Low carbon bainitic steels microalloyed with Nb, Ti and V are widely used for the pipeline, construction and automobile industries because of their excellent combination of strength, toughness and weldability. Boron as another major alloying element has been also frequently used in this type of steels since the 1970s. The purpose of adding boron is to improve the hardenability of the steel by promoting bainite formation. / It has been realized that Boron can only be effective as a strengthening element when it is prevented from forming BN and/or Fe23(C, B) 6 precipitates. Therefore, Boron is always added together with other alloying elements which are stronger Nitride or Carbide formers, such as Ti and Nb. However, the formation of complex bainitic structures and the interaction with precipitates at industrial coiling temperature are not adequately understood. / In this study, the effect of boron on the microstructure and mechanical properties of a low carbon Nb-B steel was studied by a hot compression test (50% reduction at 850°C) followed by quenching samples into a salt bath. The microstructures of the tested samples were examined through optical microscopy and SEM; and the mechanical properties of these samples were investigated by micro-hardness and shear punch tests. / The results indicate that during thermo-mechanical controlled rolling (TCR), the final properties of the products not only depend on the applied deformation but also depend on the coiling temperature where phase transformation takes place. According to the investigation, two strengthening mechanisms are responsible for the strength of the steel at the coiling temperature: phase transformation and precipitation. Under optical microscopy, the microstructures of all specimens appear to be bainite in a temperature range from 350°C to 600°C without distinct differences. However, the SEM micrographs revealed that the microstructures at 550°C are very different from the microstructures transformed at the other holding temperatures. / Two strength peaks were observed at 350°C and 550°C in the temperature range studied. It is believed that the NbC precipitates are the main contributor to the peak strength observed at 550°C because the kinetics of NbC is quite rapid at this temperature. The strength peak at 350°C is mainly due to the harder bainitic phase, which formed at relatively lower temperature.

No description available.

The need to develop light-weight and high strength materials for car frames which improve fuel efficiency and provide increased passenger safety during dynamic events such as automobile crashes has been the focus of the steel and automobile industries for the past 30 years. In recent years, the development of high strength steels such as multi-phase TRIP (Transformation-Induced Plasticity)-aided steels have shown great promise due to their excellent combination of high strength and ductility. The savings in automobile weight is provided by the inherent strength of TRIP steels which allows for the use of thinner sections. The TRIP effect is characterized by the phenomenon known as strain-induced martensitic transformation (SIMT) which enhances the work hardenability of such steels as the austenite phase transforms to the much harder martensite phase during plastic straining. This results in a resistance to local necking which subsequently enhances the strength, ductility, and formability of such steels. However, various factors exist which affect the mechanical behaviour of TRIP steels. This study will aim, through the use of finite element models, to investigate the role and influence of each of these factors on the TRIP effect in type 304 austenitic and multi-phase TRIP steels. These factors include the rate at which the martensitic transformation proceeds, the state of stress to which the material is subjected to, the interaction between the surrounding matrix and embedded retained austenite islands in multi-phase TRIP steels, and the volume fraction and morphology of the retained austenite islands. Investigation of these factors will provide further insight on each of their contributions to the TRIP effect in order to exploit the potential benefits offered by these steels.

No description available.