The carbonation of the building materials based on the ordinary Portland cement is relatively well-known and extensively studied phenomenon. Conversely mechanism, reaction products and factors affecting the carbonation of the alkali activated materials are still not sufficiently clarified. In this work, the progression of the carbonation of the alkali activated materials under different conditions was investigated. The reaction products and the microstructural changes were determined by XRD respectively SEM-EDX analysis. The corrosive conditions due to the decreasing of the pH of the binders by the carbonation were observed by XPS analysis of the steel fibers. The carbonation of the alkali activated samples was compared with the reference samples based on the Portland composite cement. Besides these analyzes, the mechanical properties of the binders were monitored.
| Identifer | oai:union.ndltd.org:nusl.cz/oai:invenio.nusl.cz:240541 |
| Date | January 2016 |
| Creators | Suchý, Rostislav |
| Contributors | Koplík, Jan, Kalina, Lukáš |
| Publisher | Vysoké učení technické v Brně. Fakulta chemická |
| Source Sets | Czech ETDs |
| Language | Czech |
| Detected Language | English |
| Type | info:eu-repo/semantics/masterThesis |
| Rights | info:eu-repo/semantics/restrictedAccess |
Page generated in 0.0024 seconds