Made available in DSpace on 2017-07-21T20:43:44Z (GMT). No. of bitstreams: 1 Sheila Cristina Jacumasso.pdf: 3640428 bytes, checksum: 9f48682e159a5b7129a15abc7bb73945 (MD5) Previous issue date: 2014-06-02 / Coordenação de Aperfeiçoamento de Pessoal de Nível Superior / The AA7050 class from the 7XXX series alloys based on Al-Zn-Mg-Cu are widely used in aerospace structures and fuselage components, when the same are subjected to high stress loading due to its high ratio mechanical strength to density, in addition, to its corrosion resistance. The increased resistance of these alloys is obtained by heat treatment that involves solution treatment and ageing followed precipitation of a fine and homogeneous phase from the own chemical composition. In this, the present study aimed to perform the of AA7050 aluminum alloy microstructural characterization with different ageing heat treatment from the T7451, T6 and T6I4-65 conditions. Thus, different characterization techniques from the Optical Microscopy (OM), Scanning Electron Microscopy (SEM), Atomic Force Microscopy (AFM), Extraction of second phase particles, X-ray Diffraction (XRD) and Transmission Electron Microscopy (TEM) were used. It was evaluated which condition results is higher precipitation hardening phases that are responsible for the increased resistance of the alloy. The most significant results were obtained by TEM where it was possible to determine the morphology of the GPII zones in needles form with approximate size of 30nm and 10nm for both T6 and T6I4-65 conditions, respectively. Moreover, the metastable η' phase was identified in platelets form in the T7451, T6 and T6I4-65 conditions with approximate size of 50nm, 20nm and 10nm, respectively. The surface roughness analyses obtained by AFM have revealed that the T6I4-65 condition has higher surface roughness (Ra=14,87nm) when compared to the T7451 (Ra=7,65nm) and T6 (Ra=8,35nm) conditions. Indicating in this case, a higher density of small particles homogeneously distributed in the T6I4-65 aluminum alloy matrix. / As ligas da série 7XXX, da classe AA7050, à base de Al-Zn-Mg-Cu, são muito utilizadas na indústria aeroespacial, em estruturas de fuselagem e componentes sob alta tensão de carregamento, devido à sua alta relação entre resistência mecânica e densidade, além de sua resistência à corrosão. O aumento da resistência destas ligas é obtido por tratamento térmico de solubilização e envelhecimento, através da precipitação de uma fase fina e homogênea, proveniente da própria composição química. Neste contexto, o presente trabalho teve como objetivo principal realizar a caracterização microestrutural de uma liga de alumínio AA7050, submetida a diferentes tratamentos térmicos de envelhecimento nas condições T7451, T6 e T6I4-65. Desse modo, fez-se o uso de diferentes técnicas de caracterização entre elas Microscopia Ótica (MO), Microscopia Eletrônica de Varredura (MEV), Microscopia de Força Atômica (AFM), Extração de Partículas de segunda fase, Difração de Raios X (DRX) e Microscopia Eletrônica de Transmissão. Consequentemente, avaliou-se qual condição apresenta maior precipitação de fases endurecedoras que são responsáveis pelo aumento de resistência da liga. Os resultados mais significativos foram obtidos por MET onde foi possível determinar a morfologia das zonas GPII presentes na forma acicular (needles) com tamanho aproximado de 30nm na condição T6 e 10nm na condição T6I4-65. A fase metaestável η’ foi identificada na forma de plaquetas finas (platelets) nas condições T7451, T6 e T6I4-65 com tamanho aproximado de 50nm, 20nm e 10nm respectivamente. A rugosidade superficial obtida por AFM revelou que a condição T6I4-65 apresenta maior rugosidade superficial (Ra=14,87nm) quando comparado às condições T7451(Ra=7,65nm) e T6 (Ra=8,35nm), indicando maior densidade de partículas de pequena dimensão distribuída homogeneamente na matriz da liga de alumínio.

