Made available in DSpace on 2016-06-02T20:16:55Z (GMT). No. of bitstreams: 1 DissMSVK.pdf: 2016332 bytes, checksum: c7d2567be46c9a21abce63c045485207 (MD5) Previous issue date: 2005-03-18 / Financiadora de Estudos e Projetos / We presented in this work a study of the influence of the thickness of Al thin film deposited in substratum of low carbon steel. Alloys of steel low carbon and aluminum are used broadly in automobile and aerospace industries. We studied the nitrides formation, starting from a process of pre-heat-treatment of the samples in the nitriding camera followed by plasma nitriding, in the temperatures of 300°C and 400°C. The following techniques: Conversion Electrons Mössbauer Spectroscopy (CEMS), X-ray diffraction (XRD), Scan Eletron Microscopy (SEM) and Vickers microhardness test were used for the characterization of those samples. The Aluminium purity for the films was 99,99%. The steel low carbon substrate was supplied by IPT-SP (Institute of Researches Technological-SP) and after the samples be cut and polished, they received the film of aluminum. Soon after they were pre-heat-treated (section 4.1) and nitreded in the temperatures of 300oC and 400oC for 4 hours in composed atmosphere for 80% of H2 and 20%N2. After the nitriding the samples were characterized by the techniques referred above. For the temperature of 300oC, the X-ray Diffraction results showed the formation of the phases α-Fe, Al and AlN. The Mössbauer spectroscopy showed α- Fe and formation of solid solution of Fe in aluminum. For the temperature of 400oC, we still observed the formation of the phase Fe4Al13, for the two techniques. The Mössbauer Spectroscopy also showed that the increase of the percentage of the phase Fe4Al13 has a possible dependence with the nitriding temperature and with the thickness of the film of aluminum. The images of MEV and the Vickers microhardness tests, just revealed the presence of nitrides of iron in the borders of the samples. / Apresentamos neste trabalho um estudo da influência da espessura do filme de Al depositado em substrato de aço baixo carbono. Ligas de aço baixo carbono e alumínio são largamente empregadas em indústrias automobilísticas e aeroespaciais. Estudamos a formação de nitretos, a partir de um processo de prétratamento das amostras por aquecimento na câmara de nitretação seguido de nitretação a plasma, nas temperaturas de 300°C e 400°C. Para a caracterização dessas amostras foram utilizadas as técnicas de espectroscopia Mössbauer de elétrons de conversão (CEMS), difratometria de raios-x, microscopia eletrônica de varredura, além de ensaios de microdureza Vickers. A pureza do alumínio utilizado na produção dos filmes é de 99,99%. A matriz de aço baixo carbono foi fornecida pelo IPT-SP (Instituto de Pesquisas Tecnológicas-SP) e após as amostras serem cortadas e polidas, receberam o filme de alumínio. Em seguida foram pré-tratadas por aquecimento (seção 4.1) e nitretadas nas temperaturas de 300oC e 400oC durante 4 horas em atmosfera composta por 80% de H2 e 20%N2. Após a nitretação as amostras foram caracterizadas pelas técnicas referidas acima. Para a temperatura de 300 oC, os resultados obtidos com a técnica de difração de raios-x mostraram a formação das fases α-Fe, Al e AlN. A espectroscopia Mössbauer; por outro lado, mostrou α-Fe e formação de solução sólida de Fe em alumínio. Já para a temperatura de 400 oC, observamos ainda a formação da fase Fe4Al13, pelas duas técnicas. A Espectroscopia Mössbauer também mostrou que o aumento da porcentagem da fase Fe4Al13 tem uma possível dependência com a temperatura de nitretação e com a espessura do filme de alumínio. As imagens de MEV e as medidas de microdureza Vickers, revelaram a presença de nitretos de ferro apenas nas bordas das amostras.

