Development of Corrosion Protective Coating Systems for AZ31B Magnesium AlloyEzhiselvi, V January 2016 (has links) (PDF)
Magnesium and its alloys are extensively used for various industries such as aerospace, automobile and electronics due to their excellent properties such as low density, high strength and stiffness and electromagnetic shielding. However, the wide spread applications of these alloys are limited due to the undesirable properties such as poor corrosion, wear and creep resistance and high chemical reactivity. These alloys are highly susceptible to galvanic corrosion in sea water environment due to their high negative potential (-2.37 V vs SHE). The effective way of preventing corrosion is through the formation of a protective coating, which acts as a barrier between the corrosive medium and the substrate. Many surface modification methods such as electro/ electroless plating, conversion coating, physical and chemical vapour depositions, thermal spray coating etc., are available currently to improve the corrosion resistance of Mg alloys. Of these methods, the electroless nickel plating has gained considerable importance because of its excellent properties such as high hardness, good wear and corrosion resistance. The properties of binary electroless nickel coating have been further improved by the addition of a third element such as cobalt, tungsten, tin and copper etc. It has been reported that the addition of tungsten as the third element in the Ni-P improves the properties such as hardness, wear and corrosion resistance, thermal stability and electrical resistance.
Magnesium alloys are categorized as a “difficult to plate metal”, because of their high reactivity in the aqueous solution. They react vigorously with atmospheric oxygen and water, resulting in the formation of the porous oxide/ hydroxide film which does not provide any protection in the corrosive environment. Further, the presence of this oxide film prevents the formation of a good adhesive bond between the coating and the
substrate. The surface treatment process for removal of the oxide layer is very much essential before plating the Mg alloy. Currently two processes such as zinc immersion and direct electroless nickel plating are adopted to plate Mg alloys. Etching in a solution of chromate and nitric acid followed by immersion in HF solution to form a conversion film is necessary for direct electroless nickel (EN) plating of Mg alloy.
However, strict environmental regulations restrict their usage because of hazardous nature. Expensive palladous activation treatment is a well-known process as a replacement for chromate-HF pretreatments for Mg alloys. It has been reported that EN plating has been carried out over Mg alloys by using conversion coating followed by HF treatment. Formation of an intermediate oxide layer by electrolytic methods is also one of the ways these toxic pretreatments can be avoided. Microarc oxidation (MAO) is an environment friendly surface treatment technique which provides high hardness, better corrosion and wear resistance properties for the Mg alloys. EN coating has been prepared on MAO layer for improving the corrosion resistance. These MAO/EN composite coatings have been prepared using chromic acid and HF pretreatment process. As the replacement for the chromate-HF pretreatment, SnCl2 and PdCl2 sensitization and activation procedures respectively were adopted over MAO layer for the deposition of Ni-P coating. From the above reported literature, it can be inferred that for the activation of inert MAO layer to deposit electroless nickel coating, the hazardous chromate/HF and highly expensive PdCl2 activation processes were followed. Therefore, there is a need for identifying an alternative simple and cost effective pretreatment process for the deposition of electroless nickel. It is well known that borohydride is a strong reducing agent that has been used for the deposition of Ni-B coatings.
In the present study, an attempt has been made to utilize borohydride in the pretreatment process for the reduction of Ni2+ ions over the MAO interlayer, which provides the nucleation sites for the deposition of Ni-P coating.
