Orientador: Marcelo Ferrarezi de Andrade / Banca: Vanderlei Salvador Bagnato / Banca: José Eduardo Pelizon Pelino / Resumo: Este estudo avaliou a resistência adesiva de microtração em reparos de resinas compostas, novas e envelhecidas, após tratamento da superfície usando irradiação a laser de Er: YAG, ponta diamantada e abrasão a ar. 36 blocos de resina composta híbrida Z100 (3M) com 5mm de comprimento e 6 mm de lado foram confeccionados com auxílio de uma matriz. Metade desses blocos foram reparados após 24 horas, e a outra metade foi reparada após envelhecimento artificial com luz ultravioleta. Cada grupo foi subdividido em 6 subgrupos e as superfícies experimentais foram submetidas a diferentes tratamentos: (G1) desgaste com ponta diamantada; (G2) jateamento com partículas de óxido de alumínio de 60 mm; (G3) ablação com laser de Er: YAG a um nível de energia de 100mJ; (G4) ablação com laser de Er:YAG a um nível de energia de 200mJ; (G5) ablação a laser de Er:YAG a um nível de energia de 300mJ; (G6) controle- ausência de tratamento de superfície. Após tratamento da superfície, o agente adesivo (Single Bond 3M) foi aplicado e os blocos foram reparados com a resina composta Point4 (KERR). Reparados, os blocos foram seccionados em espécimes de 1.0 mm2. A resistência adesiva de microtração foi medida em uma máquina de teste universal MTS. No grupo que foi reparado 24 horas após, não houve diferença estatisticamente significante na resistência adesiva interfacial entre os subgrupos. No grupo que foi envelhecido, os subgrupos G1 e G3 tiveram as maiores médias de resistência adesiva de reparo. Significantemente, os menores valores foram achados para os subgrupos G2 e G6. As médias da resistência adesiva de reparo foram estatisticamente similares para G3, G4 e G5. O exame em SEM indicou que a fratura adesiva foi o tipo predominante de falha. Os resultados desse estudo indicam que os maiores valores de resistência adesiva foram achados para o desgaste da superfície com... (Resumo completo, clicar acesso eletrônico abaixo). / Abstract: This study assessed the microtensile bond strengths of composite repairs, new and aged, after surface treatments, using Er:YAG laser irradiation, diamond bur and air abrasion. 36 blocks of hybrid composite resin Z100 (3M) with 5.0 mm length and 6.0 mm of side were made in mold. Half of these blocks were repaired after 24 hr and the other half was aged in an artificial aging chamber with exposure to a total ultraviolet irradiation. Each group was then divided into six subgroups and the experimental surface was exposed to a different treatment: (G1) grinding with diamond burs; (G2) air-abraded with 60mm aluminum oxide particles; (G3) ablation with an Er: YAG laser under the energy level of 100 mJ; (G4) ablation with an Er: YAG laser under the energy level of 200 mJ; (G5) ablation with an Er: YAG laser under the energy level of 300 mJ; (G6) controle - with no surface treatment. After the resin treatment on the surface, the bonding agent (Single bond, 3M) was applied and the blocks were repaired with the resin Point4 (Kerr) composite. Repaired, the blocks were sectioned into specimens (stick) of 1.0 mm2. Microtensile bond strength was measured in a universal testing machine MTS. The group repaired after 24 hours did not present statistically significant differences on interfacial bond strengths between the subgroups. On the aged group, the subgroups G1 and G3 presented the highest mean of repairing bond strenght. Significant lower values were found for subgroups G2 and G6 .The mean of repairing bond strenght was statistically similar for G3, G4 and G5. SEM examination indicated that adhesive failure was the predominant mode of failure. The results of this study indicate that the highest bond values were achieved by grinding the surface with diamond burs and ablating the surface with an Er: YAG laser under the energy level of 100mJ... (Complete abstract, click electronic address below). / Mestre

Resumo: O objetivo deste trabalho foi realizar avaliação da resistên - cia de união ao cisalhamento de reparos de resina compostas em restaurações com resina composta envelhecidas, em função de diferentes tratamentos superficiais. Foram confeccionados 60 corpos-de-prova de resina composta Z250 (3M) e levados a termociclagem para simular o envelhecimento da restauração, foram realizados 500 ciclos de 15 segundos cada, variando entre 5°e 55°C. Separados aleatoriamente em seis grupos que sofreram os seguintes tratamentos superficiais: nenhum tratamento (G1 - controle), desgaste com ponta diamantada (G2), jato de óxido de alumínio com partículas de 27,5æm (G3) por 10 segundos, laser de Er:YAG - 200mJ (G4), laser de Er:YAG - 300mJ (G4) e laser de Er:YAG - 400mJ (G6), os três últimos com freqüência de 10Hz por 10 segundo. Foi realizada microscopia eletrônica de varredura para observarmos o aspecto do material após os tratamentos terem sido executados. O reparo da restauração foi realizado utilizando-se a mesma resina. O teste de cisalhamento foi feito na Máquina de Ensaios Mecânicos MTS - 810. Analisando os resultados por ANOVA e pelo teste de Tukey não foram encontradas diferenças significativas (p-valor=0.5120). A análise dos valores medianos, mostrou que o tratamento superficial com jato de óxido de alumínio apresentou uma maior resistência da interface do reparo ao cisalhamento (8.91Mpa) enquanto que o laser de Er:YAG com 400mJ de potência, apresentou a menor (6.76Mpa). A análise dos tipos de fratura mostrou que 90% dos corpos-de-prova do grupo 3 (óxido de alumínio) sofreram