Thesis (Ph. D.)--University of Washington, 2001. / Vita. Includes bibliographical references (leaves 107-118).

Thesis (Ph. D.)--University of Wisconsin--Madison, 1950. / Typescript. Vita. eContent provider-neutral record in process. Description based on print version record. Includes bibliographical references (leaves 53-54).

By anodic oxidation, an aluminum plate can be covered with an amorphous or crystalline oxide layer, depending on the electrolyte used. The amorphous layer, obtained in a solution of oxalic or sulphuric acid, has a porous structure. However, the pores do not go right down to the aluminum as has been shown by many investigators, but end in a solic insulating layer, the thickness of which may be determined by capacity measurements. Corresponding to a given temperature and solic concentration of the electrolytic solution and a given formation current density, there is only one final capacity obtainable. Increasing the concentration, or temperature, or decreasing the current density, increases the final capacity obtainable. / Science, Faculty of / Physics and Astronomy, Department of / Graduate

A dissertation submitted to the Faculty of Engineering, University of the Witwatersrand, Johannesburg, in fulfillment of the requirements for the degree of Master of Science in Engineering. Johannesburg, 1998. / Experiments have been conducted at around 17000C to determine the whether carbothermic reduction of alumina is possible at these temperatures. Total pressure of the system was reduced to around 30 kPa and various metallic solvents such as copper, nickel, iron and tin were used to dissolve the metallic aluminium produced. The use of a solvent (and hence decreasing the activity of metallic aluminium) and a lower pressure are thermodynamic requirements to increase the extent of reduction under a given set of conditions. This enables the use of lower temperatures than are required under atmospheric conditions. The highest recovery of aluminium was achieved with the nickel solvent decreasing in order from iron, copper and tin. This ranking was also in accord with the extent of deviation from ideality in the respective binary solutions of these solvents with aluminiur, The nickel-aluminium system displays the largest negative deviation from ideality whereas the till, aluminium system showed a positive deviation. The rate and extent of the reduction was found to be highly dependent on temperature and pressure. The pseudo first order reaction rate was found to be the primary order for the reduction of aluminium in all the solvents used. It is also suggested that the reduction rate was controlled primarily by chemical reaction rate father than by transport processes. This is due to the extreme sensitivity of the rate and extent of the reaction to temperature. / AC2017

Thesis (Ph. D.)--Lehigh University, 2000. / Includes vita. Includes bibliographical references (leaves 158-168).

Thesis (Ph. D.)--Lehigh University, 2000. / Includes vita. Includes bibliographical references (leaves 155-166).

Thesis (M.S.)--University of Missouri, School of Mines and Metallurgy, 1940. / The entire thesis text is included in file. Typescript. Title from title screen of thesis/dissertation PDF file (viewed March 17, 2010) Includes bibliographical references (p. 32-33) and index (leaf 34).

No description available.

No description available.

No description available.