<p> Nanoparticles on a substrate have numerous applications in nanotechnology, from enhancements to solar cell efficiency to improvements in carbon nanotube growth. Producing nanoparticles in a cheap fashion with some control over size and spacing is difficult to do, but desired. This work presents a novel method for altering the radius and pitch distributions of nickel and gold nanoparticles in a scalable fashion. The introduction of alumina capping layers to thin nickel films during a pulsed laser-induced dewetting process has yielded reductions in the mean and standard deviation of radii and pitch for dewet nanoparticles. Carbon nanotube mats grown on these samples show a much thicker mat for the capped case. The same capping layers have produced an opposite effect of increased nanoparticle size and spacing during a solid state dewetting process of a gold film. These results also show a decrease in the magnitude of the effect as the capping layer thickness increases. Since the subject of research interest for using these nanoparticles has shifted towards producing ordered arrays with size and spacing control, the uncertainty in the values of these distributions needs to be quantified for any form of meaningful comparison to be made between fabrication methods. Presented here is a first step in the uncertainty analysis of such samples via synthetic images producing error distributions.</p>

No description available.

The deposition efficiencies of a number of electroless nickel and cobalt plating solutions were studied and in the case of nickel compared with a commercial plating solution Nifoss 80. At the optimum plating conditions (92ºC and pH 4.5) Nifoss 80 produced nickel layers most efficiently, the alkaline cobalt solution operated most efficiently at 90ºC and pH 9. The methods of producing compostte layers containing 2-3 µm carbide particles and chromium powder is described. Nickel and cobalt layers containing approximately 27% carbide particles, or 40% (Ni) and 30% (Co) chromium particles by volume were obtained. This value is independent of the particle concentration in the plating solution within the range (20~200 g/l). Hardness of the nickel. as deposited was 515 Hv, this was increased to a maximum of 1155 Hv by heat treatment at 200ºC for 5 hours in vacuum. Incorporation. of .chromium carbide particles resulted in a maximum hardness of 1225 Hv after heating at 500ºC for 5 hours in vacuum and chromium particles resulted in a maximum hardness of 16S0 Hv after heat treatment at 400ºC for 2 hours in vacuum. Similarly the hardness of cobalt as deposited was 600 Hv, this was increased to a maximum of 1300 Hv after heat treatment at 400ºC for 1 hour. Incorporation of chromium carbide particles resulted jn a maximum hardness of 1405 Hv after heating at 400ºC for 5 hours in vacuum and chromium particles resulted in a maximum hardness of 1440 Hv after. heat treating for 2 hours at 400ºC in vacuum. The structure of the deposits was studied by optical and scanning electron microscopy. The wear rate and coefficient of friction was determined by a pin and disc method. Wear rate and coefficient of friction decreased with increase in hardness. The wear resistance of the materials was also determined using a simulated forging test. Dies made of standard die steel were coated and the wear rates of the layers as deposited and after heat treatment were compared with those of uncoated tools. The wear resistance generally increased with hardness, it was 50-75% more than the uncoated die steel. Acetic acid salt spray test and outdoor exposure for six months was used to study the corrosion behaviour of the deposits and potentiodynamic curves plotted to find their corrosion potential. Nickel deposit exhibited less staining than carbide composite deposits and nickel-chromium deposits had the most noble corrosion potential.

Microstructural fracture processes in a BS4360 Grade 50D structural steel with lower sulphur content were studied in smooth tensile specimen tests and Charpy-size bend bar tests. Based on the experimental analysis, an experimental void growth relation with the plastic strain and stress triaxiality and multiplying factor on void growth were determined. Experimental results show that the void growth relation can be reasonably used to estimate the constraint in the specimens containing the notch or crack, also they can be used to evaluate the variations of the stress triaxiality in front of the notch and crack tip under general yielding condition. Side-grooves obviously increase the constraint of the CVN specimens. Strain hardening leads to increasing the stress triaxiality, and decelerating the net void growth. This is especially true for the values of stress triaxiality more than about one. Additionally, the effect of the stress triaxiality on the critical void growth corresponding to the onset of ductile tearing was preliminarily investigated. In this work, a large number of smaller specimens were tested to investigate the ductile-brittle transition behaviour of the structural steel. A void growth rate explanation was suggested for evaluating the temperature transition behaviour. The elastic-plastic fracture tough-ness values based on small specimen tests, such as pre-cracked side-grooved bending specimen and short bar tensile specimen, may give large overestimates of the plane strain fracture toughness.

No description available.

No description available.

The.use of high-chromium cast irons for abrasive wear resistance is restricted due to their poor fracture toughness properties. An.attempt was made to improve the fracture characteristics by altering the distribution, size and.shape of the eutectic carbide phase without sacrificing their excellent wear resistance. This was achieved by additions of molybdenum or tungsten followed by high temperature heat treatments. The absence of these alloying elements or replacement of them with vanadium or manganese did not show any significant effect and the continuous eutectic carbide morphology remained the same after application of high temperature heat treatments. The fracture characteristics of the alloys with these metallurgical variables were evaluated for both sharp-cracks and blunt notches. The results were used in conjunction with metallographic and fractographic observations to establish possible failure mechanisms. The fracture mechanism of the austenitic alloys was found to be controlled not only by the volume percent but was also greatly influenced by the size and distribution of the eutectic carbides. On the other hand, the fracture mechanism of martensitic alloys was independent of the eutectic carbide morphology. The uniformity of the secondary carbide precipitation during hardening heat treatments was shown to be a reason for consistant fracture toughness results being obtained with this series of alloys although their eutectic carbide morphologies were different. The collected data were applied to a model which incorporated the microstructural parameters and correlated them with the experimentally obtained valid stress intensity factors. The stress intensity coefficients of different short-bar fracture toughness test specimens were evaluated from analytical and experimental compliance studies. The.validity and applicability of this non-standard testing technique for determination of the fracture toughness of high-chromium cast irons were investigated. The results obtained correlated well with the valid results obtained from standard fracture toughness tests.

No description available.

No description available.

No description available.