Objective: To assess the effects of ceramic opacity and thickness on delivered radiant exposure and degree of conversion and microhardness of the light-cured resin cement.
Materials and Methods: IPS e-Max ceramic discs (Ivoclar Vivadent) were fabricated in 3 thicknesses (0.5, 1.0, and 1.5mm) and 4 opacities (HT, LT, MO, HO) (n=3/per group). Light-cured resin cement (Variolink Veneer Luting Cement - shade MVO, Ivoclar Vivadent) 50µm thick was cured through these ceramics disks using a quartz tungsten halogen curing light unit (Optilux 501, Kerr) with its radiant exposure measured by MARC from a fixed distance (1.5mm). Knoop microhardness was used to evaluate the bottom degree of cure and was correlated with the radiant exposure deliverd. Descriptive statistics were conducted. One- and two-way ANOVA with post-hoc Tukey's HSD test, Pearson correlation test, the simple linear regression analysis were used for the statistical analyses (alpha=0.05).
Results: Significant interaction was found between ceramic thickness and opacity on radiant exposure (p=0.0078). Subsequent analyses demonstrated that there was a significant simple effect for opacity and for thickness on radiant exposure under different conditions of thickness and opacity. A significant relationship was found between resin cement microhardness and radiant exposure (p=0.0001) below 4.5 J/cm2. Moreover, the Pearson correlation coefficient of 0.93 indicated a strong correlation between the two variables below 4.5 J/cm2 of radiant exposure delivered.
Conclusion: Ceramic opacity and thickness affect the polymerization of light-cured resin cements and need to be considered and compensated for when bonding indirect restorations. Based upon the findings of this preliminary study, the final study is ongoing.
| Identifer | oai:union.ndltd.org:uiowa.edu/oai:ir.uiowa.edu:etd-5325 |
| Date | 01 July 2014 |
| Creators | Alghaith, Lamya Saud M. |
| Contributors | Denehy, Gerald E., Armstrong, Steven R. |
| Publisher | University of Iowa |
| Source Sets | University of Iowa |
| Language | English |
| Detected Language | English |
| Type | thesis |
| Format | application/pdf |
| Source | Theses and Dissertations |
| Rights | Copyright 2014 Lamya Alghaith |
Page generated in 0.0024 seconds