The synthesis of NaxCoO2 by Pechini method (with initial sodium stoichiometry x = 1.0, 0.9, 0.8, and 0.7) was studied for the samples heat-treated in the temperature range from 550 řC to 750 řC. The structure characterization and phase composition was carried out by the powder X-ray diffraction (XRD) analysis. The elementary analysis was done using atomic absorption spectroscopy. From the thermoelectric properties, the Seebeck coefficient was measured for both α- and γ- phase. The Weiss constant was determined for α- and γ- phase by linear regression of 1/χ. The real sodium content in sodium cobaltate phase was found to be independent on initial sodium precursor weight and measurement by PXRD and Seebeck coefficient showed that the sodium content in NaxCoO2 falls in the range from x = 0.65 to 0.75. The magnetization measurements showed presence of spinel Co3O4 impurities in the samples and the analysis of magnetic susceptibility showed unusual high values of the Weiss constant for α- phase in comparison with structurally similar γ- NaxCoO2. Thin film of NaxCoO2 with initial sodium stoichiometry x = 1.0, 0.52, 0.32, and 0.175 was deposited by chemical solution deposition method using spin-coating deposition on a 00l-oriented α-Al2O3 single crystal substrate. The formation and structure characterization of...
| Identifer | oai:union.ndltd.org:nusl.cz/oai:invenio.nusl.cz:344050 |
| Date | January 2016 |
| Creators | Soroka, Miroslav |
| Contributors | Nižňanský, Daniel, Sedmidubský, David |
| Source Sets | Czech ETDs |
| Language | English |
| Detected Language | English |
| Type | info:eu-repo/semantics/masterThesis |
| Rights | info:eu-repo/semantics/restrictedAccess |
Page generated in 0.0023 seconds