Made available in DSpace on 2017-07-21T20:42:40Z (GMT). No. of bitstreams: 1 DANIELLE C CAMILO.pdf: 6225328 bytes, checksum: 7aa2969809ed8acd7663b74ba2aa6efd (MD5) Previous issue date: 2013-07-10 / Coordenação de Aperfeiçoamento de Pessoal de Nível Superior / The emphasis of this work was to characterize the mechanical properties of aluminum alloy AA7050 subjected to cryogenic rolling and natural aging. Samples of aluminum alloy AA7050 were cryogenically rolled in four degrees of effective strain: = 0,5, = 0,9,= 1,1 and = 1,4. For each degree of deformation, the samples were naturally aged for 0 hours, 10 hours, 100 hours and 1000 hours. The analysis of the kinetics of natural aging indicated with 10 hours was achieved transform a fraction of 50%, which shows that the rate of transformation in this alloy was relatively high, requiring low energy of activation to occur. The calculated Avrami exponent was equal to 0,828 indicating that precipitation occurs in dislocations. By means of metallographic analysis evidenced a microstructural refinement, which was more intense for higher degrees of deformation. Mechanical properties were evaluated by Vickers microhardness measurements and tensile testing. The sample without deformation the hardness increase 30% in 10 hours of natural aging, reaching a stabilization from 1000 hours. For the deformed samples had an average increase in hardness from 80% after 1000 hours regardless of the degree of deformation. There was a competition between the static recovery and precipitation in the early hours of natural aging for samples more deformed (= 1,1 and = 1,4). The results also indicate that for higher degrees of deformation (= 1,1 and = 1,4) the natural aging did not affect the mechanical properties under tension significantly. On the other hand, for lower degrees of reduction, increased mechanical strength was more significant. For the initial sample, the yield strength increased 153% with 1000 hours of natural aging. A sample of ε = 0,5 and 1000 hours presented a 323% yield strength greater than as-quench sample. Furthermore, regarding all samples deformed, this condition had the highest total elongation (15%), representing an optimal combination of deformation and thermal treatment. The images of electron microscopy of the fracture surfaces revealed the occurrence of ductile fracture primarily, with plenty of dimples, for all conditions. Thermal analysis (DSC) results confirmed the high volume fraction of GP zones and η’ phase, formed in natural aging. Moreover, the deformation changed the form of DSC curves, especially at a temperature of precipitation of η' due to the increase of sites for nucleation. The EDS microanalysis, both particles in the fracture surface when the dissolved material for extraction of precipitates indicated the elements forming the phases MgZn2, Al2CuMg, Al2Cu, Al2Zn3Mg3, Mg2Si, and Al7Cu2Fe AlZnMgCu. The x-ray diffraction indicate a crystallographic texture for lower degree of reduction in the direction [110], which was associated with bimodal distribution of grain size. / A ênfase do presente trabalho foi caracterizar as propriedades mecânicas da liga de alumínio AA7050 submetida à laminação criogênica e envelhecimento natural. Amostras da liga de alumínio AA7050 foram laminadas criogenicamente em quatro graus de deformação equivalente: = 0,5; = 0,9; = 1,1 e = 1,4. Para cada grau de deformação, as amostras foram envelhecidas naturalmente por 0 hora, 10 horas, 100 horas e 1000 horas. A análise da cinética de envelhecimento natural indicou que com 10 horas de envelhecimento foi atingida uma fração transformada de 50%, o que mostra que a velocidade de transformação nessa liga é relativamente alta, exigindo baixa energia de ativação para ocorrer. O expoente de Avrami calculado foi igual a 0,828, indicando que a precipitação ocorre em discordâncias. Por meio da análise metalográfica constatou-se um refino microestrutural, o qual foi mais intenso para maiores graus de deformação. As propriedades mecânicas foram avaliadas por meio de medidas de dureza Vickers por micro-impressão e ensaio de tração uniaxial. A amostra sem deformação aumentou sua dureza em 30% nas primeiras 10 horas de envelhecimento natural, atingindo uma estabilização a partir de 100 horas. Já as amostras deformadas tiveram um aumento médio de 80% na dureza após 1000 horas, independentemente do grau de deformação. Foi observada uma competição entre a recuperação estática e a precipitação nas primeiras horas de envelhecimento natural para as amostras mais deformadas ( = 1,1 e = 1,4). Os resultados também indicam que para maiores graus de deformação ( = 1,1 e = 1,4) o envelhecimento natural não afetou as propriedades mecânicas sob tração significativamente. Por outro lado, para menores graus de redução, o aumento da resistência mecânica foi mais significativo. Para a amostra inicial, o limite de escoamento aumentou em 153% com 1000 horas de envelhecimento natural. A amostra com ε = 0,5 e 1000 horas de envelhecimento apresentou um limite de escoamento 323% maior do que a amostra inicial, solubilizada. Além disso, em relação à todas as amostras deformadas, esta condição apresentou o maior alongamento total (15%), representando uma combinação ótima de deformação e tratamento térmico. As imagens de microscopia eletrônica das superfícies de fratura revelaram a ocorrência de fratura essencialmente dúctil, com abundância de “dimples”, para todas as condições. Os resultados de análise térmica (DSC) confirmaram a elevada fração volumétrica de zonas GP e da fase η’, formadas no envelhecimento natural. Além disso, a deformação alterou a forma das curvas de DSC, principalmente na temperatura de precipitação de η’, devido ao aumento de sítios para nucleação. As microanálises por EDS, tanto das partículas na superfície de fratura quando no material dissolvido para extração de precipitados, indicaram os elementos formadores das fases MgZn2, Al2CuMg, Al2Cu, Al2Zn3Mg3, Mg2Si, Al7Cu2Fe e AlZnMgCu. As difrações de raios x indicaram textura cristalográfica para o menor grau de redução, na direção [110], o que foi associado com a distribuição bimodal de tamanho de grão.