O objetivo deste estudo foi avaliar os efeitos dos lasers de Nd:YAG, CO2 e Er,Cr:YSGG no tratamento de superfície da cerâmica Y-TZP antes e depois da sinterização final, por meio de Microscopia Eletrônica de Varredura (MEV), mensuração da rugosidade de superfície (Ra) e teste de resistência adesiva por microcisalhamento (RAD). Para tanto, barras de Y-TZP foram confeccionadas e distribuídas entre as 3 fases do experimento, sendo as duas primeiras fases seletivas para a identificação dos parâmetros lasers a serem utilizados na fase 3 de análise da RAD. Na fase 1 MEV - foram testados parâmetros que variavam entre 50 e 100 mJ para o laser de Nd:YAG, 2 a 4W para o laser de CO2 e 1 a 3,5W para o laser de Er,Cr:YSGG, testados antes ou após a sinterização da Y-TZP. Observou-se que a maioria dos tratamentos foram capazes de promover alterações na cerâmica com diferentes intensidades dependendo do parâmetro utilizado. Para a fase 2 Ra foram selecionados apenas os tratamentos com os lasers de Nd:YAG e Er,Cr:YSGG aplicados antes da sinterização da cerâmica, sendo que cada laser foi avaliado individualmente e comparados ao tratamento de superfície com o sistema Rocatec. Os tratamentos com os maiores valores de Ra foram: para o laser de Nd:YAG - 1,6W-20Hz (11.623±3,419) e para o laser de Er,Cr:YSGG - 3W (6,051±1,991). O sistema Rocatec apresentou os menores valores de rugosidade (1,297±0,026). Para a fase 3 do estudo RAD foram selecionados os parâmetros que apresentaram os maiores valores de Ra para cada laser, além do parâmetro com características favoráveis à adesão observado na fase 1 MEV. Sendo assim, o teste de microcisalhamento foi realizado entre a cerâmica Y-TZP tratada com os lasers antes da sinterização final, nos parâmetros de 1,6W e 1,2W para o laser de Nd:YAG e 3W para o laser de Er,Cr:YSGG; e com o sistema Rocatec, utilizando-se dois cimentos resinosos de dupla ativação (Panavia e RelyX U100). A análise estatística ANOVA Split-Plot dos dados de RAD obtidos revelou que não houve diferença estatística entre os cimentos estudados. Porém, no fator tratamentos de superfície observou-se que os maiores valores de RAD foram obtidos para o sistema Rocatec (20,92±3,4MPa). Os dois parâmetros utilizados para o laser de Nd:YAG foram semelhantes entre si com valores de RAD intermediários (1,2W=9,79±4 MPa e 1,6W=11,35±3,64 MPa) e o tratamento com o laser de Er,Cr:YSGG apresentou os menores valores de RAD (1,43±1,21MPa). Pôde-se concluir que os tratamentos de superfície com todos os lasers testados nos parâmetros de irradiação após a sinterização, provocaram danos à cerâmica Y-TZP. Os tratamentos com os lasers de Nd:YAG e Er,Cr:YSGG antes da sinterização, apesar de apresentarem características micromorfológicas sugestivas de aumento da área de superfície, não foram suficientes para aumentar a resistência adesiva entre a Y-TZP e os cimentos resinosos testados. / The aim of this study was to evaluate the effects of Nd:YAG, CO2 and Er,Cr:YSGG lasers on the surface treatment of Y-TZP ceramic before and after the final sintering by means of Scanning Electron Microscope (SEM), surface roughness measurement (Ra) and microshear bond strength adhesive resistance test (RAD). In order to do so, Y-TZP bars were produced and distributed among the three experimental phases, being the two first ones selective in what regards identifying parameters for the lasers used in phase 3 of the RAD analysis. In phase 1 SEM parameters varying from 50 to 100 mJ were tested for the Nd:YAG laser, from 2 to 4W for the CO2 laser and from 1 to 3,5W for the Er,Cr:YSGG laser, either before or after the Y-TZP sintering. It was observed that most treatments were able to promote changes in the ceramic with varied intensity according to the parameter used. In phase 2 Ra only treatments with Nd:YAG and Er,Cr:YSGG lasers applied before ceramic sintering were selected, and each laser was individually evaluated and compared to the surface treatment with