The buffer layer in Cu(In,Ga)Se2 solar cells can improve cell performance. In this work we make CdS buffer layer by chemical bath deposition (CBD) without ammonia. CBD without ammonia were sought out since ammonia is a volatile compound. Different recipes for making CdS were tested; only one of the tested recipes actually produced something that is worth further investigating. This recipe used sodium citrate, an innocuous compound instead of ammonia. The best performance was 0.15 % off from the reference.This is almost as good as the used baseline process. However the worst almost completely killed the solar cells. Cell performance dropped by more than absolute 10 %. This demonstrates that chemical bath deposition can have profound effects on the solar cell performance. When trying to improve the best cells only detrimental effects showed up. This might show that, a part in the recipe used, NaOH has detrimental effects on solar cells. Ammonia free chemical bath deposition is possible, however so far it has not produced as good results as the reference. The difference is however very small, which makes it worth further investigating with moreand better solar cell material.
| Identifer | oai:union.ndltd.org:UPSALLA1/oai:DiVA.org:uu-206786 |
| Date | January 2013 |
| Creators | Hedlund, Daniel |
| Publisher | Uppsala universitet, Fasta tillståndets elektronik |
| Source Sets | DiVA Archive at Upsalla University |
| Language | English |
| Detected Language | English |
| Type | Student thesis, info:eu-repo/semantics/bachelorThesis, text |
| Format | application/pdf |
| Rights | info:eu-repo/semantics/openAccess |
| Relation | UPTEC K, 1650-8297 ; 13010 |
Page generated in 0.0051 seconds