No description available.

It has been previously established that alkali silica reaction (ASR) in concrete may be controlled by blending Portland cement with suitable hydraulic or pozzolanic materials. The controlling mechanism has been attributed to the dilution of the cement's alkali content and reduced mobility of ions in concrete's pore solution. In this project an attempt has been made to identify the factors which influence the relative importance of each mechanism in the overall suppression of the reaction by the use of blended cements. The relationship between the pore solution alkalinity and ASR was explored by the use of expansive mortar bars submerged in alkaline solutions of varying concentration. This technique enabled the blended cement's control over expansion to be assessed at given `pore solution' alkali concentrations. It was established that the cement blend, the concentration and quantity of alkali present in the pore solution were the factors which determined the rate and extent of ASR. The release of alkalis into solution by Portland cements of various alkali content was studied by analysis of pore solution samples expressed from mature specimens. The specification for avoiding ASR by alkali limitation, both by alkali content of cement and the total quantity of alkali were considered. The effect on the pore solution alkalinity when a range of Portland cements were blended with various replacement materials was measured. It was found that the relationship between the type of replacement material, its alkali content and that of the cement were the factors which primarily determined the extent of the pore solution alkali dilution effect. It was confirmed that salts of alkali metals of the kinds found as common concrete contaminants were able to increase the pore solution hydroxyl ion concentration significantly. The increase was limited by the finite anion complexing ability of the cement.

It was suggested to us that compounds of the type XCH2SiR2CH2CH2Y might show interesting chemical and biological activity due to them possessing both an alpha group and a beta group. The aim of this research was to discover whether or not the alpha and beta effects interact with each other, and if so whether interaction is via steric or electronic effects. A series of compounds were made with a constant chloromethyl alpha function and varying beta functions (hydroxy, methoxy and chloro groups); plus a second series of trimethylsilyl substituted silanes with the same variety of beta functions were synthesised. The stereochemistry of the products was investigated by analysis of NMR spectra and of dipole moment data. It was found that the -chloro-substituted compounds possessed restricted rotation. The methoxy- and hydroxy-substituted compounds which displayed more or less simple triplets, appear to possess free rotation; the smaller sized hydroxy and methoxy groups seemingly no great barrier to rotation. Similarly, compounds possessing larger alpha alkyl groups appeared also to possess restricted rotation, it was concluded that for the compounds possessing large alpha or a large beta function steric effects dominate. The kinetics of the solvolysis reaction were studied. -functional alkylsilanes commonly undergo solvolysis by unimolecular elimination at remarkably enhanced rates. The -hydroxy- and -methoxy-substituted chloroethyl derivatives reacted substantially slower that their trimethylsilyl analogues, due to the electronegative chlorine pulling electrons into the Si-C bond. For compounds possessing an electronegative substituent alpha to silicon it seems it is the electronic effects that act to inhibit the beta effect.

This thesis is concerned with the analysis of phospholipids in the tear film and with the synthesis of phospholipids analogous to hydrogels. The work consists of two areas. The first area is the study of the phospholipids in the tear film, their nature and fate. The use of liquid chromatography mass spectrometry determined that the concentration of phospholipids in the tear film was less than previously thought. Thin layer chromatography showed the presence of diacylglycerides (DAGs) in the tear film at relatively high concentrations. The activity of an enzyme, phospholipase C, was found in the tear film. It was hypothesised that the low concentration of phospholipids and high concentrations of DAG in the tear film was due to the action of this enzyme. The second area of study was the synthesis of phospholipids analogous materials for use in ocular and dermal applications. For ocular applications the synthesis involved the use of the monomer N,N-dimethyl-N-(2-acryloylethyl)-N-(3-sulfopropyl) ammonium betaine (SPDA) in combination with 2-hdyroxyethyl methacrylate (HEMA). Charge-balanced membranes were also synthesised using potentially anionic monomers in conjunction with cationic monomers in stoichiometrically equivalent ratios also with HEMA as a commoner. Membranes of SPDA copolymers and charge-balanced copolymers proved to have some properties suitable for ocular applications. The dermal materials consisted of one family of partially hydrated hydrogels synthesised from SPDA in combination with ionic monomers: sodium 2-(acrylamido)-2-methyl propane sulfonate and acrylic acid-bis(3-sulfopropyl)-ester, potassium salt. A second family of partially hydrated hydrogels was synthesised from N-vinyl pyrrolidone. Both of the partially hydrated hydrogels synthesised proved to have some properties suitable for use as adhesives for the skin.