Rocatec system. The treatments which had the highest Ra values were: 1,6W-20Hz (11.623±3,419) for the Nd:YAG laser and 3W (6,051±1,991) for Er,Cr:YSGG. Rocatec system showed the lowest roughness levels (1,297±0,026). As for phase 3 of the study RAD the highest Ra parameters for each laser were selected as well as the parameter with favorable characteristics to adherence observed in phase 1 SEM. Therefore, the microshear bond strength test was done not only in the Y-TZP ceramic treated with lasers before the final sintering (using 1,6W and 1,2W parameters for the Nd:YAG laser and 3W for Er,Cr:YSGG), but also in the Rocatec system, making use of two double activation resin cements (Panavia e RelyX U100). The ANOVA Split-Plot statistical analysis of the RAD data showed that there were no statistical variations concerning the studied cements. However, in what regards the surface treatments, it was observed that the highest RAD values were obtained for the Rocatec system (20,92±3,4MPa). Both parameters used for the Nd:YAG laser were similar, presenting intermediate RAD values (1,2W=9,79±4 and 1,6W=11,35±3,64 MPa). The treatment which used Er,Cr:YSGG laser presented the lowest RAD values (1,43±1,21MPa). It was possible to conclude that surface treatments with all tested lasers in the irradiation parameters after sintering caused damage to the Y-TZP ceramic. Treatments making use of Nd:YAG and Er,Cr:YSGG lasers before the sintering were not enough in order to increase the adhesive resistance between Y-TZP and the resin cements tested, even though they presented micromorphological characteristics that indicated growth in the surface area.

O objetivo deste estudo é avaliar a influência da irradiação com laser de Er,Cr:YSGG no espaço protético de condutos radiculares preparados para a fixação de pinos em fibra de vidro reforçados (FRC Postec®), avaliando-se o comportamento de três diferentes técnicas adesivas (self-etching= Panavia F®; total-etching= Excite DSC® + Variolink II® e self-adhesive= RelyX Unicem Aplicap®). Observaram-se as orientações da norma ISO-TS 11405 para a preparação das raízes dentais unirradiculares humanas. As amostras foram separadas na altura da junção amelo-dentinaria, tratadas endodonticamente com instrumentação rotatória e seladas com técnica de condensação lateral. Foram utilizados dois tipos diferentes de pontas de safira para irradiação intracanal o axial (Z4, 400 m de diâmetro) e o radial ou side firing (RFT4, 415 m de diâmetro) com densidade de energia de 40 J/cm2. Esta densidade de energia foi obtida como parte deste experimento, analisando-se diversos parâmetros de energia com os resultados morfológicos e térmicos obtidos. Nesta densidade, obtive-se grande quantidade de túbulos dentinários abertos e variação de temperatura segura para uso clínico. Cada raiz foi irradiada em cinco movimentos circulares, de apical para cervical, com intervalo de 20 segundos, entre elas. Os FRC Postec foram cimentados imediatamente após a irradiação e divididos randomicamente em nove grupos (n=10). Cada raiz foi seccionada em 6 discos de 1 mm de espessura para ensaio do tipo push-out, para a obtenção da força máxima de ruptura, e posterior cálculo da resistência de união adesiva em função da área de superfície do núcleo deslocado, resultando na pressão em MPa. A resistência de união adesiva nos grupos irradiados foi estatisticamente superior do que os grupos controle. Foram avaliadas as diferenças na resistência de união adesiva em diferentes porções do núcleo (cervical, médio e apical), onde o sistema adesivo tipo self-adhesive (RelyX Unicem Aplicap) teve o melhor resultado para os grupos irradiados. Avaliou-se por técnica de FTIR as diferenças químicas ocorridas na dentina intrarradicular irradiada com laser de Er,Cr:YSGG, em diferentes porções (cervical, médio e apical) em função da orientação dos túbulos. Foram observadas nos espectros de FTIR alterações na intensidade das bandas de