Submitted by Fabricia Fialho Reginato (fabriciar) on 2015-06-27T00:47:04Z No. of bitstreams: 1 MarianaBattisti.pdf: 4940838 bytes, checksum: da6b432c65c732aae6b2315e828e6836 (MD5) / Made available in DSpace on 2015-06-27T00:47:04Z (GMT). No. of bitstreams: 1 MarianaBattisti.pdf: 4940838 bytes, checksum: da6b432c65c732aae6b2315e828e6836 (MD5) Previous issue date: 2013-03-27 / CAPES - Coordenação de Aperfeiçoamento de Pessoal de Nível Superior / FAPERGS - Fundação de Amparo à Pesquisa do Estado do Rio Grande do Sul / FINEP - Financiadora de Estudos e Projetos / O concreto é o material de construção mais empregado no mundo, consumindo grandes volumes de recursos naturais não renováveis, além da obtenção de matérias primas para sua produção causar grandes impactos ambientais. Deficiências do concreto relativas às propriedades de durabilidade podem diminuir a vida útil das estruturas, gerando resíduos precocemente, ou então necessitando de intervenções não previstas. A incorporação de agregados reciclados de concreto na produção de concreto vem sendo proposto como substituição parcial do agregado natural. No entanto, seu emprego pode aumentar a porosidade do concreto e diminuir sua durabilidade. A utilização de cinza de casca de arroz pode trazer melhorias nas propriedades dos concretos, principalmente quando se refere à penetração de íons cloreto e às propriedades mecânicas. O objetivo deste trabalho é avaliar a influência da cinza de casca de arroz na penetração de íons cloreto em concretos com agregado reciclado de concreto. Foram produzidos concretos com 0; 25 e 50% de agregado reciclado em substituição ao agregado natural; 0; 10 e 20% de substituição de cimento por cinza de casca de arroz; e relações água/aglomerante iguais a 0,42, 0,53 e 0,64. A resistência à compressão foi analisada aos 7, 28, 63 e 91 dias. Os ensaios de durabilidade englobaram os ensaios de absorção de água por capilaridade e dois métodos acelerados de penetração de íons cloretos: ASTM C1202 e NT Build 492, comumente empregados em pesquisas científicas. Os resultados mostram, em média, que a cinza de casca de arroz trouxe benefícios ao concreto com agregado reciclado de concreto em todas as propriedades estudadas. O comportamento observado pode ser atribuído a uma possível interação entre o agregado reciclado e o emprego da cinza de casca de arroz, em decorrência de uma reação pozolânica da cinza com produtos de hidratação da pasta do agregado reciclado e a um efeito microfíler da mesma nos poros deste agregado. O melhor desempenho foi obtido com concreto produzido com 50% de agregado reciclado de concreto e 20% de cinza de casca de arroz, com um aumento médio da resistência à penetração de íons cloreto de 91% pela ASTM C1202 e 64% pelo NT Build 492, em relação aos concretos de mesmo teor de agregado reciclado e sem cinza de casca de arroz. / The durability of building materials is emphasized when it searches to maintain the useful life of the construction design or extend it. Corrosion reinforcement in concrete is among one major problem that affects the constructions throughout the world. Chloride ion is one of the agents that can induce the corrosion reinforcement in concrete. For this reason, research about the durability of construction materials in severe environments gained space in the scientific community. The use of recycled concrete aggregate as replacement of natural aggregate has been studied to solve the question about non-renewable raw materials. But, these recycled waste as aggregate can increase the concrete porosity and reduce its durability. The rice husk ash has been employed as supplementary material in Portland cement concrete to get a more sustainable concrete and improve its durability, mainly related to chloride ingress. The aim of this research was to study the influence of rice husk ash on the chloride penetration in concrete made with recycled concrete aggregate. The natural coarse aggregates were replaced by recycled concrete aggregates in amounts of 0; 25 and 50%. The rice husk ash was employed as replacement of Portland cement in 0; 10 and 20%. Three water/binder ratios were used in concrete production: 0.42, 0.53 and 0.64. The compressive strength tests were conducted at 7, 28, 63 and 91 days age. The concrete resistance to chloride ingress was tested by the ASTM C1202 test method and by the NT Build 492 test method. The results of all studied properties showed that the use of rice husk ash can improve the concrete resistance against chloride ingress in concrete made with recycled concrete aggregate. This behavior can be attributed to the reduction of the porosity of recycled concrete aggregate due to interaction of rice husk ash with the calcium hydroxide of this aggregate as well as due to micro filler effect. The best performance was obtained in concrete with 50% of recycled concrete aggregate and 20% of rice husk ash. The resistance against chloride ingress in relation to the same concrete without rice husk ash was increased 91% in average when tested by ASTM C1202, and 64% when tested by NT Build 492.

