Aluminum-magnesium alloy (AA5083-H116) is primarily designed for marine applications such as in ship hulls and deckhouses. Its excellent combination of physical and mechanical properties makes it useful for other applications such as aircraft construction, military equipment and vehicles and automobiles.<p>This study investigated the effect of time and temperature of sensitization on the mechanical and chemical properties of AA5083-H116 such as tensile strength, yield strength and susceptibility to intergranular corrosion (IGC). Test specimens were sensitized at various temperatures (80oC, 100oC, 175oC and 200oC) for up to 672 h (4 weeks). Microhardness measurements, tensile testing, scanning electron microscopy (SEM), energy dispersive X-ray spectrometry (EDS), inductively coupled plasma/mass spectrometry (ICP/MS) and nitric acid mass loss tests (NAMLT) were used to evaluate these effects. <p>The results obtained show that the mechanical properties of AA5083-H116 deteriorated with increasing sensitization temperature and time. The adverse effect on these properties was attributed to reduction in dislocation density and recrystallization at higher temperatures. The as-received specimens and those sensitized at 80oC showed no susceptibility to IGC. However, at higher sensitization temperatures and longer resident
times, resistance to IGC decreased dramatically. The reduction in IGC resistance was attributed to precipitation of secondary phases along the grain boundaries.
| Identifer | oai:union.ndltd.org:USASK/oai:usask.ca:etd-02222006-163020 |
| Date | 24 February 2006 |
| Creators | Adigun, Olusegun John |
| Contributors | Yang, Qiaoqin |
| Publisher | University of Saskatchewan |
| Source Sets | University of Saskatchewan Library |
| Language | English |
| Detected Language | English |
| Type | text |
| Format | application/pdf |
| Source | http://library.usask.ca/theses/available/etd-02222006-163020/ |
| Rights | unrestricted, I hereby certify that, if appropriate, I have obtained and attached hereto a written permission statement from the owner(s) of each third party copyrighted matter to be included in my thesis, dissertation, or project report, allowing distribution as specified below. I certify that the version I submitted is the same as that approved by my advisory committee. I hereby grant to University of Saskatchewan or its agents the non-exclusive license to archive and make accessible, under the conditions specified below, my thesis, dissertation, or project report in whole or in part in all forms of media, now or hereafter known. I retain all other ownership rights to the copyright of the thesis, dissertation or project report. I also retain the right to use in future works (such as articles or books) all or part of this thesis, dissertation, or project report. |
Page generated in 0.0023 seconds