Made available in DSpace on 2016-06-02T19:12:24Z (GMT). No. of bitstreams: 1 4609.pdf: 1709784 bytes, checksum: c55ba492a0a01e99f1d44d8d3578cfd4 (MD5) Previous issue date: 2012-08-07 / In this work is presented the characteristics of the steel C80U Modified, usually applied for bearing components produced through cold forming, as evaluated the influence of prior cold work on the microstructure after heat treatment by quenching and tempering. Starting from spheroidized carbides annealed structure, samples of strip steel were previously cold-rolled to different deformation degrees. The thickness reduction was based on the equivalent strain, calculated by numerical simulation in reference of a real cold formed part. These samples were quenched and tempered, and then the austenitic grain size for each different conditions of prior cold work was evaluated. By X-ray diffraction techniques the fractions of retained austenite for each degree of prior cold work were measured. Mechanical and metallurgical analysis were also carried out in rerolled strips as annealed in delivery condition, in order to characterize the fundamental properties related to drawing process. / Este trabalho tem como proposta apresentar as características do aço C80U Modificado, usualmente aplicado na confecção de componentes de rolamento através de conformação a frio pelo processo de estampagem, além de avaliar a influência da deformação preliminar a frio na microestrutura após tratamento térmico de têmpera e revenimento. Partindo da condição de microestrutura esferoidizada, amostras deste aço foram previamente laminadas a frio com diferentes graus de deformação, os quais foram determinados em uma simulação numérica da deformação real de uma peça estampada. Essas amostras foram submetidas a tratamento térmico de têmpera e revenimento, em seguida avaliado e comparado o tamanho de grão austenítico entre as diferentes condições de deformação preliminar a frio. Através da técnica de difração de raios-X foi também medida a quantidade de austenita residual para cada condição de amostras pré-deformadas. Foram também feitos ensaios mecânicos e análises metalúrgicas com tiras relaminadas no estado recozido, no que tangem às características fundamentais na condição de fornecimento para o processo de estampagem.

Devido a crescente necessidade de elevação dos níveis de conformação em peças estampadas em geral, existe uma demanda cada vez maior em ligas e processos diversificados que atendam as variadas exigências do setor de produtos estampados e posteriormente tratados termicamente para aumento de dureza. Desse modo desenvolveu-se a liga C80U modificada, que é uma variante da liga C80U especificada na norma DIN EN ISO 4957 porém com adição de Cromo, entretanto a liga C80U modificada ainda é pouco estudada e pouca informação técnica se tem a seu respeito. Com a finalidade de melhor conhecimento técnico dessa liga, foram conduzidos estudos de caracterização em amostras laminadas a quente e após processo de esferoidização posteriormente sendo revestidas com fosfato de zinco. Foram realizados estudos de composição química, microestrutura, textura cristalográfica, propriedades mecânicas e estrutura do fosfato, além de levantamento da curva CLC através do método Nakazima e evolução da rugosidade 2D e 3D em amostras com e sem revestimento de fosfato, antes e após conformação. Através dos resultados parciais encontrados, foi possível definir o lado da curva CLC relacionado ao estiramento da chapa bem como comparar o deslocamento e a força do punção no teste Nakazima conformando-se amostras esferoidizadas sem revestimento e com revestimento de fosfato. / Due to the increasing demand for enhanced formability levels of stamped parts in general, there is also an increasing demand for various alloys and processes that comply with the various requirements associated with stamped products that are subsequently heat treated to increase their hardness. Along this line, a modified C80U alloy has been developed, which is a variant of the alloy C80U specified in the standard DIN EN ISO 4957 but with the addition of Chrome. However, this alloy is still poorly studied and little technical information is available about it. In order to increase the knowledge of this alloy, characterization studies were conducted on hot rolled, after spheroidization and subsequently coated with zinc phosphate samples. The studies performed included chemical composition, microstructure, crystallografic texture, mechanical properties and analysis of the phosphate structure, as well as Nakazima tests in order to obtain the forming limit diagram (FLD) curve and the 2D and 3D roughness evolution of spheroidized samples coated and uncoated before and after the stamping process. Through the partial results obtained, it was possible to define the side of FLD curve related to stretching of the sheet as well as comparing the displacement and force of the punch on Nakazima test, stamping spheroidized samples both uncoated and coated with zinc phosphate.

Devido a crescente necessidade de elevação dos níveis de conformação em peças estampadas em geral, existe uma demanda cada vez maior em ligas e processos diversificados que atendam as variadas exigências do setor de produtos estampados e posteriormente tratados termicamente para aumento de dureza. Desse modo desenvolveu-se a liga C80U modificada, que é uma variante da liga C80U especificada na norma DIN EN ISO 4957 porém com adição de Cromo, entretanto a liga C80U modificada ainda é pouco estudada e pouca informação técnica se tem a seu respeito. Com a finalidade de melhor conhecimento técnico dessa liga, foram conduzidos estudos de caracterização em amostras laminadas a quente e após processo de esferoidização posteriormente sendo revestidas com fosfato de zinco. Foram realizados estudos de composição química, microestrutura, textura cristalográfica, propriedades mecânicas e estrutura do fosfato, além de levantamento da curva CLC através do método Nakazima e evolução da rugosidade 2D e 3D em amostras com e sem revestimento de fosfato, antes e após conformação. Através dos resultados parciais encontrados, foi possível definir o lado da curva CLC relacionado ao estiramento da chapa bem como comparar o deslocamento e a força do punção no teste Nakazima conformando-se amostras esferoidizadas sem revestimento e com revestimento de fosfato. / Due to the increasing demand for enhanced formability levels of stamped parts in general, there is also an increasing demand for various alloys and processes that comply with the various requirements associated with stamped products that are subsequently heat treated to increase their hardness. Along this line, a modified C80U alloy has been developed, which is a variant of the alloy C80U specified in the standard DIN EN ISO 4957 but with the addition of Chrome. However, this alloy is still poorly studied and little technical information is available about it. In order to increase the knowledge of this alloy, characterization studies were conducted on hot rolled, after spheroidization and subsequently coated with zinc phosphate samples. The studies performed included chemical composition, microstructure, crystallografic texture, mechanical properties and analysis of the phosphate structure, as well as Nakazima tests in order to obtain the forming limit diagram (FLD) curve and the 2D and 3D roughness evolution of spheroidized samples coated and uncoated before and after the stamping process. Through the partial results obtained, it was possible to define the side of FLD curve related to stretching of the sheet as well as comparing the displacement and force of the punch on Nakazima test, stamping spheroidized samples both uncoated and coated with zinc phosphate.