This thesis deals with usage of hybrid technology Laser-TIG for welding of boron enhanced steel 22MnB5. This thesis evaluates the influence of preheating using technology of TIG arc welding to a weld quality in comparison with laser welds. In practical part of thesis there were 1,8 mm metal sheets of 22MnB5 welded. This metal sheet specimens were welded by using constant parameters of laser with varying parameters of TIG technology. There were 12 specimens of sheet metal created including 3 specimens using only laser and 9 specimens using Laser-TIG hybrid technology while varying magnitude of current (I=20 A, 40 A a 60 A). Welds created this way were evaluated by tensile test and strength limits compared. Then metalografic survey was carried out examining macro and microstructure. Results of metalografic survey were confronted with Vickers hardness test.
| Identifer | oai:union.ndltd.org:nusl.cz/oai:invenio.nusl.cz:417452 |
| Date | January 2020 |
| Creators | Krejčí, Adam |
| Contributors | Sigmund, Marian, Mrňa, Libor |
| Publisher | Vysoké učení technické v Brně. Fakulta strojního inženýrství |
| Source Sets | Czech ETDs |
| Language | Czech |
| Detected Language | English |
| Type | info:eu-repo/semantics/masterThesis |
| Rights | info:eu-repo/semantics/restrictedAccess |
Page generated in 0.0064 seconds