Titanium powder was deposited into low-carbon steel specimens using three thermal spray technologies: plasma spray, cold spray (USA, Singapore) and warm spray (denoted as PS, CSU, CS-S, and WS, respectively, in further text). The aim was to determine the influence of the coatings on the fatigue lives of the specimens. The experimental work was carried out in a symmetrical cantilever-beam bending setup using a computer-controlled SF-Test loading device. Further to that, the micro-morphology of coatings structure, their respective porosity content and the fracture surfaces of both coatings and substrate materials was carried out.
| Identifer | oai:union.ndltd.org:nusl.cz/oai:invenio.nusl.cz:230925 |
| Date | January 2013 |
| Creators | Matějková, Michaela |
| Contributors | Kovářík,, Ondřej, Čížek, Jan |
| Publisher | Vysoké učení technické v Brně. Fakulta strojního inženýrství |
| Source Sets | Czech ETDs |
| Language | Czech |
| Detected Language | English |
| Type | info:eu-repo/semantics/masterThesis |
| Rights | info:eu-repo/semantics/restrictedAccess |
Page generated in 0.0025 seconds