Orientador: Marcelo Ferraz Mesquita / Dissertação (mestrado) - Universidade Estadual de Campinas, Faculdade de Odontologia de Piracicaba / Made available in DSpace on 2018-08-05T02:22:15Z (GMT). No. of bitstreams: 1 Matta_RosaVirginiaLopesda_M.pdf: 978981 bytes, checksum: 0c2e4ad14c0328dbbe5c05f7cc1e24f4 (MD5) Previous issue date: 2005 / Resumo: O objetivo deste estudo foi avaliar o desempenho de um condicionador tecidual (Coe-Comfort), utilizando ou não selador de superfície, em relação às propriedades de deformação permanente e resistência à tração da união com a resina acrílica (QC-20). As amostras foram armazenadas em água destilada, numa estufa a 37±1oC. Para cada ensaio foram confeccionadas 60 amostras, separadas em 6 grupos de acordo com o tratamento e o período de armazenagem, a saber: Grupo 1- Coe-Comfort sem selador, 1 hora após armazenagem; Grupo 2- Coe-Comfort com selador, 1 hora após armazenagem; Grupo 3- Coe-Comfort sem selador, após 1 semana de armazenagem; Grupo 4- Coe-Comfort com selador, após 1 semana de armazenagem; Grupo 5- Coe-Comfort sem selador, após 2 semanas de armazenagem; Grupo 6- Coe-Comfort com selador, 2 semanas após a armazenagem. Para a confecção das amostras foram utilizadas matrizes metálicas incluídas em mufla, cujo molde impresso no silicone foi preenchido com resina acrílica e/ou condicionador tecidual. O ensaio de deformação permanente foi realizado em aparelho mecânico descrito na especificação ?18 da ADA, e o ensaio de resistência à tração, na Máquina de Ensaios Universal EMIC-DL500MF (5mm/minuto). Os dados obtidos foram submetidos à análise de variância e indicado o teste não paramétrico de Mann-Whitney, em nível de 5% de probabilidade. Para deformação permanente, foram observadas diferenças estatisticamente significantes somente após 1 semana de armazenagem, com valores mais elevados para o grupo tratado com selante de superfície. Para a resistência à tração da união, em relação ao tempo de armazenagem e ao material selador de superfície, pode-se observar que o selamento foi benéfico somente na primeira hora e na primeira semana de armazenagem. Quanto ao tipo de ruptura, após 1 hora de armazenagem, observou-se presença de ruptura do tipo adesiva em 100% das amostras, após 1 semana foi predominantemente coesiva e após 2 semanas foi coesiva em 100% das amostras. Com base nos resultados obtidos, concluímos que existiram diferenças estatisticamente significativas após uma semana de armazenagem, com valores mais elevados no grupo tratado com selante de superfície. No ensaio de resistência à tração pode-se concluir que o selamento foi benéfico ao condicionador tecidual na primeira hora e na primeira semana / Abstract: The purpose of this study was to evaluate the performance of the tissue conditioner (Coe-Comfort), with or without sealer (treatment surface), in relation to permanent deformation and tensile bond strength between resin acrylic (QC-20) and tissue conditioner. In each study there were sixty samples divided in six groups(G), according to the surface treatment and storage time in water, which were the following: G 1- Coe-Comfort without sealer, after 1 hour of stored; G 2 - Coe-Comfort with sealer, after 1 hour of stored; G 3 - Coe-Comfort without sealer, after 1week of stored; G 4 - Coe-Comfort with sealer, after 1 week of stored; G 5 - Coe- Comfort without sealer, after 2 weeks of stored; G 6 - Coe- Comfort with sealer, after 2 weeks of stored. To make the samples metallic matrixes were used invested in flasks, and models were impressed in silicone filled up with acrylic resin and/or tissue conditioner. The samples were stored in water at 37±1ºC for a determined period. The permanent deformation test was done in mechanic machine described in the ? 18 A.D.A¿s specification and the tensile bond strength test was done in a universal testing machine EMIC- DL 500 MF (5 mm/mim). The obtained data was analyzed by Mann-Whitney test at 5% of probability. To permanent deformation significant statistical differences were observed only 1 week after storage, with higher values in the group with treatment surface. To the bond strength to the traction, concerning to the time of storage samples and to the surface treatment, the sealer effect was beneficial at the conditioner only at the first hour and first week. According to the kind of failure, after 1 hour of storage, 100% of samples presented adhesive failures, after 1 week 90% of cohesive and 100% of cohesive failures after 2 weeks. We concluded that the sealer effect after 1 week of storage didn¿t have beneficial influence on permanent deformation of the tissue conditioner. To the tensile bond strength sealer effect was beneficial only in the first and second time of storage / Mestrado / Protese Dental / Mestre em Clínica Odontológica