algumas moléculas, indicando variação na quantidade da parte orgânica (amida I e amida II) após a irradiação, nas diferentes regiões dentais em função do feixe laser sobre a orientação dos túbulos dentinários, sem causar alterações na sua composição. Essas diferenças podem interferir no resultado da resistência de união adesiva. A técnica de utilização de laser de Er,Cr: YSGG em dentina radicular pré-cimentação de núcleo protético aumenta a resistência de união adesiva, na dependência do cimento utilizado. / The aim of this study was to evaluate the influence of the Er,Cr:YSGG laser irradiation in the prosthetic post space before FRC Postec placement using three different adhesive systems (self-etching- Panavia F; total-etching- Excite DSC + Variolink II e self adhesive - RelyX Unicem Aplicap). According to ISO-TS 11405, sectioned at the CEJ, human dental single roots were endodontically treated with rotatory instruments and filled with gutta-percha points and sealer. Were used at 40 J/cm2 an axial Z4 laser tip (400 m diameter) and a radial (side firing) RFT4 laser tip (415 m diameter). This density of energy was experimentally determinated observing morphological changes in SEM images due to an increase range in the energy applied to dentinal root canal surface. At the length between 32 and 49 J/cm2 most of the intracanal dentinal tubules were open. The temperature increase was within the biological safe suggesting a feasible clinical use. Each root canal was irradiated five times with helicoidal movements from apical to cervical, with 20 seconds interval. FRC Postec were immediately cemented and randomly divided in nine groups (n=10). Each root canal was cut in six discs for push out test, were the maximum failure load was obtained and the bond strength was calculated as a function of post bonded area. The bond strength for the irradiated groups was superior among all control groups. The evaluation of bond strength among root region (cervical, middle and apical) was performed and differences were observed. The self-adhesive (RelyX Unicem Aplicap) system was noted superior among all irradiated groups and all regions. Chemical changes were analyzed by FTIR due to dental root portion and dentinal tubules orientation to laser beam direction. The FTIR spectra obtained indicated changes due to tubules orientation and root canal portion irradiated such as the proportion among the compositional ratio without causing chemical changes. These compositional ratio alterations may affect the bond strength results. The irradiation with Er,Cr:YSGG laser on dentinal walls of a prosthetic post space preparation before the post cementation, as suggested in this study, may increase the bond strength between the post and root canal dentin depending upon the luting cement that is used.

O objetivo deste estudo é avaliar a influência da irradiação com laser de Er,Cr:YSGG no espaço protético de condutos radiculares preparados para a fixação de pinos em fibra de vidro reforçados (FRC Postec®), avaliando-se o comportamento de três diferentes técnicas adesivas (self-etching= Panavia F®; total-etching= Excite DSC® + Variolink II® e self-adhesive= RelyX Unicem Aplicap®). Observaram-se as orientações da norma ISO-TS 11405 para a preparação das raízes dentais unirradiculares humanas. As amostras foram separadas na altura da junção amelo-dentinaria, tratadas endodonticamente com instrumentação rotatória e seladas com técnica de condensação lateral. Foram utilizados dois tipos diferentes de pontas de safira para irradiação intracanal o axial (Z4, 400 m de diâmetro) e o radial ou side firing (RFT4, 415 m de diâmetro) com densidade de energia de 40 J/cm2. Esta densidade de energia foi obtida como parte deste experimento, analisando-se diversos parâmetros de energia com os resultados morfológicos e térmicos obtidos. Nesta densidade, obtive-se grande quantidade de túbulos dentinários abertos e variação de temperatura segura para uso