The master´s thesis deals with a process called cold kinetic deposition technology. Using this technology, a copper layer was formed on a sample with an aluminium base by high-pressure cold spraying at a pressure of 25 bar. In the experimental part, the influence of corrosion degradation in the salt chamber was assessed at the time cycles of 100 h, 200 h and 300h, where changes in internal and surface resistances before and after corrosion were measured. Subsequently, the analysis of corrosion products was performed, where the extent of corrosion attack was determined using an electron microscope. These methods led to a final evaluation of the boundary limits of the applied coating layer by cold kinetic deposition, after the effect of corrosion. Finally, a theoretical application of this technology was suggested. It was discovered that the sample placed and left in the corrosion chamber for the longest time was the most affected by corrosion. Finally, a theoretical application of cold kinetic deposition was proposed.
| Identifer | oai:union.ndltd.org:nusl.cz/oai:invenio.nusl.cz:442436 |
| Date | January 2021 |
| Creators | Šteiniger, Jakub |
| Contributors | Zimáková, Jana, Binar, Tomáš |
| Publisher | Vysoké učení technické v Brně. Fakulta elektrotechniky a komunikačních technologií |
| Source Sets | Czech ETDs |
| Language | Slovak |
| Detected Language | English |
| Type | info:eu-repo/semantics/masterThesis |
| Rights | info:eu-repo/semantics/restrictedAccess |
Page generated in 0.002 seconds