In this work, organic solar cells of the configuration ITO/Pedot:PSS/CuPc/PTCBI/Al (Indium tin oxide/poly(3,4-ethylenedioxythiophene): polystyrene sulfonic acid/copper phthalocyanine/3,4,9,10-perylenetetracarboxylic bisbenzimidazole/aluminum) were investigated. A high open-circuit voltage (Voc) of 1.15 V was obtained when the PTCBI layer was 7 nm thick. Lower Voc values were observed for the same structure with silver, copper and gold electrodes instead of aluminum. However, short-circuit current density (Jsc) with these electrodes was much higher (4 mA/cm2) than in the case of aluminum (0.12 mA/cm2). Results were interpreted in terms of a modified CuPc/Al Schottky diode for the thin PTCBI case and a CuPc/PTCBI heterojunction for the thick PTCBI case. Also, the formation of a thin, protective aluminum oxide layer under the aluminum electrode was postulated. For devices with silver, copper and gold electrodes, absence of this protective layer was thought to be the cause of a relatively lower Voc and higher Jsc.
| Identifer | oai:union.ndltd.org:uky.edu/oai:uknowledge.uky.edu:gradschool_theses-1268 |
| Date | 01 January 2005 |
| Creators | Parthasarathy, Balaji |
| Publisher | UKnowledge |
| Source Sets | University of Kentucky |
| Detected Language | English |
| Type | text |
| Format | application/pdf |
| Source | University of Kentucky Master's Theses |
Page generated in 0.0021 seconds