clínico. Cada raiz foi irradiada em cinco movimentos circulares, de apical para cervical, com intervalo de 20 segundos, entre elas. Os FRC Postec foram cimentados imediatamente após a irradiação e divididos randomicamente em nove grupos (n=10). Cada raiz foi seccionada em 6 discos de 1 mm de espessura para ensaio do tipo push-out, para a obtenção da força máxima de ruptura, e posterior cálculo da resistência de união adesiva em função da área de superfície do núcleo deslocado, resultando na pressão em MPa. A resistência de união adesiva nos grupos irradiados foi estatisticamente superior do que os grupos controle. Foram avaliadas as diferenças na resistência de união adesiva em diferentes porções do núcleo (cervical, médio e apical), onde o sistema adesivo tipo self-adhesive (RelyX Unicem Aplicap) teve o melhor resultado para os grupos irradiados. Avaliou-se por técnica de FTIR as diferenças químicas ocorridas na dentina intrarradicular irradiada com laser de Er,Cr:YSGG, em diferentes porções (cervical, médio e apical) em função da orientação dos túbulos. Foram observadas nos espectros de FTIR alterações na intensidade das bandas de algumas moléculas, indicando variação na quantidade da parte orgânica (amida I e amida II) após a irradiação, nas diferentes regiões dentais em função do feixe laser sobre a orientação dos túbulos dentinários, sem causar alterações na sua composição. Essas diferenças podem interferir no resultado da resistência de união adesiva. A técnica de utilização de laser de Er,Cr: YSGG em dentina radicular pré-cimentação de núcleo protético aumenta a resistência de união adesiva, na dependência do cimento utilizado. / The aim of this study was to evaluate the influence of the Er,Cr:YSGG laser irradiation in the prosthetic post space before FRC Postec placement using three different adhesive systems (self-etching- Panavia F; total-etching- Excite DSC + Variolink II e self adhesive - RelyX Unicem Aplicap). According to ISO-TS 11405, sectioned at the CEJ, human dental single roots were endodontically treated with rotatory instruments and filled with gutta-percha points and sealer. Were used at 40 J/cm2 an axial Z4 laser tip (400 m diameter) and a radial (side firing) RFT4 laser tip (415 m diameter). This density of energy was experimentally determinated observing morphological changes in SEM images due to an increase range in the energy applied to dentinal root canal surface. At the length between 32 and 49 J/cm2 most of the intracanal dentinal tubules were open. The temperature increase was within the biological safe suggesting a feasible clinical use. Each root canal was irradiated five times with helicoidal movements from apical to cervical, with 20 seconds interval. FRC Postec were immediately cemented and randomly divided in nine groups (n=10). Each root canal was cut in six discs for push out test, were the maximum failure load was obtained and the bond strength was calculated as a function of post bonded area. The bond strength for the irradiated groups was superior among all control groups. The evaluation of bond strength among root region (cervical, middle and apical) was performed and differences were observed. The self-adhesive (RelyX Unicem Aplicap) system was noted superior among all irradiated groups and all regions. Chemical changes were analyzed by FTIR due to dental root portion and dentinal tubules orientation to laser beam direction. The FTIR spectra obtained indicated changes due to tubules orientation and root canal portion irradiated such as the proportion among the compositional ratio without causing chemical changes. These compositional ratio alterations may affect the bond strength results. The irradiation with Er,Cr:YSGG laser on dentinal walls of a prosthetic post space preparation before the post cementation, as suggested in this study, may increase the bond strength between the post and root canal dentin depending upon the luting cement that is used.

