This thesis focuses on the characterization of PEDOT:DBSA, a new semiconducting polymer for use in bioelectronic devices. It also deals with possibilities of surface treatment in order to enhance its biocompatibility and stability in aqueous environments. For this purpose, the organic polymer films were crosslinked with two crosslinking agents – GOPS and DVS. The ability of these agents to prevent leaching of some fractions of the polymer films in an aqueous environment and the ability to bind polymer molecules to each other as well as to the glass substrate was studied using the delamination test. Subsequently, the effects of these crosslinking agents on the film properties essential for the proper functions of bioelectronics made of these materials, was studied by contact angle measurements and four-point probes respectively. Moreover, several OECTs were prepared using original and crosslinked material as an active layer and were characterized by measuring transconductance and volumetric capacitance. PEDOT:DBSA has been shown to be a suitable material for use in bioelectronics, but its thin layers need to be stabilized in an aqueous environment. The agent DVS appears to be unsuitable for this purpose, mainly due to its insufficient film stabilization and its increased hydrophilicity of the film surface, thus increased tendency to interact with water, resulting in degradation of these thin layers. In contrast, GOPS, despite some reduction in film conductivity, has been able to stabilize the polymer layer over the long term, and thus appears to be a suitable way to stabilize PEDOT:DBSA.
| Identifer | oai:union.ndltd.org:nusl.cz/oai:invenio.nusl.cz:414118 |
| Date | January 2020 |
| Creators | Malečková, Romana |
| Contributors | Salyk, Ota, Vala, Martin |
| Publisher | Vysoké učení technické v Brně. Fakulta chemická |
| Source Sets | Czech ETDs |
| Language | Czech |
| Detected Language | English |
| Type | info:eu-repo/semantics/masterThesis |
| Rights | info:eu-repo/semantics/restrictedAccess |
Page generated in 0.0029 seconds