Ni-P and Ni-P/Ni-W-P duplex coatings were deposited from stabilizer free carbonate bath on AZ31B Mg alloy to improve the corrosion resistance of the base substrate. The conventional chromate and HF pretreatment processes were followed for the deposition of electroless nickel coating. In order to improve the corrosion resistance of the duplex coating, post treatments such as heat treatment (4 h at 150°C) and chromate passivation were adopted. EDX analysis of AZ31B Mg alloy showed the presence of 2.8 wt.% of Al and 1.2 wt. % Zn with the balance of Mg for AZ31B Mg alloy. After the chromic acid and HF treatment, the magnesium content was reduced from 90.0 wt % to 54.9 wt%, which could be due to the incorporation of chromium on the surface layer. The surface showed about 17.8 wt. % of F. The alloy exhibited the roughness of about 0.29± 0.01µm after mechanical polishing. The roughness value was significantly changed after the chromic acid treatment processes. The maximum roughness of about 1.28±0.06 µm was obtained after the HF activation. XPS analysis confirmed the existence of chromium in +3 oxidation state after the chromic acid treatment. The Ni-P coating thickness of about 25 microns was obtained in 1 h and 15 min. In the case of duplex coatings, Ni-P plating was done for 45 min. to obtain approx. 17 microns thickness and Ni-W-P plating was done for 1.15 h to obtain a thickness of approx. 10 microns, resulting in a total thickness of 25 ± 5 microns. Ni–P coating exhibited nodular morphology with porosity. The size of these cluster nodules were of about 10 µm in diameter. On the other hand, the duplex coating exhibited a less nodular, dense and smooth appearance. From the compositional analysis it was found that Ni–P coating contained about 6 wt. % P. In the case of duplex coating, the P content was reduced to 3 wt % due to the incorporation of about 2 wt% of tungsten. In corrosion studies, the potentiodynamic polarization data obtained for bare Ni-P coating in 0.15 M NaCl solution exhibited a higher current of about 218 μA/cm2 as compared to the substrate due to the porosity of the coating. However, the Ni-P/Ni-W-P duplex showed 55 times improvement in corrosion resistance, vis-a-vis Ni-P due to the dense nature of the coating. The corrosion resistance of the coatings increased in the following order: Ni-P < bare alloy < duplex < duplex-passivated < duplex-heat treated passivated. In EIS study, the Nyquist plot obtained for the bare substrate and Ni–P coating showed the presence of inductance behavior at the lower frequency region due to the adsorption of electroactive species over the substrate through the porous oxide layer. However, the passivated and duplex passivated coatings exhibited only capacitive behavior due to their compact nature. From the above, it can be concluded that, direct deposition of Ni-P coating over the chosen Mg alloy using chromic acid and HF pretreatment process resulted in porous morphology, which affected the corrosion resistance of the coating.
As an alternative strategy, the microarc oxidation conversion coating was developed on Mg alloy and characterized. The MAO coating was developed using silicate electrolyte at three different current densities (0.026, 0.046 and 0.067 A/cm2) for about 15 min. With respect to the MAO coating, an increase in the current density increased the pore diameter and decreased the pore density. The surface of the coating became coarser and rough. The cross-sectional morphology of the coating showed two district layers namely the dense and thin inner layer and a porous thick outer layer. The thickness of the coating increased with increase in current density. MAO coating prepared at an intermediate current density of 0.046 A/cm2 exhibited a higher thickness of about 12 µm and a further increase in current density showed a decrease in thickness, due to the greater rate of dissolution of Mg, relative to the rate of deposition. The surface roughness of the MAO coatings also increased with increase in current density. The Ra value increased from 1.39±0.06 to 3.52±0.17 µm with increase in current density. XRD peaks obtained for the Mg substrates corresponded predominately to magnesium. However, the coated specimens showed the presence of peaks corresponding to Mg2SiO4 along with Mg and MgO. The corrosion measurements for the bare substrate and MAO coatings were carried out in 3.5% NaCl medium (0.6 M). Based on potentiodynamic polarization studies, the MAO coating prepared at 0.046 A/cm2 exhibited a lower corrosion current density with a higher Rp value, which was about five orders of magnitude higher than the bare substrate, due to the dense nature of the coating. In EIS study, MAO coatings were fitted with the two time constants equivalent circuit containing outer porous layer and inner barrier layer. The barrier layer resistance values were higher than that of porous layer resistance, which indicated that the resistance offered by barrier layer was higher than the porous layer. The total resistance value obtained for the coating prepared at 0.046 A/cm2 were higher compared to the other coatings, which attested to its better corrosion resistance. The electrochemical noise measurement was carried out for longer immersion durations upto 336 h in 3.5% NaCl solution. The noise resistance value obtained for the base Mg alloy was about 100 Ω at 1h immersion, whereas for the MAO coating prepared at 0.04 A/cm2 a maximum value of about 34.8 MΩ was achieved and it was retained even after 96 h of immersion. Mott–Schottky analysis showed that the oxide layer on magnesium substrate acted as a n-type semiconductor, whereas the MAO coatings exhibited p-type semiconductor behavior. The MAO coating obtained at an intermediate current density showed a higher acceptor density and the flat band potential, which resulted in the better performance of the coating in corrosive environment.
