaO - 10.0 CaF2, at temperatures of 1) 1390°C - 1350°C - 1332°C, 2) 1325°C - 1300°C and, 3) 1300°C respectively. Newtonian behavior was found for all compositions at the temperatures investigated. General conclusions are drawn as to the likelihood of Newtonian behavior for different compositions in these systems. / Science, Faculty of / Earth, Ocean and Atmospheric Sciences, Department of / Graduate
| Identifer | oai:union.ndltd.org:UBC/oai:circle.library.ubc.ca:2429/32581 |
| Date | January 1973 |
| Creators | Michel, Jean Raymond |
| Publisher | University of British Columbia |
| Source Sets | University of British Columbia |
| Language | English |
| Detected Language | English |
| Type | Text, Thesis/Dissertation |
| Rights | For non-commercial purposes only, such as research, private study and education. Additional conditions apply, see Terms of Use https://open.library.ubc.ca/terms_of_use. |
Page generated in 0.0025 seconds