Ion exchange resins are used for many purposes in various areas of science and commerce. One example is the use of cation exchange resins in the nuclear industry for the clean up of radioactively contaminated water (for example the removal of 137Cs). However, during removal of radionuclides, the resin itself becomes radioactively contaminated, and must be treated as Intermediate Level Waste. This radioactive contamination of the resin creates a disposal problem. Conventionally, there are two main avenues of disposal for industrial wastes, landfill burial or incineration. However, these are regarded as inappropriate for the disposal of the cation exchange resin involved in this project. Thus, a method involving the use of Fenton's Reagent (Hydrogen Peroxide/soluble Iron catalyst) to destroy the resin by wet oxidation has been developed. This process converts 95% of the solid resin to gaseous CO2, thus greatly reducing the volume of radioactive waste that has to be disposed of. However, hydrogen peroxide is an expensive reagent, and is a major component of the cost of any potential plant for the destruction of ion exchange resin. The aim of my project has been to discover a way of improving the efficiency of the destruction of the resin thus reducing the cost involved in the use of hydrogen peroxide. The work on this problem has been concentrated in two main areas:-1) Use of analytical techniques such as NMR and IR to follow the process of the hydrogen peroxide destruction of both resin beads and model systems such as water soluble calixarenes. 2) Use of various physical and chemical techniques in an attempt to improve the overall efficiency of hydrogen peroxide utilization. Examples of these techniques include UV irradiation, both with and without a photocatalyst, oxygen carrying molecules and various stirring regimes.

Various monoacrylic compounds containing a hindered phenol function (e.g.3,5-di-tert.-butyl-4-hydroxy benzyl alcohol, DBBA and vinyl-3-[3',5'-di-tert.-butyl-4-hydroxy phenyl] propionate, CDBP), and a benzophenone function (2-hydroxy-4-[beta hydroxy ethoxy] benzophenone, HAEB) were synthesised and used as reactive antioxidants (AO's) for polypropylene (PP). These compounds were reacted with PP melt in the presence of low concentration of a free radical generator such a peroxide (reactive processing) to produce bound-antioxidant concentrates. The binding reaction of these AO's onto PP was found to be low and this was shown to be mainly due to competing reactions such as homopolymerisation of the antioxidant. At high concentrations of peroxide, higher binding efficiency resulted, but, this was accompanied by melt degradation of the polymer. In a special reactive processing procedure, a di- or a trifunctional reactant (referred to as coagent), e.g.tri-methylol propane tri-acrylate, Tris, and Divinyl benzene, DVB, were used with the antioxidant and this has led to an enhanced efficiency of the grating reaction of antioxidants on the polymer in the melt. The evidence suggests that this is due to copolymerisation of the antioxidants with the coagent as well as grafting of the copolymers onto the polymer backbone. Although the 'bound' AO's containing a UV stabilising function showed lower overall stabilisation effect than the unbound analogues before extraction, they were still much more effective when subjected to exhaustive solvent extraction. Furthermore, a very effective synergistic stabilising activity when two reactive AO's containing thermal and UV stabilising functions e.g. DBBA and HAEB, were reactively processed with PP in the presence of a coagent. (DX185,650)

Samples of Various industrial or pilot plant spray-dried materials were obtained from manufacturers together with details of drying conditions and feed concentrations. The samples were subjected to qualitative and semi-quantitative examination to identify structural and morphological features. The results were related to measured bulk physical properties and to drying conditions. Single particles were produced in a convective drying process Analogous to spray drying, in which different solids or mixtures of solids were dried from solutions, slurries or pastes as single suspended droplets. The localized chemical and physical structures were analysed and in some cases the retention of volatiles monitored. The results were related to experimental conditions, viz.; air temperature, initial solids concentration and the degree of feed aeration. Three distinct categories of particle morphology were identified, i.e.; crystalline, skin-forming and agglomerate. Each category is evidence of a characteristic drying behaviour which is dependent on initial solids concentration. the degree of feed aeration, and drying temperature. Powder flow ability, particle and bulk density, particle-size, particle friability, and the retention of volatiles bear a direct relationship to morphological structure. Morphologies of multicomponent mixtures were complex, but the respective migration rates of the solutes were dependent on drying temperature. Gas-film heat and SDSS transfer coefficients of single pure liquid droplets were also measured over a temperature range of 50•C to 200•C under forced convection. Balanced transfer rates were obtained attributed to droplet instability or oscillation within the airflow, demonstrated in associated work with single free-flight droplets. The results are of relevance to drier optimisation and to the optimisation of product characteristics, e.g.; particle strength and essential volatiles-retention, in convective drying.

Perturbations in the bismuth market resulted in Mining and Chemical Products Ltd., seeking further outlets in the market. Together with Manchem Ltd. they were anxious to evaluate the possibility of using bismuth compounds as a replacement for lead/calcium soaps in paint driers. A range of new organobismuth compounds were synthesised of the type RBiX2 and R3BiX2 (X= halogen, OOCR, dithiocarbamate). A variety of synthetic techniques were explored, including the use of mathematical reactions, phase-transfer catalysis and microwave energy. The preparation of a range of trivalent and pentavalent organobismuth carboxylates is reported and their infra-red , 13C, lH nmr spectra. The compounds were evaluated as paint driers and in cases found to enhance paint drying to a greater degree than the standard driers, to which they were being compared. The drying times of paint films containing the organobismuth compounds are reported, together with a comparison of the drying times with the addition of bismuth tris-diethyldithiocarbamate, which may promote the cross-linking reaction that occur in paint films during the drying process. Examples are reported to illustrate the great reductions in reaction times possible when using microwave energy. Reactions such as metallation of aromatic rings, ligand redistribution and synthesis were carried out in PTFE containers in a conventional domestic microwave oven. An X-ray diffraction study of (phenylazophenyl-C,N')mercury(II) chloride has shown it to be dimeric via long Hg-Cl bridging interactions of 3.367A. Its crystal structure is reported, together with its 13C nmr spectra and mass spectrum. The Lewis acidity of compounds of the type RBiX2 was investigated. The donor group being anchored to the organo group (R). The dithiocarbamates bis- (diethyldithiobarbamato)phenylbismuth(Ill) and [2-2-pyridyl)phenylbismuth(III) were synthesised, and their crystal structures, 14N, 13C nmr ar1d infra-red spectra are reported. Both compounds are pseudo-pentagonal bipyramidal in geometry, with two long Bi-S bonds and two short Bi-S bonds. The reaction of RBiBr2 (R= 2-(pyridyl) with various ligands is reported. The infra-red evidence suggesting that the coordination of extra ligands is accompanied by a reduction of the strength of the Bi-interaction.