In another set of investigations, the Ni-P and Ni-P/Ni-W-P coatings were deposited on AZ31B Mg alloy with MAO coating as an interlayer. The MAO layer was activated by a
simple borohydride pretreatment process. During the pretreatment process, the MAO coating was subjected to mild alkali treatment, immersion in the Ni-P plating solution and finally immersion in borohydride solution. During each pretreatment step, the sample was characterized for their surface morphology and composition. The surface morphology showed the distribution of spherical particles over the surface of MAO coating after immersion in the Ni-P plating solution. EDX analysis showed the presence of 2.4 wt. % of Ni, which confirmed that Ni ions were adsorbed over the surface of the MAO coating during the pretreatment process. XPS analysis carried out after immersion in the Ni-P plating solution indicated that Ni existed in +2 oxidation state. The surface became smooth and uniform with flake- like morphology after the borohydride treatment, which indicated that the surface was etched by the borohydride solution. EDX analysis showed the presence of 1.8 wt.% of Ni after borohydride reduction. XPS analysis confirmed the reduction of nickel to the zero oxidation state. Additionally, MAO/Ni-P and MAO/Ni-P/Ni-W-P duplex coatings were developed on MAO coating after a simple borohydride pretreatment. Ni-P and duplex coatings showed uniform and dense nodular morphology without any defects, which clearly indicated that the borohydride treatment provided a uniform and homogeneous active surface for the deposition of electroless nickel based coatings. Borohydride pretreatment process resulted in excellent bonding between MAO/Ni-P layers in the cross section. Based on potentiodynamic polarization studies, the corrosion current values obtained for MAO/ Ni-P and MAO/Ni-P/Ni-W-P duplex coatings were about 1.44 and 1.42 µA/cm2, respectively. The coating showed about 97 times improvement in corrosion resistance compared to the bare substrate, attesting to the dense nature of the coating. In EIS study, the single time constant equivalent circuit was used for fitting the spectra, which pertained to the coating /electrolyte interface. The single time constant could be attributed to the pore-free dense, uniform coatings developed over the MAO interlayer. For the MAO/Ni-P and MAO/Ni-P-Ni-W-P duplex coatings, the charge transfer resistance of about 15 and 11 kΩcm2 were obtained for duplex and Ni-P coatings, which reinforce the better corrosion protective ability of the coating.
The above investigation confirms that MAO coatings have good corrosion resistance in the aggressive chloride medium. Consequently, they can serve as an ideal interlayer for the deposition of the electroless nickel coating. Even if the electroless nickel coating is found to fail in harsh environments, the MAO interlayer can protect the base substrate due to its higher corrosion resistance. It is also noteworthy that the borohydride treatment provides better adhesion between the MAO/Ni-P interlayer.
