<p>In polymer electrolyte fuel cells (PEFC) chemical energy, in for example hydrogen, is converted by an electrochemical process into electrical energy. The PEFC has a working temperature generally below 100 °C. Under these conditions water management and transport of oxygen to the cathode are the parameters limiting the performance of the PEFC.</p><p>The purpose of this thesis was to better understand the complex processes in different parts of the PEFC. The rate-limiting processes in the cathode were studied using pure oxygen while varying oxygen pressure and humidity. Mass-transport limitations in the gas diffusion layer using oxygen diluted in nitrogen or helium was also studied. A large capacitive loop was seen at 1-10 Hz with 5-20 % oxygen. When nitrogen was changed to helium, which has a higher binary diffusion coefficient, the loop decreased and shifted to a higher frequency.</p><p>Steady-state and electrochemical impedance spectroscopy (EIS) models have been developed that accounts for water transport in the membrane and the influence of water on the anode. Due to water drag, the membrane resistance changes with current density. This gives rise to a low frequency loop in the complex plane plot. The loop appeared at a frequency of around 0.1 Hz and varied with <em>D</em>/<em>L<sub>m</sub></em><sup>2</sup>, where <em>D</em> is the water diffusion coefficient and <em>L<sub>m</sub></em> is the membrane thickness. The EIS model for the hydrogen electrode gave three to four semicircles in the complex plane plot when taking the influence of water concentration on the anode conductivity and kinetics into account. The high-frequency semicircle is attributed to the Volmer reaction, the medium-frequency semicircle to the pseudocapacitance resulting from the adsorbed hydrogen, and the low-frequency semicircles to variations in electrode performance with water concentration. These low-frequency semicircles appear in a frequency range overlapping with the low-frequency semicircles from the water transport in the membrane. The effects of current density and membrane thickness were studied experimentally. An expected shift in frequency, when varying the membrane thickness was seen. This shift confirms the theory that the low-frequency loop is connected to the water transport in the membrane.</p>
| Identifer | oai:union.ndltd.org:UPSALLA/oai:DiVA.org:kth-10087 |
| Date | January 2009 |
| Creators | Wiezell, Katarina |
| Publisher | KTH, Chemical Engineering and Technology, Stockholm : US-AB |
| Source Sets | DiVA Archive at Upsalla University |
| Language | English |
| Detected Language | English |
| Type | Licentiate thesis, comprehensive summary, text |
| Relation | Trita-CHE-Report, 1654-1081 ; 2009:6 |
Page generated in 0.002 seconds