Experiment was done in 2005–2006 years in the base of Vilnius pedagogical university in Chemistry institute. The title of this experiment is „Formation peculiarity of copper aluminates“. The author of this experiment is Jurgita Rakauskaitė and the director of this experiment is doc. dr. Raimondas Giraitis. The aim of this work was to synthesize CuAlO2 and CuAl2O4 from compounds of certain copper, alunimium nitrates and sulfates, and to compare dependance of copper aluminates formation on time and temperature. Firstly, reagents were crushed into powder, pressed and heated, changing heating time and temperature. For the reseach were used these methods: microstructural analysis, differential thermal analysis (DTA), X – ray difractional (XRD) analysis and scanning electron microscopy (SEM). When all the reseaches were finished, these conclusions were made: CuAl2O4 from nitrates begins to form at 750oC and CuAl2O4 from sulfates begins its crystalisation at 700oC. When the temperature is higher than 950oC, formation of CuAlO2 begins. The higher the temperature is, the less time the copper aluminates take to form. Copper aluminates, formed from solid phase, made small crystals and formed from liquid phase made big various shape crystals.

Šiame darbe vienfazis perovskito struktūros gadolinio aliuminatas GdAlO3 zolių-gelių metodu buvo gautas 1000 oC temperatūroje, gadolinio jonų šaltiniu naudojant Gd2O3, kompleksus sudarančiu reagentu – 1,2 etandiolį, natūralią vyno rūgštį, citrinų rūgštį arba citrinų rūgšties ir etanolamino mišinį. Sintetinant GdAlO3, gautų tyrimų rezultatai parodė, kaip yra svarbu zolių gelių procese pasirinkti tinkamas pradines medžiagas bei kompleksus su metalais sudarančius reagentus: gadolinio jonų šaltiniu naudojant Gd2O3 buvo gauti geresni rezultatai nei naudojant Gd(NO3)3•6H2O, vienfazis GdAlO3 gali būti sėkmingai susintetintas kompleksus sudarančiu reagentu naudojant tiek natūralią vyno rūgštį, tiek 1,2 etandiolį, tiek citrinų rūgštį, tiek citrinų rūgšties ir etanolamino mišinį. Nustatyta, kad sintetinant stronciu pakeistus gadolinio aliuminatus Gd1–xSrxAlO3– (x = 0,10, 0,25, 0,50, 0,75), tinkamesnis gadolinio jonų šaltinis yra gadolinio oksidas nei gadolinio nitratas heksahidratas, kompleksus sudarantis reagentas – EDTA nei natūrali vyno rūgštis. Vienfazis perovskito struktūros stronciu pakeistas gadolinio aliuminatas Gd0,90Sr0,10AlO3– buvo susintetintas zolių-gelių metodu 1000 oC temperatūroje, gadolinio jonų šaltiniu naudojant Gd2O3, stroncio jonų šaltiniu – Sr(NO3)2, kompleksus sudarančiu reagentu – EDTA. Be to, 800 ºC iškaitinimo temperatūra yra per maža šiems junginiams sintetinti. Pirmą kartą pasiūlytas vandeninis zolių gelių metodas lantano ir gadolinio kobaltatams... [toliau žr. visą tekstą] / In the present thesis the reported results let us to conclude that the developed aqueous sol–gel procedure could be successfully used for the low-temperature synthesis of monophasic perovskite gadolinium aluminate ceramics. It was also demonstrated that the selection of raw materials for the sol–gel processing should be done with care. Monophasic perovskite structure gadolinium aluminate GdAlO3 has been synthesized by sol gel synthesis method at 1000 oC, using gadolinium oxide as gadolinium raw material and 1.2 ethanediol, natural tartaric acid, citric acid or mixture of citric acid and ethanolamine as complexing agent. According to the XRD results, the Gd2O3 instead of Gd(NO3)36H2O preferably should be used as starting material for the preparation of GdAlO3. Monophasic perovskite structure strontium substituted gadolinium aluminate Gd0.90Sr0.10AlO3– was synthesized by the