Made available in DSpace on 2015-05-08T14:59:47Z (GMT). No. of bitstreams: 1 arquivototal.pdf: 4591702 bytes, checksum: d3d1162ab21be50fefa84c84806ec86f (MD5) Previous issue date: 2012-11-12 / Coordenação de Aperfeiçoamento de Pessoal de Nível Superior / The fall of ceramic tile elements in facades is a problem that still persists in countries with more then two hundred years of experience. Although there are several parameters considered important in many standards, the effects of sun rays radiation on heat transfer and its combined effect with the color of the elements are not considered. As far as temperature is concerned, standards are mostly focused on stresses generated by thermal expansion. Although temperature affects cement hydration, which is the main material used to produce facade adhesives, studies on the effect of theses parameters on the pathologies associated with tile falls is very incipient. The aim of this work is to investigate the mechanical behavior of ceramic tile beams bonded with commercial Portland cement based adhesives and geopolymerics adhesives subjected to cyclic thermal variations, proposing new materials adhesives (sustanaible) and new propositions review. First, several field cases were studied in order to assess the main features of damaged facades. It has been observed that most bond problems occurred at the ceramic tile and the adhesive material interface. Also, facades with greater damage were oriented towards greater exposure of sun rays, which temperature gradient was as high as 55oC between day and night and also between color types. A laboratory systematic study was designed to simulate real thermal cicles as in structure conditions. Test parameters where temperature exposure, type adhesives and color ceramic tile. The cyclical temperature regime was produced in an irradiation chamber designed to reach 55ºC in a black globe for one, three and seven days. The adhesion was evaluated for mechanical pull tests (NBR 14084). The experimental results confirmed that failure happens at the ceramic-adhesive interface and, also, that temperature has a negative effect on the adhesive commercial Portland cement and positive for geopolymerics adhesives The greater the temperature, the lower the adhesion, especially when the adhesive thickness increases. The results help to supply both scientific bases to understand adhesive properties of tile facades. / O descolamento de placas de revestimento em edificações é um problema que ainda persiste em diversas construções modernas. Estes descolamentos acontecem principalmente em fachadas, onde a incidência de raios solares nas superfícies, aliada aos diferentes coeficientes de dilatação dos materiais constituintes dos seus revestimentos, contribuem para deformações diferenciais gerando tensões superiores aquelas dos mecanismos de adesão. Embora vários parâmetros estejam preconizados em diversas normas nacionais e internacionais, o efeito da temperatura, da cor das placas cerâmicas e o tipo de adesivo utilizado na aderência de placas em fachadas não têm sido considerados. Desta forma, as normas não contemplam a associação entre a difusão de calor gerada por irradiação solar e as diversas cores dos elementos de revestimento, que pode contribuir para a qualidade do revestimento de fachada. Este projeto objetiva-se a avaliar o comportamento mecânico de sistemas cerâmicos colados com adesivos comerciais à base de Cimento Portland e Geopoliméricos, propondo, assim, novos materiais adesivos (sustentáveis) e novas proposições de avaliação. Uma análise de edificações reais, na cidade de João Pessoa, indicou que os principais problemas de queda de material em fachadas ocorrem, predominantemente, na interface cerâmica-cola como também nas fachadas com maior incidência de radiação solar. Os sistemas estudados em laboratório foram projetados como uma tentativa de simular condições de utilização de peças em estruturas reais. Os principais parâmetros de ensaio foram: a temperatura, o tipo de adesivo e a cor do elemento cerâmico. A temperatura da câmara de irradiação foi calibrada de maneira que um globo negro atingisse temperatura de 55ºC e simulasse chuvas. A ciclagem térmica foi controlada por um termostato automático e ocorreu por um, três e sete dias. A aderência foi avaliada de acordo com ensaios mecânicos de arrancamento, segundo a NBR 14084. Os resultados experimentais confirmam que os descolamentos ocorrem, predominantemente, na interface cerâmica-cola e que o aumento da temperatura tem um efeito negativo para a argamassa colante e positivo para os adesivos geopoliméricos. Os resultados desta pesquisa contribuirão para fornecer subsídios teórico-práticos sobre a adesão de revestimento de fachadas, bem como para avaliação do potencial de utilização de adesivos geopoliméricos na colagem de revestimentos cerâmicos.