O objetivo deste estudo foi avaliar os efeitos dos lasers de Nd:YAG, CO2 e Er,Cr:YSGG no tratamento de superfície da cerâmica Y-TZP antes e depois da sinterização final, por meio de Microscopia Eletrônica de Varredura (MEV), mensuração da rugosidade de superfície (Ra) e teste de resistência adesiva por microcisalhamento (RAD). Para tanto, barras de Y-TZP foram confeccionadas e distribuídas entre as 3 fases do experimento, sendo as duas primeiras fases seletivas para a identificação dos parâmetros lasers a serem utilizados na fase 3 de análise da RAD. Na fase 1 MEV - foram testados parâmetros que variavam entre 50 e 100 mJ para o laser de Nd:YAG, 2 a 4W para o laser de CO2 e 1 a 3,5W para o laser de Er,Cr:YSGG, testados antes ou após a sinterização da Y-TZP. Observou-se que a maioria dos tratamentos foram capazes de promover alterações na cerâmica com diferentes intensidades dependendo do parâmetro utilizado. Para a fase 2 Ra foram selecionados apenas os tratamentos com os lasers de Nd:YAG e Er,Cr:YSGG aplicados antes da sinterização da cerâmica, sendo que cada laser foi avaliado individualmente e comparados ao tratamento de superfície com o sistema Rocatec. Os tratamentos com os maiores valores de Ra foram: para o laser de Nd:YAG - 1,6W-20Hz (11.623±3,419) e para o laser de Er,Cr:YSGG - 3W (6,051±1,991). O sistema Rocatec apresentou os menores valores de rugosidade (1,297±0,026). Para a fase 3 do estudo RAD foram selecionados os parâmetros que apresentaram os maiores valores de Ra para cada laser, além do parâmetro com características favoráveis à adesão observado na fase 1 MEV. Sendo assim, o teste de microcisalhamento foi realizado entre a cerâmica Y-TZP tratada com os lasers antes da sinterização final, nos parâmetros de 1,6W e 1,2W para o laser de Nd:YAG e 3W para o laser de Er,Cr:YSGG; e com o sistema Rocatec, utilizando-se dois cimentos resinosos de dupla ativação (Panavia e RelyX U100). A análise estatística ANOVA Split-Plot dos dados de RAD obtidos revelou que não houve diferença estatística entre os cimentos estudados. Porém, no fator tratamentos de superfície observou-se que os maiores valores de RAD foram obtidos para o sistema Rocatec (20,92±3,4MPa). Os dois parâmetros utilizados para o laser de Nd:YAG foram semelhantes entre si com valores de RAD intermediários (1,2W=9,79±4 MPa e 1,6W=11,35±3,64 MPa) e o tratamento com o laser de Er,Cr:YSGG apresentou os menores valores de RAD (1,43±1,21MPa). Pôde-se concluir que os tratamentos de superfície com todos os lasers testados nos parâmetros de irradiação após a sinterização, provocaram danos à cerâmica Y-TZP. Os tratamentos com os lasers de Nd:YAG e Er,Cr:YSGG antes da sinterização, apesar de apresentarem características micromorfológicas sugestivas de aumento da área de superfície, não foram suficientes para aumentar a resistência adesiva entre a Y-TZP e os cimentos resinosos testados. / The aim of this study was to evaluate the effects of Nd:YAG, CO2 and Er,Cr:YSGG lasers on the surface treatment of Y-TZP ceramic before and after the final sintering by means of Scanning Electron Microscope (SEM), surface roughness measurement (Ra) and microshear bond strength adhesive resistance test (RAD). In order to do so, Y-TZP bars were produced and distributed among the three experimental phases, being the two first ones selective in what regards identifying parameters for the lasers used in phase 3 of the RAD analysis. In phase 1 SEM parameters varying from 50 to 100 mJ were tested for the Nd:YAG laser, from 2 to 4W for the CO2 laser and from 1 to 3,5W for the Er,Cr:YSGG laser, either before or after the Y-TZP sintering. It was observed that most treatments were able to promote changes in the ceramic with varied intensity according to the parameter used. In phase 2 Ra only treatments with Nd:YAG and Er,Cr:YSGG lasers applied before ceramic sintering were selected, and each laser was individually evaluated and compared to the surface treatment with Rocatec system. The treatments which had the highest Ra values were: 1,6W-20Hz (11.623±3,419) for the Nd:YAG laser and 3W (6,051±1,991) for Er,Cr:YSGG. Rocatec system showed the lowest roughness levels (1,297±0,026). As for phase 3 of the study RAD the highest Ra parameters for each laser were selected as well as the parameter with favorable characteristics to adherence observed in phase 1 SEM. Therefore, the microshear bond strength test was done not only in the Y-TZP ceramic treated with lasers before the final sintering (using 1,6W and 1,2W parameters for the Nd:YAG laser and 3W for Er,Cr:YSGG), but also in the Rocatec system, making use of two double activation resin cements (Panavia e RelyX U100). The ANOVA Split-Plot statistical analysis of the RAD data showed that there were no statistical variations concerning the studied cements. However, in what regards the surface treatments, it was observed that the highest RAD values were obtained for the Rocatec system (20,92±3,4MPa). Both parameters used for the Nd:YAG laser were similar, presenting intermediate RAD values (1,2W=9,79±4 and 1,6W=11,35±3,64 MPa). The treatment which used Er,Cr:YSGG laser presented the lowest RAD values (1,43±1,21MPa). It was possible to conclude that surface treatments with all tested lasers in the irradiation parameters after sintering caused damage to the Y-TZP ceramic. Treatments making use of Nd:YAG and Er,Cr:YSGG lasers before the sintering were not enough in order to increase the adhesive resistance between Y-TZP and the resin cements tested, even though they presented micromorphological characteristics that indicated growth in the surface area.

