This experimental investigation examines the influence of surface treatment on the strength of low-fired tempered ceramic bodies. Specimens prepared with commercial raw materials are employed, either finger-smoothed, burnished, textured, slipped/burnished, or resin coated; two building techniques, coiling and paddle-and-anvil, are also included since these forming processes affect the vessel surface. The modulus of rupture or flexural strength is determined by means of a four-point bending test, which is sensitive to critical surface flaws. By means of a univariate analysis of variance, small differences in strength are found between ceramic briquettes with different surface treatments. Although the differences in means for the moduli of rupture values are statistically significant, the differences are of such a low magnitude that they cannot be considered behaviorally relevant. These results are only valid for the materials, mode of preparation, and test procedures employed.
| Identifer | oai:union.ndltd.org:arizona.edu/oai:arizona.openrepository.com:10150/277112 |
| Date | January 1989 |
| Creators | Fournier GarciÌ a, Patricia |
| Contributors | Schiffer, Michael B. |
| Publisher | The University of Arizona. |
| Source Sets | University of Arizona |
| Language | en_US |
| Detected Language | English |
| Type | text, Thesis-Reproduction (electronic) |
| Rights | Copyright © is held by the author. Digital access to this material is made possible by the University Libraries, University of Arizona. Further transmission, reproduction or presentation (such as public display or performance) of protected items is prohibited except with permission of the author. |
Page generated in 0.0021 seconds