Applications of Hot Melt Extrusion (HME) in pharmaceuticals have become increasingly popular over the years but nonetheless a few obstacles still remain before wide scale implementation. In many instances these improvements are related to both processing and product performance. It is observed that HME process optimisation is majorly focused on the active pharmaceutical ingredient's (API) properties. Characterising polymeric properties for their suitability in HME should be equally studied since the impact of excipients on both product and process performance is just as vital. In this work, two well-established cellulose ester derivatives: Hydroxy Propyl Methyl Cellulose Acetate Succinate (HPMCAS) and Hydroxy Propyl Methyl Cellulose Phthalate (HPMCP) are studied for their HME suitability. Their thermal, thermodynamic, rheological, thermo-chemical and degradation kinetic properties were evaluated with model plasticisers and APIs. It was found the thermal properties of HPMCP are severely compromised whereas HPMCAS is more stable in the processing zone of 150 to 200 °C. Thermodynamic properties revealed that both polymers share an important solubility parameter range (20-30 MPa P1/2P) where the majority of plasticisers and BCS class II APIs lie. Thus, greater miscibility/solubility can be expected. Further, the processability of these two polymers investigated by rheometric measurements showed HPMCAS possesses better flow properties than HPMCP because HPMCP forms a weak network of chain interactions at a molecular level. However, adding plasticisers such as PEG and TEC the flow properties of HPMCP can be tailored. The study also showed that plasticisers have a major influence on thermo-chemical and kinetic properties of polymers. For instance, PEG reduced polymer degradation with reversal in kinetic parameters whereas blends of CA produced detrimental effects and increased polymer degradation with reduction in onset degradation temperatures. Further, both polymers are observed to be chemically reactive with the APIs containing free -OH, -SOR2RN- and -NH2 groups. Finally, these properties prove that suitability of HPMCP is highly debated for HME and demands great care in use while that of HPMCAS is relatively better than HPMCP in many instances.

Applications of Hot Melt Extrusion (HME) in pharmaceuticals have become increasingly popular over the years but nonetheless a few obstacles still remain before wide scale implementation. In many instances these improvements are related to both processing and product performance. It is observed that HME process optimisation is majorly focused on the active pharmaceutical ingredient's (API) properties. Characterising polymeric properties for their suitability in HME should be equally studied since the impact of excipients on both product and process performance is just as vital. In this work, two well-established cellulose ester derivatives: Hydroxy Propyl Methyl Cellulose Acetate Succinate (HPMCAS) and Hydroxy Propyl Methyl Cellulose Phthalate (HPMCP) are studied for their HME suitability. Their thermal, thermodynamic, rheological, thermo-chemical and degradation kinetic properties were evaluated with model plasticisers and APIs. It was found the thermal properties of HPMCP are severely compromised whereas HPMCAS is more stable in the processing zone of 150 to 200 °C. Thermodynamic properties revealed that both polymers share an important solubility parameter range (20-30 MPa P1/2P) where the majority of plasticisers and BCS class II APIs lie. Thus, greater miscibility/solubility can be expected. Further, the processability of these two polymers investigated by rheometric measurements showed HPMCAS possesses better flow properties than HPMCP because HPMCP forms a weak network of chain interactions at a molecular level. However, adding plasticisers such as PEG and TEC the flow properties of HPMCP can be tailored. The study also showed that plasticisers have a major influence on thermo-chemical and kinetic properties of polymers. For instance, PEG reduced polymer degradation with reversal in kinetic parameters whereas blends of CA produced detrimental effects and increased polymer degradation with reduction in onset degradation temperatures. Further, both polymers are observed to be chemically reactive with the APIs containing free -OH, -SOR2RN- and -NH2 groups. Finally, these properties prove that suitability of HPMCP is highly debated for HME and demands great care in use while that of HPMCAS is relatively better than HPMCP in many instances.

No / A systematic identification of the degradation products of hydroxypropyl methylcellulose phthalate (HPMCP) during hot melt extrusion (HME) has been performed. A reverse phase HPLC method was developed for the extrudates of both hydroxypropyl methylcellulose acetate succinate (HPMCAS) and HPMCP polymers to quantify their thermal hydrolytic products: acetic acid (AA), succinic acid (SA) for HPMCAS and phthalic acid (PA) for HPMCP, without hydrolysing the polymers in strong alkaline solutions. The polymers were extruded in the temperature range of 160-190 degrees C at different screw rotation speeds and hydrolytic impurities were analysed. Investigation of extruded HPMCP showed an additional thermal degradation product, who is structural elucidation revealed to be phthalic anhydride (PAH). Moreover, two environmental analytical impurities, dimethyl phthalate and methyl benzoate formed in situ were recorded on GC-MS and their origin was found to be associated with PAH derivatization. Using the experimental data gathered during this study, a degradation mechanism for HPMCP is proposed.