Orientadora: Profa. Dra. Patrícia Aparecida da Ana / Coorientadora: Profa. Dra. Ilka Tiemy Kato Prates / Dissertação (mestrado) - Universidade Federal do ABC, Programa de Pós-Graduação em Engenharia Biomédica, São Bernardo do Campo, 2018. / Lasers de erbio podem ser usados para prevencao de carie radicular, o que e de suma importancia para os idosos. Contudo, parametros seguros e eficazes de irradiacao para a dentina radicular ainda nao foram determinados empregando-se o laser de Er,Cr:YSGG para tal finalidade. Esse estudo tem por objetivo avaliar os aumentos de temperatura pulpar e superficial, assim como as alteracoes morfologicas, decorrentes da irradiacao da dentina radicular com laser de Er,Cr:YSGG quando empregado com finalidade preventiva, e avaliar os efeitos de um dos parametros estabelecidos na composicao e resistencia a desmineralizacao da dentina radicular. O estudo foi dividido em duas fases experimentais. Na primeira, os efeitos morfologicos e de variacao de temperatura pulpar e superficial foram avaliados a partir de tres potencias medias do laser de Er,Cr:YSGG, enquanto que, na segunda, um dos parametros selecionados foi avaliado quanto as mudancas composicionais, morfologicas e opticas promovidas na dentina radicular. Na primeira fase experimental, 30 dentes unirradiculares humanos e 30 blocos de dentina radicular bovina foram aleatoriamente distribuidos em tres grupos experimentais para irradiacao com laser de Er,Cr:YSGG (2,78 £gm, 600 £gm, 20 Hz, 60 £gs, sem refrigeracao): G1a ¡Vpotencia media de 0,10W; G1b - potencia media de 0,25W; G1c - potencia media de 0,50W. Foram determinadas as variacoes de temperatura intrapulpar empregando-se termopares, variacoes de temperatura superficial com termografia e alteracoes morfologicas por microscopia eletronica de varredura (MEV). Na segunda fase experimental, 75 blocos de dentina radicular bovina foram aleatoriamente distribuidos em 5 grupos experimentais: G1b: sem tratamento; G2b: tratamento com fluor fosfato acidulado (FFA, 1,23% F-, pH= 3,6 = 3,9); G3b: irradiacao com potencia media de 0,25W; G4b: irradiacao laser seguida de aplicacao de FFA; G5b: aplicacao de FFA seguida da irradiacao laser. Foram efetuadas avaliacao composicional por espectroscopia de absorcao no infravermelho por transformada de Fourier (FTIR), optica por tomografia por coerenca optica (OCT) e morfologica por MEV. Em seguida, as amostras foram submetidas a ciclagem de pH por 8 dias e, no fim, foi avaliado o coeficiente de atenuacao optco obtido por nova avaliacao por OCT. A analise estatistica foi efetuada individualmente para cada variavel resposta, sendo adotado o nivel de significancia estatistica de 5%. Todos os parametros laser promoveram alteracoes de temperatura inferior ao limiar para danos pulpares; contudo, apenas o grupo tratado com 0,50 W promoveu aumentos de temperatura superficial superiores a 100o C, indicativos de alteracoes quimicas na dentina. Os grupos irradiados com 0,25W e 0,50 W promoveram microablacoes na dentina, observados pelo MEV. Na segunda fase experimental, observou-se pelo FTIR que a irradiacao laser isoladamente nao altera a composicao da dentina, mas a aplicacao previa de FFA seguida da irradiacao laser diminuiu significativamente o conteudo de ¿Þ3¿Þ4 carbonato da dentina. Da mesma forma, este tratamento tambem promove maior alteracao morfologica e de coeficiente de atenuacao optica quando comparado aos tratamentos isoladamente. Apos desmineralizacao, observou-se que tanto a irradiacao laser isoladamente, quanto a aplicacao de FFA previamente a irradiacao, promoveram aumento significativo do coeficiente de atenuacao optico, indicando menor desmineralizacao das amostras para este grupo. Desta forma, foi possivel concluir que o laser