Today, speciality use organoclays are being developed for an increasingly large number of specific applications. Many of these, including use in cosmetics, polishes, greases and paints, require that the material be free from abrasive impurities so that the product retains a smooth `feel'. The traditional `wet' method preparation of organoclays inherently removes abrasives naturally present in the parent mineral clay, but it is time-consuming and expensive. The primary objective of this thesis was to explore the alternative `dry' method (which is both quicker and cheaper but which provides no refining of the parent clay) as a process, and to examine the nature of the organoclays produced, for the production of a wide range of commercially usable organophilic clays in a facile way. Natural Wyoming bentonite contains two quite different types of silicate surface (that of the clay mineral montmorillonite and that of a quartz impurity) that may interact with the cationic surfactant added in the `dry' process production of organoclays. However, it is oil shale, and not the quartz, that is chiefly responsible for the abrasive nature of the material, although air refinement in combination with the controlled milling of the bentonite as a pretreatment may offer a route to its removal. Ion exchange of Wyoming bentonite with a long chain quaternary ammonium salt using the `dry' process affords a partially exchanged, 69-78%, organoclay, with a monolayer formation of ammonium ions in the interlayer. Excess ion pairs are sorbed on the silicate surfaces of both the clay mineral and the quartz impurity phases. Such surface sorption is enhanced by the presence of very finely divided, super paramagnetic, Fe2O3 or Fe(O)(OH) contaminating the surfaces of the major mineral components. The sorbed material is labile to washing, and induces a measurable shielding of the 29Si nuclei in both clay and quartz phases in the MAS NMR experiment, due to an anisotropic magnetic susceptibility effect. XRD data for humidified samples reveal the interlamellar regions to be strongly hydrophobic, with the by-product sodium chloride being expelled to the external surfaces. Many organic cations will exchange onto a clay. The tetracationic cyclophane, and multipurpose receptor, cyclobis(paraquat-p-phenylene) undergoes ion exchange onto Wyoming bentonite to form a pillared clay with a very regular gallery height. The major plane of the cyclophane is normal to the silicate surfaces, thus allowing the cavity to remain available for complexation. A series of group VI substituted o-dimethoxybenzenes were introduced, and shown to participate in host/guest interactions with the cyclophane. Evidence is given which suggests that the binding of the host structure to a clay substrate offers advantages, not only of transportability and usability but of stability, to the charge-transfer complex which may prove useful in a variety of commercial applications.

This thesis concerns cell adhesion to polymer surfaces with an experimental emphasis on hydrogels. The thesis begins with a review of the literature and a synthesis of recent evidence to describe the process of cell adhesion in a given situation. The importance of understanding integrin-adhesion protein interactions and adhesion protein-surface interactions is emphasised. The experimental chapters describe three areas of investigation. Firstly, in vitro cell culture techniques are used to explore a variety of surfaces including polyethylene glycol methacrylate (PEGMA) substituted hydrogels, sequence distribution modified hydrogels and worn contact lenses. Cell adhesion to PEGMA substituted gels is found to decrease with increases in polyethylene oxide chain length and correlations are made between sequence distribution and adhesion. Worn contact lenses are investigated for their cell adhesion properties in the presence of antibodies to specific adhesion proteins, demonstrating the presence of vitronectin and fibronectin on the lenses. The second experimental chapter addresses divalent cation regulation of integrin mediated cell adhesion. Several cell types and various cations are used. Zinc, previously not regarded as an important cation in the process, is found to inhibit 3T3 cell adhesion to vitronectin that is promoted by other divalent cations. The final experimental chapter concerns cell adhesion and growth on macroporous hydrogels. A variety of freeze-thaw formed porous gels are investiated and found generally to promote cell growth rate.Interpenetrating networkbased gels (IPN) are made porous by elution of dextrin particles of varying size and loading density. These materials provide the basis for synthetic cartilage. Cartilage cells (chondrocytes) plated onto the surface of the porous IPN materials maintain a rounded shape and hence phenotypic function when a critical pore size and density is achieved. In this way, a prospective implant, made porous at the perpendicular edges contacting natural cartilage can be both mechanically stabilised and encourage the maintenance of normal matrix production at the tissue interface.