Resistência adesiva de um sistema auto-condicionante e um convencional simplificado, aplicados à dentina tratada com diferentes condicionadores /

Orientador: Josimeri Hebling / Banca: Ricardo Marins de Carvalho / Banca: Elisa Maria Aparecida Giro / Resumo: A resistência adesiva de um sistema auto-condicionante e um convencional simplificado, Clearfil SE Bond e Single Bond, respectivamente, quando aplicados à dentina superficial tratada com diferentes agentes condicionadores, foi avaliada por meio de ensaios mecânicos de microtração. Superfícies planas de dentina, obtidas removendo-se a superfície oclusal de 30 terceiros molares humanos foram polidas com lixa de granulação 600 antes da aplicação de diferentes agentes condicionadores, SE Primer, ácido fosfórico ou EDTA. O primer acidificado SE Primer foi aplicado sobre a superfície por 20 segundos, seguido de suave secagem com jatos de ar. O ácido fosfórico a 37% foi aplicado por 15 segundos, seguido de lavagem e remoção do excesso de água com papel absorvente e a solução de EDTA 0,5M pH7,2 foi aplicada por 30 segundos, também seguida de lavagem e secagem. Com exceção das superfícies que receberam a aplicação do primer acidificado, as demais foram mantidas úmidas para a posterior aplicação dos sistemas adesivos avaliados. Sobre a superfície coberta pelo sistema adesivo foi construída uma coroa em resina composta Z250 e os dentes foram mantidos em água a 37% por 24h. Após 500 ciclos térmicos em temperaturas de 5o e 55oC, cortes paralelos no sentido mesio-distal e cortes perpendiculares aos primeiros, no sentido vestibulo-lingual, permitiram a obtenção de amostras com área de secção transversal quadrangular de 1,0mm2 em número mínimo de 10 para cada dente. Cada amostra foi colada a um dispositivo especialmente desenvolvido, e este foi acoplado à uma máquina universal de testes operada à velocidade de 0,5mm/min. O lado correspondente à dentina de aproximadamente 50% das superfícies fraturadas após o ensaio mecânico foi analizado em MEV. Os resultados mostraram que o maior valor médio de resistência adesiva foi observado para a associação SE Primer... (Resumo completo, clicar acesso eletrônico abaixo). / Abstract: Microtensile bond strength of a self-etching primer and a conventional one-bottle system, Clearfi SE Bond and Single Bond, respectively, bonded to superficial dentin treated with different conditioners was investigated. Flat dentin surfaces obtained by removing the occlusal enamel with a diamond saw were ground with 600-grit SiCs under wet conditions to create the smear layer before the conditioners application. Three different dentin conditioning was performed, SE Primer, phosphoric acid and EDTA. The SE Primer was applied on dentin for 20 seconds followed by slight air-drying. Phosphoric acid (37%) was applied for 15 seconds followed by rinsing. EDTA 0.5M pH7.2 was applied for 30 seconds, also followed by water rinsing. Except for the surfaces that received the SE Primer conditioner, the surfaces were left moist by blot-drying the excess water. The adhesive systems were applied and a 5mm high composite resin (Z250) was built up covering the whole surface. After 24h of storage in water at 37oC the teeth were thermocycled for 500 cycles at preset temperatures of 5o and 55oC. The teeth were sectioned with a diamond saw, perpendicular to the adhesive interface to produce beams with 1.0mm2 of adhesive area. These specimens were then attached to a testing apparatus and a tensile load was applied by a universal machine at a crosshead speed of 0.5mm/min. After the micro-tensile bond test, the dentin side of 50% of the fractured surfaces was examined under a scanning electron microscope. The highest tensile bond strength mean was found for the association of SE Primer and Single Bond, 58.51MPa, followed by the association Clearfil SE Bond and EDTA, 47.81MPa. The remaining associations showed mean tensile bond strength statistically similar, except for the association Single Bond and EDTA, which showed the lowest... (Complete abstract, click electronic address below). / Mestre

Identiferoai:union.ndltd.org:UNESP/oai:www.athena.biblioteca.unesp.br:UEP01-000167105
Date January 2002
CreatorsJacques, Paula.
ContributorsUniversidade Estadual Paulista "Júlio de Mesquita Filho" Faculdade de Odontologia (Campus de Araraquara).
PublisherAraraquara : [s.n.],
Source SetsUniversidade Estadual Paulista
LanguagePortuguese
Detected LanguageEnglish
Typetext
Format187 f. :
RelationSistema requerido: Adobe Acrobat Reader

Page generated in 0.0021 seconds