de Er,Cr:YSGG apresenta potencial para uso em prevencao da desmineralizacao da dentina radicular, sendo segura sua aplicacao com potencia media de 0,25W e mais eficiente quando precedido da aplicacao de FFA. / Erbium lasers can be used to prevent root caries, which is imporant for the elderly. However, safe and effective irradiation parameters have not yet been determined for root dentin using the Er,Cr:YSGG laser for this purpose. The objective of this study was to evaluate the pulp and surface temperature increases, as well as the morphological alterations, due to Er,Cr:YSGG laser irradiation on root dentin when used for preventive purposes, and to evaluate the effects of one of the parameters in the composition and resistance to demineralization of root dentin. The study was split into two experimental phases. In the first one, the morphological and pulp and surface temperature variations were evaluated from three average powers of the Er,Cr:YSGG laser, while in the second phase, the compositional, morphological and optical properties promoted by one selected laser parameter were evaluated in root dentin. In the first experimental phase, 30 unirradicular human teeth and 30 bovine root dentin slabs were randomly distributed in three experimental groups for irradiation with Er,Cr:YSGG laser (2.78 £gm, 600 £gm, 20 Hz, 60 £gs, without refrigeration): G1a - average power of 0.10W; G1b - average power of 0.25W; G1c - average power of 0.50W. The pulpal temperature variations were determined using fast response thermocouples, the surface temperature variations were measured using infrared thermography and morphological changes were observed by scanning electron microscopy (SEM). In the second experimental phase, 75 slabs of bovine root dentin were randomly distributed in 5 experimental groups: G1b: without treatment; G2b: treatment with acidulated fluoride phosphate (APF, 1.23% F-, pH = 3.6 = 3.9); G3b: irradiation with average power of 0.25W; G4b: laser irradiation followed by APF application; G5b: application of APF followed by laser irradiation. The compositional evaluation was performed by Fourier transformed infrared spectroscopy (FTIR), the optical aspect was observed by optical coherence tomography (OCT) and morphology was evaluated by SEM. Afterwards, the samples were submitted to pH-cycling for 8 days and, finally, the optical attenuation coefficient was obtained by a new OCT evaluation. The statistical analysis was performed individually for each response variable, considering the level of significance of 5%. All the laser parameters promoted changes in temperature below the threshold for pulp damage; however, only the group treated with 0.50 W promoted surface temperature increases above 100 ¢XC, indicative of chemical changes in dentin. The groups irradiated with 0.25W and 0.50 W promoted microablation in dentin. In the second experimental phase, it was observed that the laser irradiation alone does not alter the composition of the dentin, but the previous application of APF followed by the laser irradiation significantly decreased the content of ¿Þ3¿Þ4 carbonate of the dentin. In the same way, this treatment also promotes greater morphological alterations when compared to treatments alone. After demineralization, it was observed that both the laser irradiation alone and the application of APF previously to the laser irradiation promoted a significant increase in the optical attenuation coefficient, indicating a lower demineralization of this group. In this way, it was possible to conclude that the Er,Cr:YSGG laser presents potential for use for preventing root dentin demineralization. Its application is safe with a mean power of 0.25W and more efficient when preceded by APF application.