In this master thesis it was studied morphology of polyamide 12 (PA12), polyamide 11 (PA11) and their blends in the percent ratios 95/5, 75/25, 50/50, 25/75 and 5/95 formed at pressure 7 MPa in a calorimeter both after continual heating and cooling and after annealing and isothermal crystallization. Neat polyamides and blends were further characterized by thermogravimetric analysis, differential scanning calorimetry at atmospheric pressure, Fourier-transform infrared spectroscopy in attenuated total refection, and X-ray diffraction analysis. The increased pressure improved level of polyamide chains ordering in crystal lamellae. Thermal annealing improved especially ordering of PA12, isothermal crystallization led to considerable increase of crystallinity, whereas PA11-rich blends supported perfection of PA12 crystals. Partial transformation of - to -structure occurred in case of neat PA12 at high pressure, the change of the chain conformation into the closer one occurred in neat PA11 without transformation of the type of crystal structure.
| Identifer | oai:union.ndltd.org:nusl.cz/oai:invenio.nusl.cz:316212 |
| Date | January 2017 |
| Creators | Bělašková, Marie |
| Contributors | Tocháček, Jiří, Bálková, Radka |
| Publisher | Vysoké učení technické v Brně. Fakulta chemická |
| Source Sets | Czech ETDs |
| Language | Czech |
| Detected Language | English |
| Type | info:eu-repo/semantics/masterThesis |
| Rights | info:eu-repo/semantics/restrictedAccess |
Page generated in 0.0024 seconds