|
12 |
Dépôt en couches minces de nickel chimique multifonctionnel / Thin Deposit of Multifunctional Electroless NickelForestier, Igor 18 May 2018 (has links)
Les pompes sèches primaires dédiées aux procédés de fabrication en microélectronique sont soumises à des environnements très corrosifs de plus en plus oxydants et halogénés (Cl2, F2 et O2). Or pour des raisons mécaniques et économiques, les parties fonctionnelles des pompes sont usinées dans la fonte à graphite sphéroïdale EN-GJS-500-7. La fonte est alors protégée par un dépôt de nickel-phosphore (NiP) chimique. Cette thèse, reprend des études classiques sur la cinétique et le mécanisme de nickelage d'une part, et sur l'optimisation des propriétés mécaniques et la résistance à la corrosion des couches de NiP d'autre part. Cependant, le caractère innovant de ce travail repose sur la réalisation de couches NiP sur un substrat en fonte à graphite sphéroïdale.L'étude de la cinétique de nickelage et la caractérisation morphologique des revêtements en fonction du temps de dépôt a montré l'influence de la nature chimique du substrat. Les sphères de graphite affleurantes à la surface du substrat n'étant pas catalyseur du nickel chimique, provoque des défauts dans le revêtement, dommageables pour la conformité du dépôt. Il a été montré qu'une polarisation cathodique de la surface du substrat pouvait, dans les premiers instants du dépôt, amorcer le nickelage à l'aplomb des sphères de graphite.Une relation entre la microstructure des dépôts en fonction des traitements thermiques subis et des propriétés mécaniques des couches de NiP a été mise une évidence. Les dépôts NiP amorphes présentent une faible dureté et un comportement ductile tandis que les dépôts cristallisés possèdent une dureté élevée et un comportement fragile. Ces dépôts ont une bonne tenue à la corrosion en milieux halogéné lorsqu'ils sont intacts. Actuellement, au niveau industriel, les dépôts les plus fragiles sont choisis, bien qu'ils présentent une résistance à la corrosion plus faible : en effet, la durée de vie des pompes est alors supérieure car les effets de grippage sont atténués.Mots-clés : nickel chimique, résistance à la corrosion, fonte à graphite sphéroïdale, caractérisation physico-chimique, couches minces, durabilité mécanique / Primary dry pumps dedicated to manufacturing processes in microelectronics are subjected to highly corrosive environments that are increasingly oxidizing and halogenous (Cl2, F2 and O2). However, for mechanical and economic reasons, the functional parts of the pumps are machined in EN-GJS-500-7 spheroidal graphite cast iron. The cast iron is consequently protected by a nickel-phosphorus chemical deposit. This thesis is based on classical studies on the kinetics and the nickel-plating mechanism on the one hand, and on the optimization of the mechanical properties and corrosion resistance of the NiP layers on the other hand. The innovative nature of this work is based on the production of NiP layers on a spheroidal graphite cast iron substrate.The study of the kinetics of nickel-plating as well as the morphological characterization of coatings as a function of the deposit time showed the influence of the chemical nature of the substrate. The flush graphite spheres on the surface of the substrate being not a catalyst for the chemical nickel, they can cause defects in the coating and a loss of compliance. It has been shown that a cathodic polarization of the surface of the substrate, in the first moments of the deposit, could initiate the nickel-plating right on the graphite spheres.A relationship exists between the microstructure of the deposits as a function of the thermal treatments undergone and the mechanical properties of the NiP layers. The amorphous NiP deposits have a low hardness and a ductile behavior while crystallized deposits have a high hardness and a brittle behavior. These deposits have a good resistance to corrosion in halogenated environments when they are intact. Actually, at the industrial level, the most brittle deposits are chosen, although they have a lower corrosion résistance: indeed, the service life of the pumps is higher because the seizing effect are minimized.Keywords: electroless nickel, resistance to corrosion, spheroidal graphite cast iron, physicochemical characterization, thin layers, mechanical durability
|
13 |
Modifikace povrchu pokročilých hořčíkových slitin povlaky na bázi Ni-P / Advanced Magnesium Alloys Surface Modification by Ni-P Based CoatingsKosár, Petr January 2017 (has links)
The dissertation thesis deals with the modification of the surface of advanced magnesium alloys with Ni-P based coatings. At the beginning of the theoretical part, the structures of the used magnesium alloys and the influence of individual alloying elements on their properties are characterized. In the following part of the thesis the current knowledge in the field of electroless deposition on metal substrates is summarized. The theoretical part of the thesis is closed with contemporary research study in the field of clarification and determination of possible mechanism of electroless deposition. For the subsequent investigation of the mechanism of electroless deposition on magnesium alloys, it was necessary to characterize the microstructure and composition of individual magnesium alloys in the first phase of the experimental part. The exact composition of elements was determined using glow discharge optical emission spectroscopy and scanning electron microscopy with EDS was used for composition of phases of magnesium alloys. Using scanning electron microscopy and detailed elemental analysis of the coated magnesium substrate, it was found that for optimal Ni-P coating deposition on magnesium alloys, acid pickling prior coating is required in a mixture of acetic acid and sodium nitrate. Using the XPS method, it was found that the phosphorus atom in the sodium dihydride-diphosphate reducing agent has a + V charge. 4 At the end of the experimental part scanning electron microscopy and detailed elemental analyses were used for monitoring of the Ni-P particles nucleation and growth in the first 120 seconds of the coating process.
|