by Kwong Wai Kuen = 鋁銘金屬間化合物的製造和性能測試 / 鄺偉權. / Thesis (M.Phil.)--Chinese University of Hong Kong, 2003. / Includes bibliographical references. / Text in English; abstracts in English and Chinese. / by Kwong Wai Kuen = Lü ming jin shu jian hua he wu de zhi zao he xing neng ce shi / Kuang Weiquan. / Acknowledgement --- p.i / Abstract --- p.ii / 摘要 --- p.iii / List of tables --- p.iv / List of figures --- p.v / Table of contents --- p.xi / Chapter Chapter 1 --- Background / Chapter 1.1 --- Introduction --- p.1-1 / Chapter 1.2 --- Aluminum --- p.1-1 / Chapter 1.3 --- Chromium --- p.1-3 / Chapter 1.4 --- Intermetallics --- p.1-4 / Chapter 1.4.1 --- Alloys and intermetallics --- p.1-4 / Chapter 1.4.2 --- Properties of intermetallics --- p.1-5 / Chapter 1.4.3 --- Intermetallics 一 past to present --- p.1-6 / Chapter 1.4.4 --- Commonly used intermetallics --- p.1-7 / Chapter 1.4.5 --- Prospects of intermetallic compounds --- p.1-9 / Chapter 1.5 --- Previous works --- p.1-11 / Chapter 1.6 --- Current work --- p.1-12 / Chapter 1.7 --- Outline of thesis --- p.1-12 / References --- p.1-14 / Tables and figures --- p.1-17 / Chapter Chapter 2 --- Methodology and Instrumentation / Chapter 2.1 --- Experimental approaches --- p.2-1 / Chapter 2.2 --- Sample preparation --- p.2-2 / Chapter 2.2.1 --- Powder mixture --- p.2-2 / Chapter 2.2.2 --- Cold-pressing --- p.2-2 / Chapter 2.2.3 --- Pressureless sintering --- p.2-2 / Chapter 2.2.4 --- Hot-pressing --- p.2-3 / Chapter 2.2.5 --- Arc-melting --- p.2-4 / Chapter 2.3 --- Sample characterization --- p.2-5 / Chapter 2.3.1 --- DTA --- p.2-5 / Chapter 2.3.2 --- TMA --- p.2-5 / Chapter 2.3.3 --- Density measurement --- p.2-6 / Chapter 2.3.4 --- Microhardness measurement --- p.2-7 / Chapter 2.3.5 --- Scanning electron microscopy --- p.2-8 / Chapter 2.3.6 --- X-ray powder diffractometry --- p.2-9 / References --- p.2-10 / Figures --- p.2-11 / Chapter Chapter 3 --- Thermal analysis of Al-Cr powder mixtures / Chapter 3.1 --- Introduction --- p.3-1 / Chapter 3.2 --- Experiments --- p.3-1 / Chapter 3.3 --- Results and discussions --- p.3-2 / Chapter 3.3.1 --- DTA results --- p.3-2 / Chapter 3.3.2 --- Al-23wt%Cr --- p.3-2 / Chapter 3.3.3 --- Al-28wt%Cr and Al-33wt%Cr --- p.3-5 / Chapter 3.3.4 --- Al-46wt%Cr --- p.3-8 / Chapter 3.3.5 --- Al-55wt%Cr --- p.3-9 / Chapter 3.3.6 --- Al-79wt%Cr --- p.3-10 / Chapter 3.4 --- Reaction mechanisms in the formation of Al-Cr intermetallic compounds --- p.3-12 / Chapter 3.5 --- Summary --- p.3-12 / References --- p.3-14 / Tables and figures --- p.3-15 / Chapter Chapter 4 --- Fabrication of Al-Cr samples by hot-pressing and by arc-melting / Chapter 4.1 --- Introduction --- p.4-1 / Chapter 4.1.1 --- Hot-pressing method --- p.4-1 / Chapter 4.1.2 --- Arc-melting method --- p.4-2 / Chapter 4.2 --- Experiments --- p.4-2 / Chapter 4.3 --- Results and discussions --- p.4-3 / Chapter 4.3.1 --- Hot-pressing method for some specific compositions --- p.4-3 / Chapter 4.3.2 --- Hot-pressing method to produce low Cr content (LC) samples --- p.4-5 / Chapter 4.3.3 --- Effects of hot-pressed time and temperature --- p.4-6 / Chapter 4.3.4 --- Arc-melting method for some specific compositions --- p.4-8 / Chapter 4.3.5 --- Arc-melting method to produce LC samples --- p.4-10 / Chapter 4.4 --- Summary --- p.4-11 / Reference --- p.4-12 / Tables and figures --- p.4-13 / Chapter Chapter 5 --- Thermal expansion coefficients of arc-melted Al-Cr samples / Chapter 5.1 --- Introduction --- p.5-1 / Chapter 5.1.1 --- Thermal expansion --- p.5-1 / Chapter 5.1.2 --- Relations between thermal expansion and structural material --- p.5-1 / Chapter 5.2 --- Experiments --- p.5-2 / Chapter 5.3 --- Results and discussions --- p.5-3 / Chapter 5.3.1 --- TMA results of A1 and Cr --- p.5-3 / Chapter 5.3.2 --- TMA for Al-Cr IMCs --- p.5-3 / Chapter 5.4 --- Summary --- p.5-4 / References --- p.5-6 / Figures --- p.5-7 / Chapter Chapter 6 --- Physical properties of Al-Cr intermetallic compounds / Chapter 6.1 --- Introduction --- p.6-1 / Chapter 6.2 --- Results and discussion --- p.6-1 / Chapter 6.2.1 --- Hot-pressed samples --- p.6-1 / Chapter 6.2.1.1 --- Hot-pressed LC samples --- p.6-2 / Chapter 6.2.1.2 --- Effects of hot-pressing temperature and time --- p.6-3 / Chapter 6.2.2 --- Arc-melted samples --- p.6-4 / Chapter 6.2.3 --- Comparison between the hot-pressed sample and the arc-melted sample --- p.6-6 / Chapter 6.3 --- Summary --- p.6-7 / Tables and figures --- p.6-9 / Chapter Chapter 7 --- Conclusions / Chapter 7.1 --- Summary --- p.7-1 / Chapter 7.2 --- Future works --- p.7-2
| Identifer | oai:union.ndltd.org:cuhk.edu.hk/oai:cuhk-dr:cuhk_324218 |
| Date | January 2003 |
| Contributors | Kwong, Wai Kuen., Chinese University of Hong Kong Graduate School. Division of Physics. |
| Source Sets | The Chinese University of Hong Kong |
| Language | English, Chinese |
| Detected Language | English |
| Type | Text, bibliography |
| Format | print, 1 v. (various paging) : ill. ; 30 cm. |
| Rights | Use of this resource is governed by the terms and conditions of the Creative Commons “Attribution-NonCommercial-NoDerivatives 4.0 International” License (http://creativecommons.org/licenses/by-nc-nd/4.0/) |
Page generated in 0.0018 seconds