In this work, the growth and characterisation of the chalcopyrite semiconductor CuGaS2 is presented. The purpose of this study is to gain a better understanding of the defect chemistry of this class of materials through a systematic study relating the structural and optical properties to the composition of thin films grown by metalorganic vapour phase epitaxy. Details associated with the optimisation of the growth process are presented in a format relating the changes in the composition and morphology to variations in the growth process. The structural properties of thin films grown on GaAs(001) substrates are described. A dominance of polycrystalline growth is found to occur for Cu-rich material, whereas near-stoichiometric to Ga-rich material is typified by epitaxial growth. Secondary phases are identified by X-ray diffractometry and Raman spectroscopy for severely non-stoichiometric material. In some cases, the formation of the cubic zincblende and CuPt polytype of CuGaS2 are identified by transmission electron microscopy. It will be shown that changes in the Cu/Ga ratio of the solid strongly influence the photoluminescence response of the layers. Weak excitonic luminescence is observed for both slightly Ga-rich and Cu-rich material. Near stoichiometric layers exhibit luminescence centered at ~2.4 eV. Cu-rich layers are dominated by a line occurring at ~2.1 eV, whereas a different line at ~2.25 eV dominates for Ga-rich layers. A clear picture emerges of the radiative mechanisms dominating for Cu-rich and Ga-rich layers.
| Identifer | oai:union.ndltd.org:netd.ac.za/oai:union.ndltd.org:nmmu/vital:10541 |
| Date | January 2006 |
| Creators | Branch, Matthew Stewart |
| Publisher | Nelson Mandela Metropolitan University, Faculty of Science |
| Source Sets | South African National ETD Portal |
| Language | English |
| Detected Language | English |
| Type | Thesis, Doctoral, PhD |
| Format | 183 leaves, pdf |
| Rights | Nelson Mandela Metropolitan University |
Page generated in 0.0182 seconds