The aim of this work is to define relations between grain size and bioaktivity of oxide ceramics, specifically ZrO2, Al2O3 and HA. Ceramic materials with grain size from 100 nm up to 10 m, with various surface roughness, were tested for its bioactivity. Ceramography analysis was performed for all tested materials to precisely describe microstructures. Biological properties of the ceramic materials were tested via dilation tests directly in-vitro and by in-vitro extraction. Three cell culturing lines: osteoblast MG63, fibroblast L929, and epithelioid HeLa, were used for our testing. An influence of the grain size on the biological response was only found for the ceramic materials which had been thermally etched. The thermally etched nanocrystalline samples had larger areas covered by cells than ceramics with coarse grain microstructure. Biological tests on layered composites Al2O3×ZrO2 showed the cell selection determined by the type of material, where ZrO2 surfaces were preferably covered. Improved biological response of nanocrystalline ZrO2 was demonstrated on ceramic ZrO2, Al2O3 and SiO2 substrates with nanocrystalline coating of ZrO2. In this work a novel technological process for the formation of defect-free coatings was developed. Sintered coatings were tested using in-vitro technique with cell line HeLa, L929 and MG63 for up to 72 hours. The results of the biological tests of nanocrystalline coatings were consistent with results from the bulk nanocrystalline thermally etched ZrO2 ceramics.
| Identifer | oai:union.ndltd.org:nusl.cz/oai:invenio.nusl.cz:234143 |
| Date | January 2012 |
| Creators | Matoušek, Aleš |
| Contributors | Vaněk,, Jiří, Lapčík,, Lubomír, Cihlář, Jaroslav |
| Publisher | Vysoké učení technické v Brně. Fakulta strojního inženýrství |
| Source Sets | Czech ETDs |
| Language | Czech |
| Detected Language | English |
| Type | info:eu-repo/semantics/doctoralThesis |
| Rights | info:eu-repo/semantics/restrictedAccess |
Page generated in 0.0019 seconds