The presented PhD thesis is focused on the synthesis, characterization, and modifications of zeolites and zeolitic materials. The main interests are two-dimensional (2D) zeolites and modification of their interlamellar space. Presented work was performed at the Department of Synthesis and Catalysis at J. Heyrovský Institute of Physical Chemistry in Prague, Czech Republic under the supervision of Prof. Jiří Čejka. Zeolites are inorganic crystalline solids with a microporous framework structure. They are widely used as catalysts, sorbents, and ion-exchangers. Conventional zeolites have been recognized as three-dimensional (3D) tetrahedrally-connected frameworks. However, some of them are also known to exist in various layered forms (2D zeolites). Recently, the transformation of 3D germanosilicate UTL into layers (IPC-1P) has started a new branch in 2D zeolites chemistry. This chemically selective degradation of UTL framework was performed via acid hydrolysis. In the structure of this germanosilicate, Ge atoms are preferentially located in specific building units, double-four-rings (D4R), which connect dense silica layers. Modifications of the layered precursor IPC-1P led to discovery of the two novel 3D zeolites: IPC-4 (PCR) and IPC-2 (OKO). This novel approach in the zeolite synthesis, called ADOR...
| Identifer | oai:union.ndltd.org:nusl.cz/oai:invenio.nusl.cz:352050 |
| Date | January 2016 |
| Creators | Mazur, Michal |
| Contributors | Čejka, Jiří, Zima, Vítězslav, Hronec, Mlan |
| Source Sets | Czech ETDs |
| Language | English |
| Detected Language | English |
| Type | info:eu-repo/semantics/doctoralThesis |
| Rights | info:eu-repo/semantics/restrictedAccess |
Page generated in 0.0017 seconds