Orientador: Celia Marisa Rizzatti Barbosa / Tese (doutorado) - Universidade Estadual de Campinas, Faculdade de Odontologia de Piracicaba / Made available in DSpace on 2018-08-06T09:27:11Z (GMT). No. of bitstreams: 1 Silva-Concilio_LaisRegianeda_D.pdf: 1615286 bytes, checksum: 5b5a37d894f9d8d033b5fba17bb3f697 (MD5) Previous issue date: 2006 / Resumo: O objetivo deste estudo foi avaliar a influência da técnica de processamento laboratorial na área de contato em máxima intercuspidação e dimensão vertical de oclusão em pares de próteses totais analisadas antes e após processamento laboratorial. Para isto foram confeccionadas 40 pares de próteses, separadas aleatoriamente em 4 grupos de acordo com o método de polimerização e tipo de mufla: GI ¿ polimerizadas em água 73oC / 9 horas em muflas monomaxilares; GII ¿ polimerizadas por energia de microondas 20 min. a 20% de potência e 5 minutos a 60% de potência em muflas monomaxilares; GIII ¿ polimerizadas em água 73oC / 9 horas em muflas bimaxilares; GIV ¿ polimerizadas por energia de microondas 20 min. a 20% de potência e 5 minutos a 60% de potência em muflas bimaxilares. Foi realizada a mensuração da DVO e da Superfície de Contato antes e após o processamento laboratorial. Para a mensuração da DVO foi utilizada uma base plana e rígida na qual encaixava-se o paquímetro digital e o articulador. Foram realizadas 3 mensurações em cada fase e calculadas as médias. Para a avaliação das superfícies de contato foi utilizado o software Qwin 550 (Leica®), que foram mensuradas 3 vezes em cada amostra nos períodos pré e pós processamento, e calculadas as respectivas médias. Os dados obtidos foram submetidos à Análise de Variância e teste de Tukey em nível de 5% de significância. Os resultados demonstraram que todos os grupos apresentaram uma variação percentual positiva para a DVO: GI= 1,92%; GII= 2,92; GIII= 2,27% e GIV= 2,72%, sendo que GI e GII apresentaram diferença estatística entre si (p= 0,083). Os dados da superficie de contato demonstraram que não houve diferença estatística entre os grupos tanto nos modelos superiores como nos inferiores. Com exceção do grupo GII nos modelos superiores, todos os grupos apresentaram diminuição da superfície de contato. Pode-se concluir que: 1) a DVO foi alterada em todos os grupos estudados independentemente do método de polimerização; 2) o grupo GII apresentou menor variação percentual da DVO; 3) o grupo GI apresentou maior variação percentual da DVO; 4) não houve diferença entre os grupos quanto a análise da Superfície de Contato Oclusal / Abstract: The purpose of this study was to evaluate different flasking technics using monomaxillary and bimaxillary flasks by microwave irradiation and water bath, in the occlusal vertical dimension and the area of the occlusive contact, before and after the curing. Forty pairs of complete dentures were distributed into four groups of ten pair each, according to the treatments: GI ¿ cured by water bath 73oC/9h and monomaxillary flasks; GII ¿ cured by microwave irradiation 20 minutes at 20% power and 5 minutes at 60% power and monomaxillary flasks; GIII ¿ cured by water bath 73oC/9h and bimaxillary flasks; GIV¿ cured by microwave irradiation 20 minutes at 20% power and 5 minutes at 60% power and bimaxillary flasks. For the measurement of the occlusal vertical dimension was used the table that the articulator and the digital caliper was positioned correctly, three vertical measurements were made before and after the curing. The area of occlusive contact was measure using the software Qwin 550 (Leica®), each pair of denture was measure three times before and after the curing. Datas were submitted to variance analysis and Tukey¿s test at 5% significance level. These demonstrated that all groups showed positive percent variation for the occlusal vertical dimension: GI= 1.92%; GII= 2.92; GIII= 2.27% e GIV= 2.72%, there were significant statistical differences between GI and GII (p=0.083). There weren¿t statistical differences in the datas of the area of the occlusive contact, in the upper and lower models. Except GII, in the upper models, every groups showed reduction in the area of the occlusive contact. It is concluded that: 1) the occlusal vertical dimension changed in all groups independently of curing method; 2) the group GII showed the lowest percent variation of the occlusal vertical dimension; 3) the group GI showed the highest percent variation of the occlusal vertical dimension; 4) there weren¿t statistical differences between the groups in the area of the occlusive contact; 5) all the groups, except GII, showed decreasing of the area of the occlusive contact after laboratorial processing / Doutorado / Protese Dental / Doutor em Clínica Odontológica

Orientador: Simonides Consani / Tese (doutorado) - Universidade Estadual de Campinas, Faculdade de Odontologia de Piracicaba / Made available in DSpace on 2018-08-04T11:55:19Z (GMT). No. of bitstreams: 1 Monteiro_WildesdaCosta_D.pdf: 6985087 bytes, checksum: dab5ef3ae95601eac48a0d542f0cf87f (MD5) Previous issue date: 2005 / Resumo: O objetivo deste estudo foi analisar por meio de medições tridimensionais, as alterações dimensionais que ocorrem nos modelos de gesso utilizados na confecção de prótese total, em função de diferentes materiais para moldagem: silicone, alginato e godiva equalizada com alginato. Foram confeccionados 45 modelos de gesso tipo IV, (n=15) construídos a partir de moldes obtidos de um modelo padrão metálico de alumínio, onde foram colocados 7 parafusos com 3,5 mm de diâmetro, para estabelecer pontos referenciais das