The goal of this research was the fabrication of thin films with magneto-optic (MO) properties. Accomplishment of this task was achieved via sol-gel processing of rare-earth and aluminum substituted yttrium-iron garnet (RxY3-xAlyFe5-yO12, R,Al:YIG), where R= Bi, Gd, Er, Ho. Detailed are the processing conditions, parameters and results leading to R,Al:YIG films with MO response. Success was attained with a 0.25M Gd,Al:YIG solution spin coated for 120 seconds at 3500rpm onto a (111) gadolinium gallium garnet (GGG) substrate and calcinated at 900°C for 4 hours. Samples were characterized via x-ray diffraction (XRD), magneto-optical loop tracer, scanning electron microscopy (SEM), energy dispersive x-ray spectroscopy (EDS), profilometry and optical microscopy. / Master of Science
| Identifer | oai:union.ndltd.org:VTETD/oai:vtechworks.lib.vt.edu:10919/36458 |
| Date | 31 March 2003 |
| Creators | DiBiccari, Anders Owen |
| Contributors | Materials Science and Engineering, Lu, Guo-Quan, Corcoran, Sean G., Reynolds, William T. Jr. |
| Publisher | Virginia Tech |
| Source Sets | Virginia Tech Theses and Dissertation |
| Detected Language | English |
| Type | Thesis |
| Format | application/pdf |
| Rights | In Copyright, http://rightsstatements.org/vocab/InC/1.0/ |
| Relation | etd.pdf |
Page generated in 0.0025 seconds