same sol gel synthesis method at 1000 oC, using gadolinium oxide as gadolinium raw material, strontium nitrate as strontium ion source and EDTA as complexing agent. It was proved that better gadolinium ion source is gadolinium oxide than gadolinium nitate hexahydrate, better complexing agent – EDTA than natural tartaric acid in the synthesis of GdAlO3 and strontium substituted Gd1–xSrxAlO3– (x = 0.10, 0.25, 0.50, 0.75) samples. According to the XRD results, increasing amount of strontium reduces amount of peaks of perovskite structure gadolinium aluminate. Besides, 800 ºC temperature is too low for the... [to full text]

In the present thesis the reported results let us to conclude that the developed aqueous sol–gel procedure could be successfully used for the low-temperature synthesis of monophasic perovskite gadolinium aluminate ceramics. It was also demonstrated that the selection of raw materials for the sol–gel processing should be done with care. Monophasic perovskite structure gadolinium aluminate GdAlO3 has been synthesized by sol gel synthesis method at 1000 oC, using gadolinium oxide as gadolinium raw material and 1.2 ethanediol, natural tartaric acid, citric acid or mixture of citric acid and ethanolamine as complexing agent. According to the XRD results, the Gd2O3 instead of Gd(NO3)36H2O preferably should be used as starting material for the preparation of GdAlO3. Monophasic perovskite structure strontium substituted gadolinium aluminate Gd0.90Sr0.10AlO3– was synthesized by the same sol gel synthesis method at 1000 oC, using gadolinium oxide as gadolinium raw material, strontium nitrate as strontium ion source and EDTA as complexing agent. It was proved that better gadolinium ion source is gadolinium oxide than gadolinium nitate hexahydrate, better complexing agent – EDTA than natural tartaric acid in the synthesis of GdAlO3 and strontium substituted Gd1–xSrxAlO3– (x = 0.10, 0.25, 0.50, 0.75) samples. According to the XRD results, increasing amount of strontium reduces amount of peaks of perovskite structure gadolinium aluminate. Besides, 800 ºC temperature is too low for the... [to full text] / Šiame darbe vienfazis perovskito struktūros gadolinio aliuminatas GdAlO3 zolių-gelių metodu buvo gautas 1000 oC temperatūroje, gadolinio jonų šaltiniu naudojant Gd2O3, kompleksus sudarančiu reagentu – 1,2 etandiolį, natūralią vyno rūgštį, citrinų rūgštį arba citrinų rūgšties ir etanolamino mišinį. Sintetinant GdAlO3, gautų tyrimų rezultatai parodė, kaip yra svarbu zolių gelių procese pasirinkti tinkamas pradines medžiagas bei kompleksus su metalais sudarančius reagentus: gadolinio jonų šaltiniu naudojant Gd2O3 buvo gauti geresni rezultatai nei naudojant Gd(NO3)3•6H2O, vienfazis GdAlO3 gali būti sėkmingai susintetintas kompleksus sudarančiu reagentu naudojant tiek natūralią vyno rūgštį, tiek 1,2 etandiolį, tiek citrinų rūgštį, tiek citrinų rūgšties ir etanolamino mišinį. Nustatyta, kad sintetinant stronciu pakeistus gadolinio aliuminatus Gd1–xSrxAlO3– (x = 0,10, 0,25, 0,50, 0,75), tinkamesnis gadolinio jonų šaltinis yra gadolinio oksidas nei gadolinio nitratas heksahidratas, kompleksus sudarantis reagentas – EDTA nei natūrali vyno rūgštis. Vienfazis perovskito struktūros stronciu pakeistas gadolinio aliuminatas Gd0,90Sr0,10AlO3– buvo susintetintas zolių-gelių metodu 1000 oC temperatūroje, gadolinio jonų šaltiniu naudojant Gd2O3, stroncio jonų šaltiniu – Sr(NO3)2, kompleksus sudarančiu reagentu – EDTA. Be to, 800 ºC iškaitinimo temperatūra yra per maža šiems junginiams sintetinti. Pirmą kartą pasiūlytas vandeninis zolių gelių metodas lantano ir gadolinio kobaltatams... [toliau žr. visą tekstą]