Natural precious opals consist of silica nanoparticles of uniform diameter organised in a periodic three-dimensional structure. The physical structure of the material produces the perceived colour by a process of light diffraction. The modification of light by the physical structure of the material is also known as structural colour. This is a different process from how most surface colours are produced where light is more usually absorbed by dye and/or pigment molecules. Desirable aesthetic qualities could be achieved if the structural colours produced by natural opals could be replicated in the form of a film or a coating on textile substrates. The work presented investigates how to produce structurally coloured textiles using surface applications of uniform spherical silica nanoparticles (USSNPs). A novel one-step solvent varying (SV) technique has been developed to synthesise USSNPs with particle diameters in a controlled size range. Using suspensions containing USSNPs, structurally coloured artificial opal (AO) films have been fabricated by self-assembly using a process of natural gravity sedimentation. The sedimentation of a particular particle size range of USSNPs (from which a coloured film was produced), onto the surface of fabrics, produced a structurally coloured fabric. By controlling the mean particle diameter a wide range of spectral colours from red to blue was obtained. The light fastness properties of the coloured textiles were investigated. A further surface modification of USSNPs was performed by adding vinyl functional groups to improve the mechanical strength of the structural colour. This work suggested a novel approach to colouring textile materials without using traditional dyes and/or pigments.
| Identifer | oai:union.ndltd.org:bl.uk/oai:ethos.bl.uk:680029 |
| Date | January 2016 |
| Creators | Gao, Weihong |
| Publisher | University of Manchester |
| Source Sets | Ethos UK |
| Detected Language | English |
| Type | Electronic Thesis or Dissertation |
| Source | https://www.research.manchester.ac.uk/portal/en/theses/the-fabrication-of-structurally-coloured-textile-materials-using-uniform-spherical-silica-nanoparticles(c2815c09-5353-4667-a1a3-1b31b62f8787).html |
Page generated in 0.0027 seconds