distâncias a serem mensuradas. Esses pontos referenciais permitiram criar segmentos para o cálculo do volume e da área gerados nas figuras representativas dos modelos de gesso, permitindo avaliar a estabilidade dimensional dos modelos em gesso por meio de medições tridimensionais. No CETEF os modelos de gesso foram submetidos às medições tridimensionais no aparelho Mitutoyo, modelo BLN 710, equipado com cabeça de medição Renishaw PH9 e apalpador TP200 com esfera de 1mm de diâmetro, para as seguintes etapas: 1- transferência das coordenadas tridimensionais para o programa Mechanical Desktop; realização dos desenhos bidimensionais; medição dos seguimentos que compõem cada figura desenhada de cada desenho; realização dos desenhos tridimensionais; cálculo do volume e da área projetada utilizando a malha de elementos finitos e confecção de uma planilha de cálculo para cada material de moldagem; tratamento estatístico dos dados e determinação matemática das variações e das coordenadas x, y e z dos comprimentos de cada um dos segmentos, dos perímetros e das áreas de cada figura dos quarenta e cinco modelos. 2- lançamento dos dados nas planilhas de cálculo; tratamento estatístico dos dados e determinação matemática das variações e das coordenadas x, y e z dos comprimentos de cada um dos segmentos, dos perímetros e das áreas de cada figura. 3- apresentação tridimensional das variações dimensionais encontradas nos modelos; transferência das variações das coordenadas do grupo de modelos de cada material, em relação ao modelo padrão, para o software de desenho 3D ¿ Mechanical Desktop; geração das figuras para visualização das variações e elaboração de relatório técnico. Os resultados foram submetidos à média matemática simples da dispersão ou variação dos dados, que é o grau no qual os dados numéricos da amostra tendem a dispersar-se em torno de um valor médio. Foi utilizado neste trabalho o cálculo do desvio padrão simples. Os moldes feitos com silicone por adição produziram modelos com menor variação dimensional (capacidade de repetitibilidade) quando comparados aos modelos obtidos com moldes de alginato e godiva equalizada com alginato. O alginato produziu modelos com grande fidelidade de cópias em função da matriz metálica / Abstract: The purpose of this study was to analyze, through three-dimensional measurements, the dimensional changes in casts of stone used to make complete dentures, in function of different materials for impression: addition reaction silicone, alginate and impression compound reline with alginate. The casts of stone type IV were made from molds obtained from a metallic standard die of aluminum. In this metallic die were put seven screws with 3,5mm diameter, to establish referential points of the measured distances. The referential points allowed creating segments for the calculation of the area and volume in the representative drawings generated for the stone casts. The procedure allows evaluating the dimensional stability through three-dimensional measurements. In CETEF the stone die were measured with three-dimensional equipment Mitutoyo, model BLN 710, equipped with measurement head Renishaw PH9 and feeler TP200 with sphere of 1mm of diameter, for the stages: 1- Transfer of the three-dimensional coordinates for the program Mechanical Desktop; generation of the two-dimensional drawings; measurement of the segments that compose each drawing; generation of the three-dimensional drawings; projected area determination and volume calculation using the finite elements net; making of a calculation spread sheet for each impression material; statistical treatment of the data and mathematical determination of the variations in the x, y and z coordinates in the lengths of each segments, in the perimeters and in the areas of each drawing of the forty five casts. 2 - Insertion of the data in the calculation spread sheets; statistical treatment of the data and mathematical determination of the variations and in the x, y and z coordinates in the lengths of each one of the segments, in the perimeters and of the areas of each drawing. 3 - Three-dimensional presentation of the dimensional variations found in the models; transfer of the variations of the coordinates of the group of models of each material, for the software of 3D drawing ¿ Mechanical Desktop; generation of the drawings for visualization of the variations and elaboration of technical report. The results were submitted to the simple mathematics medium of the dispersion or variation of the data, that it is the degree, in which the numeric data of the sample tend to disperse around a medium value. It was used in this work the calculation of the simple standard deviation. The molds made with addition reaction silicone produced casts with smaller dimensional variation, when compared to the casts obtained with alginate or impression compound reline with alginate. The silicone presented larger capacity to repeat generated copies of the molds, from the standard die. The cast made with addition reaction silicone presented small variation among themselves when compared to the standard metallic die / Doutorado / Protese Dental / Doutor em Clínica Odontológica