Orientador : Fernando Mandarino / Banca: Welingtom Dinelli / Banca: Rosehelene Marotta Araújo / Abstract: The aim of this study was to evaluate "in vitro" the occurrence and width of fissures on cervical walls through electronic microscopy of scintiscan, and the marginal microleakage in class II restorations using composite resins Charisma and Solitaire (with direct and indirect techniques) and Artglass systems (using the indirect technique). Sixty human permanent molar teeth, without caries and recently avulsed, were used. Class II cavity preparations type slot were accomplished, on mesial aspects, which cervical wall was localized 1 mm before cement-enamel junction (in enamel); and on distal aspects, which cervical wall was located 1mm beyond cement-enamel junction (in cement). The adhesive system Solid bond was standardized and employed with three restorative materials. The teeth were separated in three groups, according the restoration technique and material applied, namely: group G1, restorations with Charisma resin (direct technique); group G2, restorations with Solitaire resin (direct technique); and group G3, restorations with Artglass resin (indirect technique). The obtained restorations were stored in physiological solution at 37o C for a week and subsequently submitted to polishing and thermocycled in water 200 times at 10oC l 2oC and 50oC l 2oC temperatures. The specimens were coated with Araldite and nail varnish, with 2 mm margin before the restoration limits. For the marginal microleakage analysis the teeth were immersed in Rodomin B 0,2% solution during 24 hours in kiln at 36o C temperature. After that, the teeth were sectioned and analyzed in a Zeiss stereoscope by three observer calibrated through scores ranging from zero to four. The results were submitted to Kruskal-Wallis and Mann-Whitney non-parametric statistical analysis and showed that no material or technique was capable to prevent the marginal...(Complete abstract, click electronic address below) / Resumo: O objetivo deste estudo foi avaliar in vitro a ocorrência e a largura de fenda na parede cervical através de microscopia eletrônica de varredura, e a microinfiltração marginal em restaurações de classe II com a utilização das resinas compostas Charisma e Solitaire (com a técnica restauradora direta) e o sistema Artglass (com o uso da técnica indireta). Foram utilizados 60 dentes molares permanentes de humanos hígidos e recentemente extraídos nos quais, foram realizados preparos cavitários classe II tipo slot nas faces mesiais cuja a parede cervical localizou-se 1 mm aquém da junção cemento/esmalte (em esmalte), e preparos nas faces distais com a parede cervical ultrapassando em 1mm a junção cemento/esmalte (em cemento). O sistema adesivo Solid bond (Hereaus KULZER) foi padronizado e utilizado com os três materiais restauradores. Os dentes foram divididos em três grupos variando-se Material e Técnica Restauradora, a saber: grupo G1, restaurações com a resina Charisma ;grupo G2, restaurações com a resina Solitaire; e o grupo G3, restaurações com a resina Artglass. As restaurações obtidas foram armazenadas em soro fisiológico por + 370C por 1 semana e posteriormente submetidas ao polimento e ciclagem térmica em água por 200 ciclos em temperaturas de 100 + 20C e 500 + 20C. Os espécimes foram cobertos com Araldite e esmalte de unhas, com margem de 2 mm aquém dos limites das restaurações. Para a análise da microinfiltração os dentes foram imersos em solução de Rodamina B à 0,2% durante 24 horas em estufa à 360C de temperatura. A seguir, os dentes seccionados e analisados em lupa estereoscópica Zeiss por três observadores calibrados através de escores de 0-4. Os resultados foram submetidos às análises não paramétricas de Kruskal-Wallis e Mann-Whitney e demonstraram que nenhum dos materiais e técnicas foram capazes...(Resumo completo, clicar acesso eletrônico abaixo) / Mestre