Made available in DSpace on 2015-05-14T12:09:41Z (GMT). No. of bitstreams: 1 arquivototal.pdf: 3971695 bytes, checksum: 7164e4a06c778dc9c0e90c74de8e25d1 (MD5) Previous issue date: 2005-09-30 / Coordenação de Aperfeiçoamento de Pessoal de Nível Superior - CAPES / The generation of residues by the footwear s industry, especially E.V.A. residues (Ethilene Vinil Acetate), is calling specialist s attention for the elaboration of researches that make possible to recycle these residues for the Civil Construction Industry. It is known that such residues have as characteristics: low specific mass, good acoustic and thermal behavior, stability, inert, not susceptible to fungi, besides having good potential to be used as a of synthetic attaché for elaboration of light composites, being a substitute for part of the natural aggregates. This work presents results of a research about the use of these residues as a light aggregate for the fabrication of masonry blocks designated to the Civil Construction, using an alternative material and a new geometry (EVANG Block). The objective was to develop a new masonry block with increased dimensions, if compared to the traditional sizes, to be used as an alternative masonry reusing industrial residues, preserving the environment, considering its characteristics and the manual process of manufacture with a steel mold specified at the experiments. The results show that the block, with dimensions of 59,0 cm x 26,5 cm x 11,5 cm (determined by a modulated pattern of construction), is highly flexible with an average strength of 0,82 MPa, using 80% of residues on its composition to replace the natural aggregates. Therefore, it may be told that there are important contributions in this research, showing its technical viability: the possibility to recycle an industrial residue, the reduction of the need of natural aggregates and the increase of productivity for the masonry walls at the buildings / A geração de resíduos de E.V.A. (Etileno Acetato de Vinila) pela indústria calçadista tem se constituído num problema para o setor e, ao mesmo tempo, tem despertado a atenção de pesquisadores para a reciclagem desses resíduos pela construção civil. Sabe-se que tais resíduos têm baixa massa específica e características termo-acústicas favoráveis, não são susceptíveis a fungos e têm grande potencial, para serem empregados como agregados artificiais sintéticos, em substituição aos naturais, na elaboração de compósitos cimentícios. Neste trabalho, apresentam-se os resultados de uma ampla investigação sobre a utilização desse resíduo como agregado leve na confecção de vedações na construção civil, utilizando um bloco não convencional com nova geometria (bloco EVANG). O objetivo foi projetar um novo bloco de vedação com novas geometrias, diferentes dos convencionais para se utilizar como elemento de vedação alternativo aproveitando os resíduos industriais, preservando o meio ambiente, considerando as peculiaridades do compósito utilizado e o processo manual de confecção dos mesmos em forma metálica, estabelecido nos experimentos. Os resultados demonstraram que o bloco projetado, que resultou nas dimensões: 59,0 cm x 26,5 cm x 11,5 cm (conforme estudo de modulação), possui uma boa característica de ductilidade com resistênc ia média de 0,82 MPa, utilizando 80% de resíduo de E.V.A. em substituição aos agregados naturais. Portanto pode-se dizer que há contribuições importantes neste estudo, viabilizando tecnicamente a reciclagem de um resíduo, a redução do consumo de agregados naturais e o aumento na produtividade na execução de alvenarias nas construções Alvenarias; Blocos; E.V.A.; Materiais não convencionais; Reciclagem; Resíduos Industriais.