Made available in DSpace on 2014-12-17T14:58:06Z (GMT). No. of bitstreams: 1 RogerioCAP_DISSERT.pdf: 2453474 bytes, checksum: fb99d0d9567bd4529ff9de7138566071 (MD5) Previous issue date: 2010-12-17 / The sector of civil construction is strongly related to the red ceramic industry. This sector uses clay as raw material for manufacturing of various products such as ceramic plates. In this study, two types of clay called clay 1 and clay 2 were collected on deposit in Ielmo Marinho city (RN) and then characterized by thermogravimetric analysis (TG/DTG), differential thermal analysis (DTA), X-ray diffraction (XRD), X-ray fluorescence (XRF), rational analysis and particle size distribution and dilatometric analyses. Ceramic plates were manufactured by uniaxial pressing and by extrusion. The plates obtained by pressing were produced from the four formulations called 1, 2, 3 and 4, which presented, respectively, the following proportions by mass: 66.5% clay 1 and 33.5% clay 2, 50% clay 1 and 50% clay 2, 33.5% clay 1 and 66.5% clay 2, 25% clay 1 and 75% clay 2. After firing at 850, 950 and 1050 ?C with heating rate of 10 ?C/min and soaking time of 30 minutes, the following technological properties were determined: linear firing shrinkage, water absorption, apparent porosity, apparent specific mass and tensile strength (3 points). The formulation containing 25% clay 1 produced plates with most satisfactory results of water absorption and mechanical resistance, because of that it was chosen for manufacturing plates by extrusion. A single firing cycle was established for these plates, which took place as follow: heating rate of 2 ?C/min up to 600 ?C with soaking time of 60 minutes, followed by heating using the same rate up to 1050 ?C with soaking time of 30 minutes. After this cycle, the same technological properties investigated in the plates obtained by pressing were determined. The results indicate (according to NRB 13818/1997) that the plates obtained by pressing from the mixture containing 25 wt% clay 1, after firing at 1050 ?C, reach the specifications for semi-porous coating (BIIb). On the other hand, the plates obtained by extrusion were classified as semi-stoneware (group AIIa) / O setor de constru??o civil est? fortemente relacionado ? ind?stria de cer?mica. Esse setor utiliza a argila como mat?ria-prima para fabrica??o de diversos produtos como, por exemplo, placas cer?micas. Neste estudo, dois tipos de argila, que receberam a denomina??o de argila 1 e 2, foram coletados em jazida localizada no munic?pio de Ielmo Marinho (RN) e caracterizados por an?lise termogravim?trica (TG/DrTG), an?lise t?rmica diferencial (DTA), difratometria de raios X (DRX), fluoresc?ncia de raios X (FRX), an?lise racional e an?lises de distribui??o de tamanho de part?cula (DTP) e dilatom?trica (AD). Placas cer?micas foram fabricadas por prensagem uniaxial e extrus?o. As placas conformadas por prensagem foram produzidas a partir de quatro formula??es denominadas 1, 2, 3 e 4, as quais apresentavam, respectivamente, as seguintes propor??es em massa: 66,5 % de argila 1 e 33,5% de argila 2, 50% de argila 1 e 50% de argila 2, 33,5% de argila 1 e 66,5% de argila 2 e 25% de argila 1 e 75% de argila 2. Ap?s queima a 850, 950 e 1050 ?C, com taxa de aquecimento de 10 ?C/min e isoterma de 30 minutos, foram determinadas as seguintes propriedades tecnol?gicas: retra??o linear de queima, absor??o de ?gua, porosidade aparente, massa espec?fica aparente e tens?o de ruptura ? flex?o. A formula??o com 25% de argila 1 produziu placas com resultados mais satisfat?rios de absor??o de ?gua e resist?ncia mec?nica e desta forma foi a selecionada para conforma??o das placas por extrus?o. Um ?nico ciclo de queima foi estabelecido para essas placas, o qual ocorreu da seguinte forma: taxa de aquecimento de 2 ?C/min at? 600 ?C, com isoterma de 60 minutos, seguido de aquecimento a mesma taxa at? 1050 ?C, com isoterma de 30 minutos. Ap?s esse ciclo, foram determinadas as mesmas propriedades tecnol?gicas das placas conformadas por prensagem. Os resultados indicam, conforme a NBR 13818/1997, que as placas conformadas por prensagem a partir da formula??o contendo 25% em massa da argila 1, ap?s queima a 1050 ?C, atingem as especifica??es para revestimento semi-poroso (BIIb); e aquelas conformadas por extrus?o atendem ?s exig?ncias para serem classificadas como revestimento semi-gr?s (grupo AIIa)