Calcium aluminate phases are important parts of Ordinary Portland cement and Alumina cement. Various calcium aluminate hydrates originate during the hydration of calcium alumina phases. Their origin depends on the conditions of hydration. In the diploma thesis was investigated hydration of four calcium aluminate phases – CA, CA2, C12A7, C3A under the conditions of four pH – 6, 9, 11, 12,65. Calcium aluminate phases were prepared from CaCO3 and Al2O3 by clinkering in solid phase in laboratory oven. The phases were hydrated for 48 hours. Kinetics of the hydration was investigated by calorimetry. Calcium aluminate hydrates were identified by XRD and DTA.
| Identifer | oai:union.ndltd.org:nusl.cz/oai:invenio.nusl.cz:216353 |
| Date | January 2008 |
| Creators | Koplík, Jan |
| Contributors | Opravil, Tomáš, Šoukal, František |
| Publisher | Vysoké učení technické v Brně. Fakulta chemická |
| Source Sets | Czech ETDs |
| Language | Czech |
| Detected Language | English |
| Type | info:eu-repo/semantics/masterThesis |
| Rights | info:eu-repo/semantics/restrictedAccess |
Page generated in 0.0021 seconds