DANTAS, Davi Soares. Estruturas de confinamento de baixa dimensionalidade em superfícies de hélio líquido suspensas. 2012. 73 f. Dissertação (Mestrado em Física) - Programa de Pós-Graduação em Física, Departamento de Física, Centro de Ciências, Universidade Federal do Ceará, Fortaleza, 2012. / Submitted by Edvander Pires (edvanderpires@gmail.com) on 2015-10-21T21:20:12Z No. of bitstreams: 1 2012_dis_dsdantas.pdf: 7266499 bytes, checksum: 9ac270f80eddaf4378a655a66bd0d2e6 (MD5) / Approved for entry into archive by Edvander Pires(edvanderpires@gmail.com) on 2015-10-22T21:33:49Z (GMT) No. of bitstreams: 1 2012_dis_dsdantas.pdf: 7266499 bytes, checksum: 9ac270f80eddaf4378a655a66bd0d2e6 (MD5) / Made available in DSpace on 2015-10-22T21:33:49Z (GMT). No. of bitstreams: 1 2012_dis_dsdantas.pdf: 7266499 bytes, checksum: 9ac270f80eddaf4378a655a66bd0d2e6 (MD5) Previous issue date: 2012 / The system of electrons on liquid helium (EoH) is one of the most ideal objects for investigating the fundamental principles of the physics of low dimensionality, since they do not have the inhomogeneities and impurities generally found on semiconductors. Besisdes, these systems are expected to have future technological applications as quantum bits, which are of fundamental importance as building blocks of future quantum computers. Usually, the low-dimensional confinements structures for EoH suggested in the literature are based on a planar surface, where the lateral confinement is induced by an external potential controlled by electrodes. In this work, we suggest an alternative way to produce lateral confinement in liquid helium surfaces, namely, we demonstrate that the shape of the surface can be designed to produce single and double quantum dots by adjusting the shape of a cavity in the substrate. The surface was calculated for four different shapes of substrate cavity: i) a cilyndrical cavity, generating a single quantum dot; ii) a ring-shaped cavity, generating a quantum ring; iii) two cubic cavities connected by a channel, creating a coupled double-dot structure; and iv) two channel-shaped cavities that intersect perpendicularly to each other, where a single dot is formed in the intersection point. The electron is then deposited and confined to move on each surface by an external electric field. Our results show that the electron energy levels in these systems can be tuned by varying the electric field and the bulk level, which are easily adjustably. The effect of an external magnetic field on the energy spectrum in one of these systems is also investigated. / O sistema de elétrons na superfície de hélio líquido é considerado um dos melhores objetos na investigação de príncipios fundamentais da Física de baixa dimensionalidade, uma vez que estes não apresentam heterogeneidades e impurezas geralmente encontradas em heteroestruturas semicondutoras. Além disso, espera-se que estes sistemas tenham uma aplicação tecnológica futura como extit{bits} quânticos, que são fundamentais na construção de blocos dos futuros computadores quânticos. Geralmente, as estruturas de confinamento de baixa dimensionalidade sugeridas para elétrons na superfície de hélio líquido na literatura são baseadas em superfícies planas, onde o confinamento lateral é induzido por um potencial externo controlado por eletrodos. No presente trabalho, é sugerida uma forma alternativa de produzir o confinamento lateral em superfícies de hélio líquido, isto é, é demonstrado que a forma da superfície pode ser projetada para produzir anéis, fios e pontos quânticos apenas variando a forma da cavidade do substrato no qual o hélio líquido se encontra suspenso. A superfície foi calculada para quatro formas diferentes de cavidade: i) uma cavidade cilíndrica, gerando um ponto quântico simples; ii) uma cavidade em forma de anel circular, gerando um anel quântico; iii) duas cavidades em forma de canais que se interceptam perpendicularmente, formando um ponto quântico simples no ponto de interceptação; e iv) duas cavidades retangulares conectadas por um canal estreito, gerando um ponto duplo. O elétron é então depositado sobre a superfície e confinado a se mover em cada superfície devido à ação de um campo elétrico externo. Os resultados apresentados aqui mostram que os níveis de energia para estes sistemas podem ser alterados através da variação do campo elétrico e do banho de hélio, que são facilmente ajustáveis. O efeito de um campo magnético externo é também investigado em um destes sistemas.