Submitted by Johnny Rodrigues (johnnyrodrigues@ufcg.edu.br) on 2018-03-23T22:49:00Z No. of bitstreams: 1 KATYA DIAS NERI - TESE PPGEQ 2015..pdf: 3049984 bytes, checksum: 969f88ceb2c88dcdfa2fecfab097dea8 (MD5) / Made available in DSpace on 2018-03-23T22:49:00Z (GMT). No. of bitstreams: 1 KATYA DIAS NERI - TESE PPGEQ 2015..pdf: 3049984 bytes, checksum: 969f88ceb2c88dcdfa2fecfab097dea8 (MD5) Previous issue date: 2015-04-17 / O íon cloreto é um dos agentes mais agressivos no processo corrosivo em concreto armado. A chegada de cloretos nas proximidades da armadura, por si só, não representa o início do processo de corrosão. Assim, é necessário que esses íons estejam em quantidades suficientes para desencadear o processo corrosivo, denominado teor crítico de cloretos. Neste trabalho, estuda-se o comportamento de estruturas de concreto com relações água/aglomerante 0,4; 0,5 e 0,6 com adição de sílica ou metacaulim submetidos ao ataque químico em solução com cloreto de sódio (NaCl), 1M em ensaios acelerados induzidos por campo elétrico e novo ensaio proposto com aplicação do campo magnético, com objetivo de avaliar o teor crítico de cloretos no concreto com adição de pozolanas. Foram realizadas medidas de polarização linear e impedância eletroquímica para avaliar o início do processo de corrosão. Uma vez identificado o início da corrosão, foram realizadas determinações de pH, teores de cloretos totais e livres por titulação potenciométrica, e o teor crítico [Cl-]/[OH-] em amostras próximas à armadura. Observou-se inicialmente no ensaio de resistência a compressão, o índice de vazios e a absorção em água que a relação água/aglomerante e o tipo de pozolana são fatores determinantes para durabilidade do concreto. Os concretos com adição de pozolanas apresentaram ganho de resistência superior ao concreto referência, e consequentemente diminuíram o índice de vázios e absorção de água. Para o ensaio acelerado de migração de penetração de cloretos, com aplicação de campo elétrico dos concretos a/agl. 0.4 e 0.5, com adição de pozolanas, aumentaram o tempo de ensaio e reduziram a densidade de corrente de corrosão (taxa de corrosão) em relação aos concretos de referência. Consequentemente apresentou-se uma retenção de cloretos que resultou em valores de teores de cloretos livres e totais baixos e alta relação iônica [Cl-]/[OH-]. Para o concreto a/agl. 0.6, as adições pozolânicas promoveram uma ação positiva no efeito físico dos Cps, porém quimicamente a ação foi negativa, que possivelmente provocou a saída precoce dos Cps nos ensaios acelerados de migração dos cloretos. Para os ensaios acelerados de indução de cloretos com aplicação do campo magnéticos, obteve-se o mesmo comportamento que o elétrico nos concretos a/agl. 0.4 e 0.5 com retenção de cloretos livres e totais em concretos com adição. Apresentou mesmo perfil crescente da relação iônica [Cl-]/[OH-]. Porém, o ensaio magnético apresentou melhor desempenho que o elétrico, pois sua sensibilidade detectou teores de cloretos livres e relação iônica [Cl-]/[OH-] menores.