Lithium-ion batteries are of great importance for today's society. The state-of-the-art batteries that are used today use a fluorinated electrolyte that contains the salt LiPF6 and acts as both a safety hazard and an environmental issue due to its ability to form the toxic gas hydrogen fluoride (HF). This project aims to find a fluorine-free electrolyte that can be used in silicon-based lithium-ion batteries to make them more environmentally friendly without detriment to the electrochemical performance. To do so, an additive that may form a solid electrolyte interphase (SEI) stable enough to allow a fluorine-free electrolyte to replace the ones used today is sought for. The salt of interest is lithium bis(oxalato)borate (LiBOB). Based on previous research electrolytes using LiBOB in either the solvent γ-Butyrolactone (GBL) or a mixture of ethylene carbonate (EC) and ethyl methyl carbonate (EMC) are examined. The additives used are vinylene carbonate (VC) and 1,3,2-dioxathiolane 2,2-dioxide (DTD). Techniques used are cyclic voltammetry, linear sweep voltammetry, galvanostatic charge and discharge, X-ray photoelectron spectroscopy and scanning electron microscopy. The cells using GBL as solvent have cycled very poorly during this project while LiBOB in EC:EMC + VC shows the most promising results, with highest capacity retention and less amount of degraded LiBOB during the first charge. It is also to be noted that both EC:EMC based electrolytes provide the formation of a passivating solid electrolyte interface (SEI) and are of interest for further investigation based on the results obtained during this project.
| Identifer | oai:union.ndltd.org:UPSALLA1/oai:DiVA.org:uu-456129 |
| Date | January 2021 |
| Creators | Wahlfort, Filippa |
| Publisher | Uppsala universitet, Strukturkemi |
| Source Sets | DiVA Archive at Upsalla University |
| Language | English |
| Detected Language | English |
| Type | Student thesis, info:eu-repo/semantics/bachelorThesis, text |
| Format | application/pdf |
| Rights | info:eu-repo/semantics/openAccess |
| Relation | UPTEC K, 1650-8297 ; 21010 |
Page generated in 0.1093 seconds