Dissertação (mestrado)—Universidade de Brasília, Instituto de Física, 2009. / Submitted by Raquel Viana (tempestade_b@hotmail.com) on 2010-03-22T20:05:27Z No. of bitstreams: 1 2009_GabrielaCunhaPossa.pdf: 1320756 bytes, checksum: 3df92e6a7fe87ee48d9a57c93af4760f (MD5) / Approved for entry into archive by Daniel Ribeiro(daniel@bce.unb.br) on 2010-04-06T20:46:30Z (GMT) No. of bitstreams: 1 2009_GabrielaCunhaPossa.pdf: 1320756 bytes, checksum: 3df92e6a7fe87ee48d9a57c93af4760f (MD5) / Made available in DSpace on 2010-04-06T20:46:30Z (GMT). No. of bitstreams: 1 2009_GabrielaCunhaPossa.pdf: 1320756 bytes, checksum: 3df92e6a7fe87ee48d9a57c93af4760f (MD5) Previous issue date: 2009-03 / O Laboratório de Plasmas do Instituto de Física da Universidade de Brasília (LP) vem trabalhando desde 2002 com o Projeto PHALL, que consiste no desenvolvimento e caracterização de um sistema de propulsão a plasma por efeito Hall, indicado para controle de atitude de satélites e missões espaciais de longa duração. O grande diferencial deste propulsor consiste na utilização de ímas permanentes para geração do campo magnético e confinamento dos elétrons para formação da corrente Hall, o que faz com que o consumo energético do propulsor seja reduzido, tornando-se mais promissor para a capacitação espacial. Um dos fenômenos que pode influenciar significativamente no desempenho de propulsores a plasma é a ocorrência de instabilidades. Neste trabalho analisamos as possíveis instabilidades que podem ocorrer no interior do canal de aceleração através de um desenvolvimento teórico e propomos a utilização de um sistema para detecção das mesmas a partir de uma sonda detectora de RF (rádio freqüência). _________________________________________________________________________________________ ABSTRACT / The Plasma Laboratory of UnB has been developing a Hall Thruster since 2002. The project consists on the construction and charactrerization of a plasma propulsion engine based on the Hall Effect. This thrusting system is designed to be used in satellite attitude control and long term space missions. A great advantage of this kind of thruster is the production of a steady state magnetic field by permanent magnets providing electral trapping and Hall Current generation within a significant decrease on the energy used and thus turning this thruster into a good option when it comes to space usage. One of the phenomena that may significantly interfere in the device’s performance is the occurrence of instabilities. In this work, we trated the theory of instabilities that can occur inside the Hall channel and, in order to better understand the oscillations that occur during the thruster’s operation we propose the use of a instability detection system based on a RF (radio frequency) detection probe.

Adições de Ti-C e Cr refinam o grão em nanocompósitos de Nd-Fe-B, aumentando substancialmente o valor de seu campo coercivo Hc. Isto motivou a investigação do efeito da adição de Ti-C e Cr em nanocompósitos de Pr-Fe-B e em outros nanocompóstitos à base de Nd-Fe-B. Fitas metálicas das composições (Pr9,5Fe84,5B6)0,97-x(TiC)0,03Crx (x = 0; 0,0025; 0,005; 0,0075; 0,01) e (Nd9,5Fe84,5B6)0,97-x (TiC)0,03Crx (x = 0,005; 0,01) foram produzidas por resfriamento rápido. Medidas de magnetização em campos magnéticos de até 90 kOe mostraram que os materiais contendo Cr possuem Hc substancialmente maior do que os demais sem. Para um nanocompósito de Pr com 1% Cr, o campo coercivo obtido foi Hc = 12,5 kOe, enquanto que para um nanocompósito de Pr com 0% Cr obtivemos um Hc = 5,1 kOe. O produto energético máximo da amostra com 1% Cr foi de, aproximadamente, 13,6 MGOe, valor este limitado pela remanência. Uma análise do difratograma de raios X mostrou que as fitas à base de Pr-Fe-B com 1%Cr consistem basicamente de uma fase Pr2Fe14B dura e uma fase α-Fe mole. Uma espectroscopia Mössbauer foi realizada em 300 K e mostrou uma redução dos campos hiperfinos devido à adição do Cr. Também foi realizada uma microscopia eletrônica de transmissão na amostra Pr-Fe-B com 1% Cr e os resultados mostraram que o nanocompósito possui um tamanho de grão maior do que o material sem Cr, sendo que a microestrutura majoritária são de grãos constituídos de α-Fe, de tamanho médio de 100 nm, imersos numa matriz de Pr2Fe14B. / Submitted by Marcelo Teixeira (mvteixeira@ucs.br) on 2014-05-30T15:59:14Z No. of bitstreams: 1 Dissertacao Vinicius Cappellano de Franco.pdf: 2554552 