fraturas coesivas. / Abstract: The aim of this work was to perform the evaluation of the shear bond strength of the composite resin repairs in old composite restorations, modifying the superficial treatment of the samples. Sixty samples of the composite resin Z250 (3M) were prepared and thermocycled for 500 cycles at 5° and 55°C with a dwelling time of 15 seconds. Speciments were randomly divided into six groups and subjected to different surface treatments as follows: No surface treatment (G1 - control), grinding with a diamond bur (G2), sandblasting with a microetcher for 10 seconds with 27,5æm Al2O3 particles (G3), treated with Er:YAG laser with an energy intensity of 200mJ (G4), 300mJ (G5), 400mJ (G6), frequency of 10Hz for 10 seconds. The speciments after surface treatment were observed using the scanning electron microscope. The repair of the old resin was done with the same material. The shear bond strength test was performed in a Mechanic Testing MTS - 810. Statistical treatment by ANOVA and Tukey's test showed no significant differences between the groups tested (p=0.5120). The highest shear bond strength values were achieved by sandblasting the surface with a microetcher with Al2O3 (8,91Mpa), whereas the lowest values were obtained with Er:YAG laser with energy intensity of 400mJ (6.76Mpa). Observing the rupture surface, G3 presented 90% of cohesive failures. / Orientador: José Roberto Cury Saad / Coorientador: Rosane F. Z. Lizarelli / Banca: Celso Luiz de Angelis Porto / Banca: Elda Pisaneschi / Mestre

Resumo: O objetivo do presente estudo foi comparar o efeito do laser de Er:YAG, associado ou não, à raspagem e alisamento radicular no tratamento periodontal não cirúrgico. Foram selecionados 21 pacientes saudáveis, com doença periodontal crônica, apresentando 4 bolsas periodontais entre 5 e 9mm, em sítios não vizinhos. Os pacientes foram tratados sob efeito de anestesia local e os sítios foram divididos aleatoriamente em quatro grupos, sendo: Grupo Raspagem+Laser: associação da raspagem e alisamento radicular com instrumentos manuais com o laser Er:YAG; Grupo Laser: laser Er:YAG sozinho; Grupo Raspagem: somente raspagem e alisamento radicular com instrumentos manuais; Grupo Controle: não foi feito tratamento algum. Os parâmetros utilizados para o laser de Er:YAG foram 100mJ/pulso em uma freqüência de 10Hz (12,9J/cm2). Os parâmetros clínicos índice de placa (IP), índice gengival (IG), sangramento à sondagem (SS), profundidade de sondagem (PS), recessão gengival (RG) e nível de inserção clínico relativo (NICR) foram avaliados antes, 30 e 90 dias após o tratamento. Amostras de fluido crevicular das bolsas foram coletadas junto com IP, IG e SS para análise da concentração do mediador de inflamação Interleucina-1Beta (IL-1b). Os resultados, após 90 dias, demonstraram para IP melhora significante para somente para o grupo Raspagem (p<0,01), enquanto o IG apresentou melhoras significantes para os grupos Raspagem+Laser e Raspagem (p<0,05), sendo que o grupo Raspagem+Laser obteve uma melhora significantemente maior que o grupo Controle, após 30 e 90 dias (p<0,05). O valor do sangramento à sondagem diminuiu significantemente para os grupos Raspagem+Laser, Laser e Raspagem após 30 dias (p<0,01) e também, com diferença significante quando comparados ao grupo Controle (p<0,05); após 90 dias diferença significante ocorreu para todos os grupos (p<0,01)... (Resumo completo, clicar acesso eletrônico abaixo). / Abstract: The aim of the present study was to compare the effectiveness of an Er:YAG laser, with a combination or not, to that of scaling and root planning (SRP) with hand instruments for non-surgical periodontal treatment. Twenty-one healthy patients with chronic periodontal disease were selected presenting 4 periodontal pockets between 5 and 9mm, in sites non-neighbors. The patients were treated under local anesthesia and the sites were divided randomly in four groups, being: Group Scaling+Laser (Group 1): combination of SRP with manual instruments and an Er:YAG laser; Group Laser (Group 2): an Er:YAG laser alone; Group Sacaling (Group 3): only SRP with hand instruments; Group Control (Group 4): it was not made any treatment. The parameters used for the Er:YAG laser were 100mJ/pulso and 10Hz (12,9J/cm2). Clinical assessments plaque index (PI), gingival index (GI), bleeding on probing (BOP), probing depth (PD), gingival resection (GR), and clinical attachment level (CAL) were made prior to and at 30 and 90 days after the treatment. Gingival crevicular fluid samples were taken for analyses concentration of the mediator of inflammation interleukin-1b in the same day that IP, IG and SS. The results, after 90 days, demonstrated for PI a significant reduction only for the group 3 (p<0,01), while GI presented significant improvements for groups 1 and 3 (p<0,05), and the group 1 showed an improvement was significantly higher than the group 4, after 30 and 90 days (p<0,05). The reduction of BOP was significant to groups 1, 2 and 3 after 30 days (p<0,01) and also, with significant difference when compared to the group 4 (p<0,05); after 90 days significant difference occurred for all the groups (p<0,01). The mean value of the PD, after 30 days (p<0,001) and after 90 days (p<0,001), decreased in all groups, except in group 4; and still, after... (Complete abstract, click electronic address below). / Orientador: Rosemary Adriana Chiérici Marcantonio / Coorientador: Letícia Helena Theodoro / Banca: Denise Madalena Palomari Spolidorio / Banca: Silvia Rosana Soares Carneiro / Mestre