<p>During this master thesis, wear and friction properties for the high-temperature alloy Kanthal APMT were studied. The results were also compared to 253MA. The initial tests showed, among other things, that the surface fineness of the muffle tubes matters in real applications like conveyor belts. A 253MA-sample wear-tested against a 253MA-tube showed lowest wear at 900°C while a pre-oxidized APMT-sample wear-tested against a APMT-tube had the lowest mean value of the friction force at 1100°C, compared to all other tests.</p>