bytes, checksum: ca6455aec67ec4bd99efc6bdb3497dc6 (MD5) / Made available in DSpace on 2014-05-30T15:59:14Z (GMT). No. of bitstreams: 1 Dissertacao Vinicius Cappellano de Franco.pdf: 2554552 bytes, checksum: ca6455aec67ec4bd99efc6bdb3497dc6 (MD5) / The addition of both Ti and Cr-C refine the grains in nanocomposites of Nd-Fe-B, increasing substantially the coercive field Hc . This motived our investigation of the effect of the addition of Ti-C and Cr to nanocomposites of Pr-Fe-B and Nd-Fe-B. Ribbons compositions (Pr9,5Fe84,5B6)0,97-x(TiC)0,03Crx (x = 0; 0,0025; 0,005; 0,0075; 0,01) and (Nd9,5Fe84,5B6)0,97-x (TiC)0,03Crx (x = 0,005; 0,01) were produced by melt-spinning. Magnetization measures in fields up to 90 kOe showed that materials containing Cr have substantially higher Hc than the other materials without Cr. For a Pr nanocomposites with 1% Cr, the coercive field Hc was 12.5 kOe, while for a Pr nanocomposites with 0% Cr, Hc = 5.1 kOe. For the sample with 1% Cr, the maximum energy product was approximately 13.6 MGOe, a value limited by the remanence. The X-ray diffractogram analysis showed that the ribbons based on Pr-Fe-B with 1% Cr consist basically of a Pr2Fe14B hard phase and an α-Fe soft phase. Mössbauer spectroscopy was performed at 300 K and showed a reduction of the hyperfine field due to the addition of Cr. Transmission electronic microscopy of the Pr-Fe-B sample with 1% Cr showed that the nanocomposites have a grain size larger than the material without Cr, the microstructure consisting of α Fe grains, with an average size of 100 nm, in a matrix of Pr2Fe14B.

Adições de Ti-C e Cr refinam o grão em nanocompósitos de Nd-Fe-B, aumentando substancialmente o valor de seu campo coercivo Hc. Isto motivou a investigação do efeito da adição de Ti-C e Cr em nanocompósitos de Pr-Fe-B e em outros nanocompóstitos à base de Nd-Fe-B. Fitas metálicas das composições (Pr9,5Fe84,5B6)0,97-x(TiC)0,03Crx (x = 0; 0,0025; 0,005; 0,0075; 0,01) e (Nd9,5Fe84,5B6)0,97-x (TiC)0,03Crx (x = 0,005; 0,01) foram produzidas por resfriamento rápido. Medidas de magnetização em campos magnéticos de até 90 kOe mostraram que os materiais contendo Cr possuem Hc substancialmente maior do que os demais sem. Para um nanocompósito de Pr com 1% Cr, o campo coercivo obtido foi Hc = 12,5 kOe, enquanto que para um nanocompósito de Pr com 0% Cr obtivemos um Hc = 5,1 kOe. O produto energético máximo da amostra com 1% Cr foi de, aproximadamente, 13,6 MGOe, valor este limitado pela remanência. Uma análise do difratograma de raios X mostrou que as fitas à base de Pr-Fe-B com 1%Cr consistem basicamente de uma fase Pr2Fe14B dura e uma fase α-Fe mole. Uma espectroscopia Mössbauer foi realizada em 300 K e mostrou uma redução dos campos hiperfinos devido à adição do Cr. Também foi realizada uma microscopia eletrônica de transmissão na amostra Pr-Fe-B com 1% Cr e os resultados mostraram que o nanocompósito possui um tamanho de grão maior do que o material sem Cr, sendo que a microestrutura majoritária são de grãos constituídos de α-Fe, de tamanho médio de 100 nm, imersos numa matriz de Pr2Fe14B. / The addition of both Ti and Cr-C refine the grains in nanocomposites of Nd-Fe-B, increasing substantially the coercive field Hc . This motived our investigation of the effect of the addition of Ti-C and Cr to nanocomposites of Pr-Fe-B and Nd-Fe-B. Ribbons compositions (Pr9,5Fe84,5B6)0,97-x(TiC)0,03Crx (x = 0; 0,0025; 0,005; 0,0075; 0,01) and (Nd9,5Fe84,5B6)0,97-x (TiC)0,03Crx (x = 0,005; 0,01) were produced by melt-spinning. Magnetization measures in fields up to 90 kOe showed that materials containing Cr have substantially higher Hc than the other materials without Cr. For a Pr nanocomposites with 1% Cr, the coercive field Hc was 12.5 kOe, while for a Pr nanocomposites with 0% Cr, Hc = 5.1 kOe. For the sample with 1% Cr, the maximum energy product was approximately 13.6 MGOe, a value limited by the remanence. The X-ray diffractogram analysis showed that the ribbons based on Pr-Fe-B with 1% Cr consist basically of a Pr2Fe14B hard phase and an α-Fe soft phase. Mössbauer spectroscopy was performed at 300 K and showed a reduction of the hyperfine field due to the addition of Cr. Transmission electronic microscopy of the Pr-Fe-B sample with 1% Cr showed that the nanocomposites have a grain size larger than the material without Cr, the microstructure consisting of α Fe grains, with an average size of 100 nm, in a matrix of Pr2Fe14B.