Neste trabalho foram estudados compósitos que apresentam como matriz polimérica uma blenda composta por polietileno de alta densidade (HDPE) e copolímero etileno acetato de vinila (EVA) e como nanocarga, silsesquioxano poliédrico oligomérico (POSS). Os compósitos foram processados em câmara de mistura fechada e caracterizados quanto às propriedades térmicas e morfológicas. Para a preparação dos compósitos foram variadas as concentrações dos componentes da blenda (0, 25, 50, 75 e 100%) e da nanocarga (0, 0,5, 1, 1,5, 2, 5 e 10%). Os resultados de processamento mostraram que o aumento da concentração de POSS na matriz polimérica provocou a agregação do mesmo na matriz polimérica. As análises de calorimetria diferencial de varredura e termogravimetria indicaram que o POSS não afetou as temperaturas de fusão, cristalização e degradação da matriz polimérica. Os resultados de raios X indicaram que a presença do EVA no compósito promoveu o aparecimento de domínios cristalinos em concentrações menores de POSS. A microscopia eletrônica de varredura indicou que as amostras com 1% de POSS apresentam distribuição homogênea na matriz polimérica. Por outro lado, ocorreu a formação de agregados nas amostras com 5% de POSS. Os valores de Tg obtidos por análise térmica dinâmico-mecânica indicaram que o POSS causou um efeito plastificante na fase HDPE e uma redução da mobilidade na fase EVA. Ocorreu um aumento nos valores de módulo de armazenamento com a incorporação de POSS na matriz polimérica. / Submitted by Marcelo Teixeira (mvteixeira@ucs.br) on 2014-05-22T19:03:21Z No. of bitstreams: 1 Dissertacao Patricia Scapini.pdf: 2020883 bytes, checksum: 2c7249d3915135dd5f3cba151cf459db (MD5) / Made available in DSpace on 2014-05-22T19:03:21Z (GMT). No. of bitstreams: 1 Dissertacao Patricia Scapini.pdf: 2020883 bytes, checksum: 2c7249d3915135dd5f3cba151cf459db (MD5) / In this study composites with a polymeric matrix comprising a blend of high density polyethylene (HDPE) and the copolymer ethylene vinyl acetate (EVA), and with polyhedral oligomeric silsesquioxane (POSS) as the nanoclay, were processed and characterized. The composites were processed in a closed mixing chamber and characterized in terms of their thermal and morphological properties. For the preparation of the composites the concentrations of the blend components (0, 25, 50, 75 and 100%) and of the nanoclay (0, 0.5, 1, 1.5, 2, 5 and 10%) were varied. The results of the processing showed that an increase in the POSS concentration in the polymeric matrix caused the aggregation of the system. The differential scanning calorimetry and thermogravimetry analyses indicated that the POSS did not affect the melt, crystallization and degradation temperatures of the polymeric matrix. The X-ray results indicated that the presence of EVA in the composite led to the appearance of crystalline domains at lower POSS concentrations. Scanning electron microscopy indicated that the samples with 1% of POSS have a homogeneous distribution in the polymeric matrix. However, the formation of aggregates occurred in samples with 5% of POSS. The Tg values obtained from the thermo dynamic mechanical analysis indicated that the POSS had a plasticizing effect on the HDPE phase and caused a reduction in the mobility of the EVA phase. There was an increase in the storage modulus values with the incorporation of POSS into the polymeric matrix.

Neste trabalho foram estudados compósitos que apresentam como matriz polimérica uma blenda composta por polietileno de alta densidade (HDPE) e copolímero etileno acetato de vinila (EVA) e como nanocarga, silsesquioxano poliédrico oligomérico (POSS). Os compósitos foram processados em câmara de mistura fechada e caracterizados quanto às propriedades térmicas e morfológicas. Para a preparação dos compósitos foram variadas as concentrações dos componentes da blenda (0, 25, 50, 75 e 100%) e da nanocarga (0, 0,5, 1, 1,5, 2, 5 e 10%). Os resultados de processamento mostraram que o aumento da concentração de POSS na matriz polimérica provocou a agregação do mesmo na matriz polimérica. As análises de calorimetria diferencial de varredura e termogravimetria indicaram que o POSS não afetou as temperaturas de fusão, cristalização e degradação da matriz polimérica. Os resultados de raios X indicaram que a presença do EVA no compósito promoveu o aparecimento de domínios cristalinos em concentrações menores de POSS. A microscopia eletrônica de varredura indicou que as amostras com 1% de POSS apresentam distribuição homogênea na matriz polimérica. Por outro lado, ocorreu a formação de agregados nas amostras com 5% de POSS. Os valores de Tg obtidos por análise térmica dinâmico-mecânica indicaram que o POSS causou um efeito plastificante na fase HDPE e uma redução da mobilidade na fase EVA. Ocorreu um aumento nos valores de módulo de armazenamento com a incorporação de POSS na matriz polimérica. / In this study composites with a polymeric matrix comprising a blend of high density polyethylene (HDPE) and the copolymer ethylene vinyl acetate (EVA), and with polyhedral oligomeric silsesquioxane (POSS) as the nanoclay, were processed and characterized. The composites were processed in a closed mixing chamber and characterized in terms of their thermal and morphological properties. For the preparation of the composites the concentrations of the blend components (0, 25, 50, 75 and 100%) and of the nanoclay (0, 0.5, 1, 1.5, 2, 5 and 10%) were varied. The results of the processing showed that an increase in the POSS concentration in the polymeric matrix caused the aggregation of the system. The differential scanning calorimetry and thermogravimetry analyses indicated that the POSS did not affect the melt, crystallization and degradation temperatures of the polymeric matrix. The X-ray results indicated that the presence of EVA in the composite led to the appearance of crystalline domains at lower POSS concentrations. Scanning electron microscopy indicated that the samples with 1% of POSS have a homogeneous distribution in the polymeric matrix. However, the formation of aggregates occurred in samples with 5% of POSS. The Tg values obtained from the thermo dynamic mechanical analysis indicated that the POSS had a plasticizing effect on the HDPE phase and caused a reduction in the mobility of the EVA phase. There was an increase in the storage modulus values with the incorporation of POSS into the polymeric matrix.